Survey
* Your assessment is very important for improving the workof artificial intelligence, which forms the content of this project
* Your assessment is very important for improving the workof artificial intelligence, which forms the content of this project
Chemical Engineering Journal xxx (2012) xxx–xxx Contents lists available at SciVerse ScienceDirect Chemical Engineering Journal journal homepage: www.elsevier.com/locate/cej Effect of alkali species on synthesis of K-F zeolitic materials from paper sludge ash for soil amendment Takaaki Wajima ⇑, Kenzo Munakata Graduate School of Engineering and Resource Sciences, Akita University, 1-1 Tegata-gakuen-cho, Akita 010-8502, Japan h i g h l i g h t s " Zeolite K-F and hydroxysodalite were formed in KOH–NaOH solutions. " Zeolite K-F and calcium hydrate minerals, such as katoite, were formed in KOH–LiOH solutions. + " Properties for K release depend on formation of an amorphous gel and zeolite K-F. 2+ " Properties for Ca release depends on formation of an amorphous gel and calcium hydrate minerals. " Zeolite K-F formation in KOH–LiOH solution with Li/(Li + K) = 0.25 is faster than that in KOH alone. a r t i c l e i n f o Article history: Available online xxxx Keywords: Paper sludge ash Zeolite K-F Alkali synthesis Soil amendment a b s t r a c t Zeolitic material including zeolite K-F (KAlSiO41.5H2O) with soil amendment properties was synthesized at 90 °C from paper sludge ash in KOH–NaOH and KOH–LiOH mixtures. The total alkali concentration in each solution was maintained at 4 mol/L and the relative amounts of the cationic species (K+/Na+ and K+/ Li+) were varied. Zeolite K-F crystal could be obtained in KOH–NaOH solutions with Na/(Na + K) ratios lower than 0.5 or KOH–LiOH solutions with Li/(Li + K) molar ratios lower than 0.25, while hydroxysodalite (Na6Al6Si6O248H2O) and katoite (Ca3Al2(SiO4)(OH)8) were formed at other cation molar ratios in each mixture. The observed concentrations of Si and Al in the solution during the reaction explain the synthesis of reaction products with soil amendment properties. The properties of a product intended for K+ release depend on formation of an amorphous gel and zeolite K-F, while that for Ca2+ release depends on formation of an amorphous gel and calcium hydrate minerals, such as katoite. The formation of zeolite K-F in a KOH–LiOH solution with Li/(Li + K) ratio = 0.25 is faster than that in KOH alone and the product with good properties, high cation exchange capacity and high released amount of Ca2+, for soil amendment could be obtained. Ó 2012 Elsevier B.V. All rights reserved. 1. Introduction Paper sludge is generated as an industrial waste during the manufacture of recycled paper products and the amounts generated are increasing annually. Over 3 million tons of sludge are discharged annually in Japan and approximately 8 and 2 million tons are discharged in the United States and the United Kingdom, respectively [1–3]. The sludge consists of organic fibers, inorganic clay-sized materials, and about 60% water and can be incinerated to produce paper sludge ash (PSA) by burning out the organic materials, thereby reducing the volume of waste. Although a small portion of the ash has been used as cement fillers, lightweight aggregates in the construction industry and other minor applications [4,5], most is dumped in landfills. The large daily output of ⇑ Corresponding author. Tel./fax: +81 18 889 2748. E-mail address: [email protected] (T. Wajima). PSA and the limited landfill capacity causes social and environmental problems. It is therefore essential to develop new ash utilization techniques for improved recycling. PSA contains SiO2, Al2O3, CaO and MgO and normally has extremely low potentially toxic components and has shown good capability for removal for phosphate ions from solution [6–8]. It has been reported that PSA can be treated with NaOH solution at low temperature (<100 °C) to improve the cation exchange capacity (CEC) through the synthesis of zeolite crystals on its surface [9– 13]. The resulting product has the ability to simultaneously remove ammonium and phosphate ions through ion exchange of the zeolite crystals with ammonium ions and chemical precipitation of phosphate ions with calcium ions dissolved from PSA [8,14–18]. Thus, this method can potentially produce environmentally friendly materials from waste PSA. In our previous study, zeolite K-F (KAlSiO41.5H2O) was synthesized from PSA in KOH solution [19]. Zeolite K-F is a potassium-type 1385-8947/$ - see front matter Ó 2012 Elsevier B.V. All rights reserved. http://dx.doi.org/10.1016/j.cej.2012.06.136 Please cite this article in press as: T. Wajima, K. Munakata, Effect of alkali species on synthesis of K-F zeolitic materials from paper sludge ash for soil amendment, Chem. Eng. J. (2012), http://dx.doi.org/10.1016/j.cej.2012.06.136 2 T. Wajima, K. Munakata / Chemical Engineering Journal xxx (2012) xxx–xxx zeolite in the edingtonite group and has a high affinity towards NHþ 4, making it potentially useful for soil amendment [20]. Because potassium, ammonium and phosphate ions are important ions in agricultural fertilizers, there is good potential for producing a useful soil amendment material that can simultaneously adsorb both ammonium and phosphate ions by treatment of PSA with KOH. However, the reaction rate for zeolite synthesis from PSA using KOH is slower than with other alkali species, such as NaOH and LiOH [19]. The reaction rate depends on many factors, such as temperature, pH and alkali species. It would be possible to promote the zeolite K-F synthesis reaction rate using two-component alkali solutions, NaOH/KOH and LiOH/KOH solution. The obtained product including zeolite K-F crystal, which has high cation exchange capacity, could be used for soil amendment by KCl washing to remove other cations, Na+ and Li+. Also, little information is available on the conversion of PSA into a product for removal of ammonium and phosphate using KOH solution. To our knowledge, no previous efforts have been made to determine the effect of alkali species during product synthesis on the latter’s soil amendment characteristics. In the present study, the effects of alkali species on the formation of K-F zeolite from PSA were examined. The aim of this study was to improve the formation rate of zeolite K-F in the products and to obtain the product with high soil amendment abilities, high cation exchange capacity (CEC) and high released Ca2+ to adsorb both ammonium and phosphate ions. component alkali solutions, NaOH/KOH and LiOH/KOH, were used as alkali sources. The total alkali concentration in the solution was maintained at 4 mol/L to clarify the difference of reaction behavior by the reference of our previous study [19]. The amounts of Na+ and K+ or of Li+ and K+ were varied under a constant OH concentration. Each reaction, using these alkali solutions, was carried out as follows. 100 g of ash were added to 1 L of alkali solution in a 1 L Erlenmeyer flask (made of poly methyl pentene) with a dimroth condenser and the mixture (slurry) was continuously stirred at 90 °C. Five mL aliquots of each slurry were removed at various time intervals to monitor the reaction process over a period of 24 h. The aliquots were filtered, the solid residue was washed with purified water (using a Millipore Milli-Q Labo system, USA) and dried for 12 h at 60 °C in a drying oven. The solid residue was then analyzed by XRD to determine the minerals present. The intensity of the major XRD peaks for mineralogical phases: zeolite K-F (2 2 2), hydroxysodalite (2 1 1), and katoite (4 2 0), were used to determine changes in the mineralogical phases. The chemical composition of the product was analyzed by the same method as used for the ash. The filtrates were analyzed by ICP-AES to determine the concentration of Si and Al in the alkali solution during the reaction. 2.3. Properties of the product for soil amendment The amounts of K+, Ca2+, Na+ and Li+ released from each product in an ammonium solution and CEC of the product were examined to indicate the soil amendment material properties by modified Schöerrenberg’s method [21]. 0.1 g of the solid residue was treated with 10 mL of 1 M ammonium acetate solution, separated from the solution by centrifugation, and added again to fresh 1 M ammonium acetate. This process was repeated three times for 20 min per exchange. The total amounts of K+, Ca2+, Na+ and Li+ ions in the ammonium acetate solution were analyzed by ICP. After three times ammonium acetate treatments, the sample washed with 80% EtOH solution two times in preparation of the + next step replacement. The NHþ 4 replaced by K in 10% KCl solution, in a procedure repeated three times. Finally, total amount of NHþ 4 in the solutions was analyzed by the method of Koyama et al. [22] to determine the CEC of the sample. The amounts of K+ and Ca2+ released from the product and CEC of the product were calculated as follows. 2. Materials and methods 2.1. Paper sludge ash Raw PSA was obtained from a major paper manufacturer in Japan. The chemical composition of the ash, determined by scanning electron microscopy (SEM) (Hitachi, S-2600H, Japan) equipped with energy dispersive spectrometry (EDS) (Horiba, EX-200, Japan) [19], is shown in Table 1. It is noted that Li content is analyzed by an inductively coupled plasma method (ICP-AES) (SPS4000, Seiko, Japan) after dissolving the sample in aqua regia, because EDS cannot detect Li content. The ash consisted mainly of SiO2 (43.0%), Al2O3 (23.9%) and CaO (22.9%) in the form of amorphous matter and the minerals gehlenite (Ca2Al2SiO7) and anorthite (CaAl2Si2O8), determined by X-ray diffraction (XRD) (Rigaku, Rint-2200U/PC-LH, Japan), as shown in Fig. 1. The remaining components were essentially low-concentration impurities, such as Na2O, K2O, MgO, Fe2O3 and TiO2. þ qM ¼ ðC M Þ=ðM wÞ½M : Kþ ; Ca2þ ; Naþ ; Li ; NHþ4 where CM is the total amount of each ions from samples (mg), M is the molar mass of K+, Ca2+ and NHþ 4 (g/mol), and w is the mass of PSA added (g). The units of qM were converted from mmol/g to cmol/kg, which is the general unit for soil properties, by multiplied by 10. This procedure was done three times, and the average of these data was used. 2.2. Zeolite synthesis PSA was partially converted to zeolites and other minerals by reaction with alkaline solutions. To investigate the effect of the cationic species in alkali solutions on zeolite synthesis, two- Table 1 Chemical compositions of PSA and the products. Reaction solution PSA The product 4M 1M 2M 3M 4M 3M 2M 1M 4M KOH NaOH + 3 M KOH NaOH + 2 M KOH NaOH + 1 M KOH NaOH KOH + 1 M LiOH KOH + 2 M LiOH KOH + 3 M LiOH LiOH Chemical composiiton (wt.%) SiO2 Al2O3 CaO Na2O K2O MgO Fe2O3 TiO2 Li 43.0 23.9 22.9 0.3 0.0 7.3 0.8 1.8 0.0 41.6 37.9 37.9 39.2 38.2 38.7 37.2 39.4 31.9 21.0 19.4 18.1 19.7 19.5 20.1 20.0 22.0 27.4 20.9 23.5 25.9 25.0 26.3 24.1 29.0 25.6 26.5 0.1 1.5 3.4 6.0 6.4 0.0 0.0 0.0 0.1 8.1 9.9 6.2 2.2 0.0 8.1 2.6 0.4 0.0 6.3 5.6 6.3 6.0 7.1 6.2 6.5 6.7 7.5 0.7 0.7 0.9 0.6 0.9 0.6 0.8 0.5 0.9 1.3 1.5 1.2 1.2 1.7 1.6 1.7 2.1 1.6 0.0 0.0 0.0 0.0 0.0 0.6 2.2 3.3 4.2 Please cite this article in press as: T. Wajima, K. Munakata, Effect of alkali species on synthesis of K-F zeolitic materials from paper sludge ash for soil amendment, Chem. Eng. J. (2012), http://dx.doi.org/10.1016/j.cej.2012.06.136 3 : Anorthite [CaAl2Si2O8] 200 100 0 0 10 20 2 30 [CuK 40 50 60 (degree)] Fig. 1. Powder X-ray diffraction patterns of PSA. 500 300 400 200 300 200 100 100 0 0 0 0.25 0.5 0.75 Ratio of Na+/total cation Zeolite K-F K+ Na+ 3. Results 3.1. Reaction in KOH–NaOH solution PSA was reacted in NaOH–KOH mixed solutions at 90 °C for 24 h. XRD patterns of the five reaction products are shown in Fig. 2. In the original ash (Fig. 1), two mineral phases, gehlenite and anorthite, existed. The intensity of the anorthite diffraction peaks in all products diminished, indicating that anorthite dissolves in NaOH–KOH mixed solutions, while the intensity of the gehlenite diffraction peaks in all products did not change over 24 h. The zeolite K-F (KAlSiO41.5H2O) formed when using Na/ (Na + K) molar ratios below 0.5, while hydroxysodalite (Na6Al6Si6O248H2O) formed at Na/(Na + K) molar ratios of 0.75 and 1.0. The chemical compositions of products synthesized using KOH– NaOH solution are shown in Table 1. The K content in the product was higher than that in the ash and increased with increasing K content in the mixed solution because of the formation of a crystalline zeolite K-F phase, while the Na content in the product increased with increasing Na content in the mixed solution, due to the formation of a crystalline hydroxysodalite zeolite phase. Intensities of the major mineralogical phases in the products, the amounts of K+, Ca2+ and Na+ released from the products, and CEC of the product after 24 h reaction are shown in Fig. 3. It is noted that the released amounts of K+, Na+ from raw ash and CEC of the ash are zero and the released amounts of Ca2+ is 30 cmol/kg. The intensity of zeolite K-F was almost constant at Na/(Na + K) = 0 and 0.25 but gradually decreased above Na/(K + Na) = 0.25, while that of hydroxysodalite was almost constant at Na/(Na + K) = 0 and 0.25 and gradually increased above Na/(K + Na) = 0.5. The amount of K+ released from the product was almost constant at Na/(Na + K) = 0 and 0.25 and gradually decreased above Na/(K + Na) = 0.5, which correlated with the amount of zeolite K-F in the product. On the other hand, θ α 1 and Na+ , and CEC (cmol/kg) Intensity (cps) : Gehlenite [Ca2Al2SiO7] Released amounts of K+, Ca2+, 300 Intensities of zeolite K-F and hydroxysodalite (cps) T. Wajima, K. Munakata / Chemical Engineering Journal xxx (2012) xxx–xxx Hydroxysodalite 2+ Ca CEC Fig. 3. Intensity of zeolite K-F and hydroxysodalite in the product and amounts of K+, Ca2+, and Na+ released from the product, and CECs of the product after 24 h reaction in each mixed solution. the amount of Na+ released from the product gradually increased with increasing Na+ content in the solution, which correlated with the amount of hydroxysodalite in the product. Regardless of Na+ content, the CEC of the product is almost constant, which are almost same as the sum of released amounts of K+ and Na+. The amount of Ca2+ released gradually increased to 500 cmol/kg and decreased to 300 cmol/kg at Na/(Na + K) = 1, with increasing Na/(Na + K) ratios in the mixed solution, which mean that the product synthesized in mixed solution contains higher releasable Ca than those in single solutions. The reaction process was monitored by measuring the concentrations of Al and Si in the solutions and analyzing the properties of the solid product for release of K+ and Ca2+ during each 24 h experiment. Although Ca is also a major elemental constituent of the ash, its concentration in solution is not a reliable indicator of the bulk system chemistry, because Ca is incorporated into insoluble solid phases in alkaline solutions [23]. Fig. 4 shows the concentrations of Al and Si in the solutions, together with the properties of the product solids, as a function of reaction time using the mixed solutions at each Na/ (Na + K) ratio. The concentration of Al in solution always exceeded that of Si, even though the Si concentration exceeded that of Al in the starting ash. In the case of 4 M KOH solution (Fig. 4a), the concentrations of Si and Al initially increased after introduction of PSA, then became almost constant after 4 h, and thereafter the Si concentration rapidly decreased to approximately 30 mM, while Al remained in the solution after 12 h. The K+ release from the solid product gradually increased to 100 cmol/kg, while that for Ca2+ release rapidly increased to 300 cmol/kg and became constant after 3 h of reaction. With increasing Na content in the mixed solution, the initial concentration of dissolved Si was lower and the Si concentration decreased more rapidly after its initial increase. On the contrary, the initial concentration of dissolved Al was higher and the Al concentration decreased more rapidly after its initial increase. The K+ release property of the solid product gradually increased during the reaction in all solutions but the amount of K+ released decreased with increasing Na content in the solution because of the decrease in zeolite K-F content in the solid product. In contrast, the amounts of Ca2+ released rapidly increased during initial stages in all solutions, which was correlated with the initial increases of the Si and Al concentrations, and then remained almost constant. With increasing Na content in the solution, the amount of Ca2+ released from the solid product increased, reaching a maximum amount of approximately 500 cmol/kg when Na/(K + Na) = 0.5 and 0.75, decreasing to 300 cmol/kg in 4 M NaOH solution. 3.2. Reaction in KOH–LiOH solution Fig. 2. Powder X-ray diffraction patterns of the product derived from PSA with KOH–NaOH mixtures; (a) 4 M KOH, (b) 3 M KOH + 1 M NaOH, (c) 2 M KOH + 2 M NaOH, (d) 1 M KOH + 3 M NaOH, and (e) 4 M NaOH. The experimental procedure described above was also applied to KOH–LiOH solutions. XRD patterns of the reaction products in Please cite this article in press as: T. Wajima, K. Munakata, Effect of alkali species on synthesis of K-F zeolitic materials from paper sludge ash for soil amendment, Chem. Eng. J. (2012), http://dx.doi.org/10.1016/j.cej.2012.06.136 4 8 12 16 Reaction time (h) 0 24 20 500 150 400 100 300 Si Al 50 K+ Ca2+ 200 100 0 0 4 8 12 16 0 24 20 Fig. 5. Powder X-ray diffraction patterns of the product derived from PSA using KOH–LiOH mixtures; (a) 4 M KOH, (b) 3 M KOH + 1 M LiOH, (c) 2 M KOH + 2 M LiOH, (d) 1 M KOH + 3 M LiOH, and (e) 4 M LiOH. Reaction time (h) 100 0 0 4 8 12 16 0 24 20 (cmol/kg) K and Ca 200 2+ 50 300 + K 2+ Ca (Fig. 5), which suggests that these two phases dissolve into the alkaline solution. Also, the minerals formed at high Li content were calcium hydrate minerals, such as hydrocalumite [Ca2Al(OH)7 3H2O], katoite (Ca3Al2(SiO4)(OH)8) and portlandite (Ca(OH)2). Zeolite K-F could be synthesized in mixed solutions with low Li/(Li + K) ratios of 0 or 0.25. The chemical compositions of the products synthesized in KOH–LiOH solutions are shown in Table 1. The K content in the product was higher than that in the ash and increased with increasing K content in the mixed solution, through the formation of a crystalline zeolite K-F phase. The Li content in the product increased with increasing Li content in the solution. The intensities of the major mineralogical phases in the product, the amounts of K+, Ca2+, and Li+ released from the product, and CEC of the product after 24 h reaction are shown in Fig. 6. The intensities of zeolite K-F in the products at Li/(Li + K) ratios = 0 and 0.25 were higher than that at other ratios, while those of katoite in the products at Li/(Li + K) ratios = 0 and 0.25 were lower than at other ratios. The amount of K+ released from the product was almost constant at 100 cmol/kg at Li/(Li + K) = 0 and 0.25 and gradually decreased to zero above Li/(Li + K) = 0.25, which correlated with intensity of zeolite K-F in the product. The amount of Li+ released from the product lineally increased with increasing Li content in the solution. The CEC of the product gradually decreased with increasing Li content, which are almost same as the amount of K+ released. This means that CEC of the product mainly depends on zeolite K-F, and released + Si Al Released amounts of 400 100 Released amounts of 500 150 Reaction time (h) 500 150 400 100 300 Si Al 50 + K 2+ Ca 200 100 0 0 4 8 12 16 20 0 24 100 + K 2+ Ca 400 300 200 50 100 0 0 4 8 12 16 Reaction time (h) 20 0 24 (cmol/kg) 500 Si Al K and Ca 150 + Si and Al concentrations (mM) Reaction time (h) (e) α θ + Fig. 4. Concentrations of Si and Al in the solutions during reaction, and the K and Ca2+ release properties of the solid products for soil amendment after synthesis, for each mixed solution; (a) 4 M KOH, (b) 3 M KOH + 1 M NaOH, (c) 2 M KOH + 2 M NaOH, (d) 1 M KOH + 3 M NaOH, and (e) 4 M NaOH. each KOH–LiOH mixed solution after 24 h reaction are shown in Fig. 5. For NaOH–KOH solutions, only anorthite dissolved into the alkaline solution, while gehlenite remained in the solids throughout all reactions. In the case of KOH–LiOH solutions, however, the reactions differed from the previous cases. First, both anorthite and gehlenite decreased with increasing Li content in the solution 300 800 600 200 400 100 200 0 0 0 0.25 0.5 0.75 Ratio of Li+/total cation Zeolite K-F Katoite K Ca Li CEC 1 and Li+ , and CEC (cmol/kg) 0 Released amounts of K+, Ca2+, 100 0 Intensities of zeolite K-F and katoite (cps) 200 50 Released amounts of 300 Released amoutns of 400 K+ and Ca2+ (cmol/kg) 100 K 2+ Ca K+ and Ca2+ (cmol/kg) Si and Al concentrations (mM) 500 + Si Al 2+ (d) 150 Released amounts of (c) Si and Al concentrations (mM) (b) Si and Al concentraitons (mM) (a) K+ and Ca2+ (cmol/kg) T. Wajima, K. Munakata / Chemical Engineering Journal xxx (2012) xxx–xxx Si and Al concentrations (mM) 4 Fig. 6. Intensity of zeolite K-F and katoite in the product and amounts of K+, Ca2+, and Li+ released from the product and CECs of the product after 24 h reaction for each mixed solution. Please cite this article in press as: T. Wajima, K. Munakata, Effect of alkali species on synthesis of K-F zeolitic materials from paper sludge ash for soil amendment, Chem. Eng. J. (2012), http://dx.doi.org/10.1016/j.cej.2012.06.136 200 40 100 20 0 0 4 0 24 8 12 16 20 Reaction time (h) 400 K+ 2+ Ca 300 100 Si Al 80 60 200 40 100 20 0 0 4 8 12 16 Reaction time (h) 20 100 0 24 400 + Si Al 80 K Ca2+ 300 60 200 40 100 20 0 0 4 8 12 16 20 Reaction time (h) 100 400 80 300 60 Si Al 40 K+ 2+ Ca 200 100 20 0 0 4 8 12 16 20 Reaction time (h) 0 24 K+ and Ca2+ (cmol/kg) Released amounts of 0 24 K and Ca (cmol/kg) 300 (cmol/kg) K+ 2+ Ca Si Al 60 K and Ca 80 K and Ca (cmol/kg) 400 100 K and Ca (cmol/kg) 20 2+ 8 12 16 Reaction time (h) + 4 Released amounts of 0 the solid product for K+ and Ca2+ release during each 24 h experiment (Fig. 7). As observed in KOH–NaOH experiments, the concentration of Al was always higher than that of Si in solution. The trends in the concentration curves in Fig. 7a and b are almost same as those for KOH–NaOH solutions, except those in Fig. 7c–e exhibit different shapes from the other reactions. In the case of Li/(K + Li) = 0.25 (Fig. 7b), the concentrations of Si and Al increased initially after introduction of PSA and then the Al content became almost constant after 2 h, while the Si concentration rapidly decreased to approximately 30 mM. The changes shown in Fig. 7b occurred faster than those shown in Fig. 7a. The K+ release from the solid product increased to 100 cmol/kg and became almost constant after 4 h, meaning that K+ release from the product at Li/ (K + Li) = 0.25 reached a maximum faster than when using KOH alone. In contrast, the Ca2+ release rapidly increased to 300 cmol/ kg and became constant after 3 h of reaction, which was similar to using KOH alone. In the case of Li/(K + Li) ratios higher than 0.5 (Fig. 7c–e), the concentrations of Si and Al initially increased after introduction of PSA and the Si and Al concentrations decreased. The rates of decrease were faster with increasing Li content in the solution and the amounts of Si and Al dissolved decreased. The amount of K+ released from the solid product decreased because of the decrease in zeolite K-F crystal content. The Ca2+ release rapidly increased to 300 cmol/kg and then decreased, which was correlated with the Al content in the solution. The rate of decrease in Ca2+ release was also higher with increasing Li content in the solution. 2+ 0 24 0 5 4. Discussion + 100 20 Released amoutns of 200 2+ K 2+ Ca Si Al 40 + + Released amounts of 300 60 2+ Si and Al concentraitons (mM) 80 + (e) 400 100 Released amounts of (d) Si and Al concentraitons (mM) (c) Si and Al concentrations (mM) (b) Si and Al concentrations (mM) (a) Si and Al concentrations (mM) T. Wajima, K. Munakata / Chemical Engineering Journal xxx (2012) xxx–xxx Fig. 7. Concentrations of Si and Al in the solution during reaction, and the K+ and Ca2+ release properties of the solid product for soil amendment after synthesis in each mixed solution; (a) 4 M KOH, (b) 3 M KOH + 1 M LiOH, (c) 2 M KOH + 2 M LiOH, (d) 1 M KOH + 3 M LiOH, and (e) 4 M LiOH. Li+ has no relationship to cation exchange reaction. The amount of Ca2+ released gradually decreased to zero with increasing Li/(Li + K) ratio in the mixed solution, which correlated with the intensity of katoite. The reaction process was monitored by measuring the concentrations of Al and Si in the solutions and analyzing the properties of A number of studies have dealt with the alkaline reaction of incinerated ash, including low Ca content (<10 wt.%) [9,24–34]. In these studies, the concentration of Si in solution was invariably greater than that of Al, under all reaction conditions. However, in the case of PSA with high Ca content, the opposite concentration relation was found in our previous study [8,19] and in the current study, as shown in Figs. 4 and 7, in which the concentration of Al was greater than that of Si under all reaction conditions. Catalfamo et al. [35] reported that the high affinity of Ca2+ ions for the silicate species inhibits the dissolution of Si into the alkali solution. The reason for the difference in the relative concentrations of Si and Al may be related in part to the much higher Ca content in the starting ash used in the current study compared to that in the previous studies. Previous studies of alkali reactions with incinerated ash tested the effects of pH, alkali concentration, temperature, or alkali species on reactions but, to date, none has studied the dependence of the alkali species on the properties of the product derived from high-Ca PSA, especially the synthesis of zeolite K-F. In the case of KOH–NaOH solutions, only anorthite dissolved into the alkali, which resulted in a solid reaction product containing hydroxysodalite and zeolite K-F, which crystallized from solution, and undissolved gehlenite. However, in the case of KOH–LiOH solution, both anorthite and gehlenite dissolved into the solution, and the calcium aluminosilicate mineral, katoite, was formed. Furthermore, the XRD patterns suggest that, for higher Li content in the solution, the amorphous component of the products (indicated by a broad hump between 20° and 40°) was less abundant than with lower Li content solutions. It is considered that amorphous phases are dissolved and subsequently converted into calcium aluminosilicate crystals in higher Li content solutions. Murayama et al. [36] proposed the following mechanism for zeolite formation from coal fly ash: release of Si and Al from the ash into the alkaline solution, followed by the formation of an aluminosilicate gel as a precursor to crystalline solids, and finally Please cite this article in press as: T. Wajima, K. Munakata, Effect of alkali species on synthesis of K-F zeolitic materials from paper sludge ash for soil amendment, Chem. Eng. J. (2012), http://dx.doi.org/10.1016/j.cej.2012.06.136 6 T. Wajima, K. Munakata / Chemical Engineering Journal xxx (2012) xxx–xxx crystallization of zeolites from the gel. In our experiments, the Al concentration in solution was always higher than that of Si. In the case of KOH–NaOH solutions and KOH–LiOH solutions with Li content lower than Li/(Li + K) = 0.25, assuming that gel formation preceded crystallization in our experiments, the higher Al concentration resulted in an aluminosilicate gel with a low Si:Al ratio, from which Al-rich zeolite phases formed (i.e., hydroxysodalite and zeolite K-F). These results agree with the prediction of Barrer [37] that elevated Al dissolution will lead to unique reaction products, such as zeolites with low Si:Al ratios. However, in the case of KOH–LiOH solutions with Li contents higher than Li/(Li + K) = 0.5, a high Ca content was supplied into the solution by dissolution of gehlenite and the production of an amorphous calcium aluminosilicate gel, using Si and Al in the solution, increased, to crystallize katoite. Barrer [37] also concluded that the order for gelation rates was Li+ > Na+ > K+, which corresponds to the order of hydrated ionic radius. The relative reaction rates observed in our experiments, as shown in Figs. 4 and 7, are consistent with these results. Also, as the rate of gelation reaction is faster, the dissolution rate promote by keeping chemical equilibrium. In our experiments, the products mainly contained zeolite K-F, hydroxysodalite and katoite. Zeolite K-F is a member of the edingtonite group, hydroxysodalite is a member of the sodalite group, and katoite is a member of the garnet group. Zeolite K-F and hydroxysodalite have cation exchange ability, wherein K+ releases from zeolite K-F and Na+ from hydroxysodalite by ion exchange with NHþ 4 . Therefore, the product synthesized in KOH–NaOH solution has high CEC. On the other hands, katoite, hydrocalumite and portlandite has little CEC, and the product synthesized in KOH– LiOH solution with high Li content, including these calcium minerals, indicates low CEC. Okada et al. [38] reported that poorly crystalline calcium aluminum silicate hydrate (CASH) gels were hydrothermally synthesized from mixtures of PSA, calcia and silica in NaOH solution, and showed excellent simultaneous sorption abilities for ammonium by ion exchange and for phosphate ions by the reaction with dissolved Ca2+ ions. It can be considered that release of Ca2+ mainly depends on the amorphous CASH gel in the product and that part of the K+ release is from CASH gel. Furthermore, the released Ca2+ suggests that, for higher Li content solutions, the amorphous CASH in the products is less abundant in katoite formation and the amount of released Ca2+ decreases. In the case of KOH–NaOH solution, it is unclear why the amount of Ca2+ released decreased to 300 cmol/kg in NaOH solution. The only difference is that the solution is mixture of K+ and Na+ ions, which may influence to gelation reaction by interaction of two cations. These results are in good accordance with the change in Si and Al concentrations in the solutions and the properties of the solids during the reaction. As shown in Figs. 4 and 7a and b, part of the soluble Si and Al content in raw ash was dissolved into alkali solution. Here, the Si content decreased due to gelation with Ca and Si, and Si and Al, leaving Al in solution after 24 h of alkali reaction. As shown in Fig. 7c–e, not only a major part of the Si and Al content but the Ca content in the ash was dissolved into alkali solution, where the Si and Al content decreased due to gelation with the high Ca content. Because the Ca dissolution was higher, a larger amount of CASH gel was formed, crystallizing katoite. In summary, we propose the following mechanism for the chemical conversion of PSA into the zeolite K-F. PSA is mainly composed of gehlenite, anorthite, and other amorphous phases, and the order of solubility with respect to alkali reaction is: amorphous phases > anorthite > gehlenite. During alkali reaction in KOH– NaOH solution, most of the amorphous phase and the anorthite dissolves into the solution, and precipitates as amorphous CASH and aluminosilicate gel to form zeolite crystals, zeolite K-F in solutions with Na/(Na + K) ratios lower than 0.5, and hydroxysodalite in solutions with other ratios, leaving Al3+ in solution. Under the condi- tions for obtaining products containing zeolite K-F, with increasing Na content in the solution, the amount of K+ released gradually decreases and that of Ca2+ increases, along with the time required to reach the maximum amount of Ca2+ released. In the case of KOH–LiOH solutions, in solutions where the Li/(Li + K) ratio is lower than 2.5, most of the amorphous phase and the anorthite dissolves into the solution and precipitates as amorphous CASH and aluminosilicate gel to form zeolite K-F. At higher Li solution content, the amount of K+ released is similar and the time required to reach the maximum amount of released K+ is shorter, while that of Ca2+ is slightly lower. However, at Li content in the solution higher than Li/(Li + K) = 0.5, not only amorphous phase and anorthite but also gehlenite dissolves in the solution and the precipitation of amorphous CASH to katoite is promoted. The product displays low release of K+ and Ca2+, which is not good for soil amendment. From these results, products containing zeolite K-F can be synthesized in KOH–NaOH solutions with Na/(Na + K) = 0, 0.25 and 0.5, or in KOH–LiOH solutions with Li/(Li + K) = 0 and 0.25. Under zeolite K-F synthesis conditions, for all five products, the amount of Ca2+ released from the products for phosphate fixation are enough, and the time to the Ca2+ release capability are shorter than 4 h. The CEC of the product synthesized in all three solutions after 24-h reaction are almost same, 100 cmol/kg, but the time to reach 100 cmol/kg for the product synthesized in KOH–LiOH solution with Li/(Li + K) = 0.25 is faster than those in other solutions. From these results, the optimal conditions for the synthesis of soil amendment materials from PSA would involve KOH–LiOH solutions with Li/(Li + K) = 0.25, because a product with high CEC and high capability for releasing Ca2+ can be synthesized faster than when using other synthesis solutions. 5. Conclusions Soil amendment materials containing zeolite K-F were synthesized from PSA in KOH–NaOH and KOH–LiOH solutions at 90 °C. Zeolite K-F, hydroxysodalite, katoite, hydrocalumite and portlandite were synthesized in the products. Using KOH–NaOH mixtures, zeolite K-F was synthesized in solutions with Na/(Na + K) ratios lower than 0.5, while hydroxysodalite was synthesized at other Na/(Na + K) ratios. Increasing the Na/(Na + K) ratio to 0.75 gradually decreased the K+ released from the product, increased the Na+ released from the product, and increased Ca2+ release, while the CEC of the product is almost constant. In KOH–LiOH mixtures, zeolite K-F was synthesized at Li/(Li + K) ratios lower than 0.25, while calcium hydrate minerals, such as katoite, hydrocalumite and portlandite, were synthesized using other ratios. Increasing the Li content to Li/(Li + K) = 0.75 gradually decreased K+ and Ca2+ release from the product, increasing Li+ release from the product, while the CEC of the product decreases. The concentrations of Si and Al in the solution observed during the reaction explain the synthesis of products with differing soil amendment properties. The release of K+ from the product depends on formation of precursor gel and zeolite K-F crystals, while Ca2+ release depends on formation of CASH gel. The formation of zeolite K-F in the KOH–LiOH solutions with Li/(Li + K) ratio = 0.25 is faster than using KOH solution alone, and the product would have good properties for soil amendment after KCl washing. This was identified as the best conditions for synthesis of soil amendment materials from PSA in this work. Acknowledgments This work was supported by a Research Promotion Grant from the Iron and Steel Institute of Japan, and MEXT/JSPS Grant-in-Aid for Young Scientists (B): 24710086. Please cite this article in press as: T. Wajima, K. Munakata, Effect of alkali species on synthesis of K-F zeolitic materials from paper sludge ash for soil amendment, Chem. Eng. J. (2012), http://dx.doi.org/10.1016/j.cej.2012.06.136 T. Wajima, K. Munakata / Chemical Engineering Journal xxx (2012) xxx–xxx References [1] R.G. Barton, W.R. Seeker, H.E. Bostian, The behavior of metals in municipal sludge incinerators, Trans. Inst. Chem. Eng. 69 (1991) 29–36. [2] T.H.Y. Tebbutt, Incineration of waste water sludges, Proc. Inst. Civil Eng. Water Marit. Energy 112 (1995) 39–47. [3] H. Ishimoto, T. Otiguchi, M. Yasuda, Use of papermaking sludge into microporous crystal material, J. Mater. Civil Eng. 12 (2000) 310–313. [4] M. Singh, M. Garg, Cementitious binder from fly ash and other industrial wastes, Cem. Concr. Res. 29 (1999) 309–314. [5] R. Kikuhi, Recycling of municipal solid waste into cement clinker, Resour. Conserv. Recy. 31 (2001) 137–147. [6] V.K. Jha, Y. Kameshima, A. Nakajima, K. Okada, K.J.D. Mackenzie, Multifunctional uptake behavior of materials prepared by calcining waste paper sludge, J. Environ. Sci. Health A41 (2006) 703–719. [7] M. Hojamberdiev, Y. Kameshima, A. Nakajima, K. Okada, Z. Kadirova, Preparation and sorption properties of materials from paper sludge, J. Hazard. Mater. 151 (2008) 710–719. [8] T. Wajima, K. Munakata, Material conversion from paper sludge ash in NaOH 3 solution to synthesize adsorbent for removal of Pb2+, NHþ from 4 and PO4 aqueous solution, J. Environ. Sci. 23 (2010) 718–724. [9] S.P. Mun, B.J. Ahn, Chemical conversion of paper sludge incineration ash into synthetic zeolite, J. Ind. Eng. Chem. 7 (2001) 292–298. [10] T. Ando, T. Sakamoto, O. Sugiyama, K. Hiyoshi, N. Matsue, T. Henmi, Adsorption mechanism of Pb on paper sludge ash treated by NaOH hydrothermal reaction, Clay Sci. 12 (2004) 243–248. [11] T. Wajima, K. Kuzawa, H. Ishimoto, O. Tamada, T. Nishiyama, The synthesis of zeolite-P, Linde Type A, and hydroxysodalite zeolites from paper sludge ash at low temperature (80 °C): optimal ash-leaching condition for zeolite synthesis, Am. Mineral. 89 (2004) 1694–1700. [12] H. Ishimoto, M. Yasuda, Technology for converting papermaking sludge into micro-porous crystal materials, NTT Tech. Rev. 9 (1997) 51–56. [13] T. Wajima, Y. Ikegami, Zeolite synthesis from paper sludge ash via acid leaching, Chem. Eng. Commun. 195 (2008) 305–315. [14] K. Okada, Y. Ono, Y. Kameshima, A. Nakajima, K.D.J. MacKenzie, Simultaneous uptake of ammonium and phosphate ions by compounds prepared from paper sludge ash, J. Hazard. Mater. 141 (2007) 622–629. [15] H. Ishimoto, M. Yasuda, O. Sasaki, Application of new materials from paper recycling for purifying domestic wastewater, NTT Tech. Rev. 15 (2003) 43–47. [16] T. Wajima, M. Haga, K. Kuzawa, H. Ishimoto, O. Tamada, K. Ito, T. Nishiyama, R.T. Downs, J.F. Rakovan, Zeolite synthesis from paper sludge ash at low temperature (90 °C) with addition of diatomite, J. Hazard. Mater. 132 (2006) 244–252. [17] T. Wajima, T. Shimizu, Y. Ikegami, Synthesis of zeolites from paper sludge ash 3 and their ability to simultaneous removal NHþ 4 and PO4 , J. Environ. Sci. Health A42 (2007) 345–350. [18] T. Wajima, T. Shimizu, Y. Ikegami, Zeolite synthesis from paper sludge ash with addition of diatomite, J. Chem. Technol. Biotechnol. 83 (2008) 921–927. [19] T. Wajima, H. Ishimoto, K. Kuzawa, K. Ito, O. Tamada, M.E. Gunter, J.F. Rakovan, Material conversion from paper sludge ash in NaOH, KOH, and LiOH solution, Am. Mineral. 92 (2007) 1105–1111. 7 [20] V.S. Jakkula, C.D. Williams, T.J. Hocking, M.A. Fullen, High selectivity and affinity of Linde type F towards NHþ 4 on application as a soil amendment for maize growth, Micropor. Mesopor. Mater. 88 (2006) 101–104. [21] Development of New Utilization of Materials (DNUM), Natural Zeolite and its Utilization, No. 111 Committee, Japan Society for the promotion of Science, Tokyo, 1994, pp. 318–325. [22] M. Koyama, T. Hori, Y. Kitayama, IARC Reports, Kyoto Univeristy 2 (1978) 11– 14. [23] J. Kragten, Atlas of Metal-ligand Equilibria in Aqueous Solution, Ellis Horwood Limited, Chichester, 1978. [24] N. Sigemoto, H. Hayashi, K. Miyaura, Selective formation of Na-X zeolite from coal fly ash by fusion with sodium hydroxide prior to hydrothermal reaction, J. Mater. Sci. 28 (1993) 4781–4786. [25] N. Shigemoto, S. Sugiyama, H. Hayashi, Characterization of Na-X, Na-A, and coal fly ash zeolites and their amorphous precursors by IR, MAS-NMR and XPS, J. Mater. Sci. 30 (1995) 5777–5783. [26] C.F. Lin, H.C. His, Resource recovery of waste fly ash: synthesis of zeolite-like materials, Environ. Sci. Technol. 29 (1995) 1109–1117. [27] M. Park, J. Choi, Synthesis of phillipsite from fly ash, Clay Sci. 9 (1995) 219– 229. [28] V. Berkgaut, A. Shinger, High capacity cation exchanger by hydrothermal zeolitization of coal fly ash, Appl. Clay Sci. 10 (1996) 369–378. [29] G.C.C. Yang, T.Y. Yang, Synthesis of zeolites from municipal incinerator fly ash, J. Hazard. Mater. 62 (1998) 75–89. [30] C. Poole, H. Prijatama, N.M. Rice, Synthesis of zeolite absorbents by hydrothermal treatment of PFA waste: a comparative study, Miner. Eng. 13 (2000) 831–842. [31] X. Querol, N. Moreno, J.C. Umaña, A. Alastuey, E. Hernández, A. Lopez-Soler, F. Plana, Synthesis of zeolites from coal fly ash: an overview, Int. J. Coal Geol. 50 (2002) 413–423. [32] H. Tanaka, Y. Sakai, R. Hino, Formation of Na-A and -X zeolites from waste solution in conversion of coal fly ash to zeolites, Mater. Res. Bull. 37 (2002) 1873–1884. [33] N.J. Coleman, D.S. Brassington, Synthesis of Al-substituted 11 Å tobermorite from newsprint recycling residue: a feasibility study, Mater. Res. Bull. 38 (2003) 485–497. [34] N.J. Coleman, Synthesis, structure and ion exchange properties of 11 Å tobermorites from newsprint recycling residue, Mater. Res. Bull. 40 (2005) 2000–2013. [35] P. Catalfamo, G. Patane, P. Primerano, S.D. Pasquale, F. Corigliano, The presence of calcium in the hydrothermal conversion of amorphous aluminosilicates into zeolites: interference and removal, Mater. Eng. 5 (1994) 159–173. [36] N. Murayama, H. Yamamoto, J. Shibata, Mechanism of zeolite synthesis from coal fly ash by alkali hydrothermal reaction, Int. J. Miner. Process. 64 (2002) 1– 17. [37] R.M. Barrer, Hydrothermal Chemistry of Zeolites, Academic Press, New York, 1992. [38] K. Okada, Y. Ono, Y. Kameshima, A. Nakajima, K.J.D. MacKenzie, Simultaneous uptake of ammonium and phosphate ions by compounds prepared from paper sludge ash, J. Hazard. Mater. 141 (2007) 622–629. Please cite this article in press as: T. Wajima, K. Munakata, Effect of alkali species on synthesis of K-F zeolitic materials from paper sludge ash for soil amendment, Chem. Eng. J. (2012), http://dx.doi.org/10.1016/j.cej.2012.06.136