* Your assessment is very important for improving the workof artificial intelligence, which forms the content of this project
Download Multiferroic Metal Organic Frameworks with Perovskite Architecture
Survey
Document related concepts
Transcript
Florida State University Libraries Electronic Theses, Treatises and Dissertations The Graduate School 2010 Multiferroic Metal Organic Frameworks with Perovskite Architecture Prashant Jain Follow this and additional works at the FSU Digital Library. For more information, please contact [email protected] THE FLORIDA STATE UNIVERSITY COLLEGE OF ARTS AND SCIENCES MULTIFERROIC METAL ORGANIC FRAMEWORKS WITH PEROVSKITE ARCHITECTURE By PRASHANT JAIN A Dissertation submitted to the Department of Chemistry and Biochemistry in partial fulfillment of the requirements for the degree of Doctor of Philosophy Degree Awarded: Summer Semester, 2010 The members of the committee approve the dissertation of Prashant Jain defended on April 15, 2010. __________________________________ Harold W. Kroto Professor Directing Dissertation __________________________________ James Brooks University Representative __________________________________ Naresh Dalal Committee Member __________________________________ Lei Zhu Committee Member Approved: _____________________________________ Joseph B. Schlenoff, Chair, Department of Chemistry and Biochemistry The Graduate School has verified and approved the above-named committee members. ii ACKNOWLEDGEMENTS I would like to thank my supervisors Prof. Harry Kroto and Prof. Tony Cheetham who have supported me throughout this dissertation process. I am also thankful to Prof. Naresh Dalal who has advised me throughout this PhD. I would also like to thank Cheetham, Kroto, and Dalal group members, present and past, with whom I was fortunate to work. In particular, I would like to mention Vasanth Ramachandran, Dr. Steve Acquah, Dr. Crystal Merrill, Dr. Russel K. Feller, Dr. Gautam Gundiah, Dr. Katherine Page, Dr. Kinson Kam, and Dr. Thirumurugan Alagarsamy. I am also grateful to various interns who worked with me. I would like to especially thank Rose who supported me and brought laughter and stability to my life. Finally, I would like to thank my family for all of their support all these years. iii TABLE OF CONTENTS ACKNOWLEDGEMENTS ................................................................................................ iii TABLE OF CONTENTS.................................................................................................... iv LIST OF TABLES ............................................................................................................... ix LIST OF FIGURES ...............................................................................................................x ABSTRACT ........................................................................................................................ xiv CHAPTER 1 .......................................................................................................................... 1 INTRODUCTION ................................................................................................................ 1 1.1 Metal organic frameworks .................................................................................... 1 1.1.1 General introduction ............................................................................................ 1 1.1.2 Open and dense frameworks............................................................................ 3 1.2 Ferroelectrics and multiferroics ......................................................................... 7 1.2.1 Ferroelectric ............................................................................................................ 7 1.2.1.1 Crystallography and ferroelectrics ............................................................ 9 1.2.2 Multiferroic materials....................................................................................... 11 1.2.3 Glossary of terms ................................................................................................ 12 1.3 Ferroelectric metal organic frameworks ..................................................... 14 iv 1.3.1 Rochelle salt, KDP, and triglycine sulfate (TGS). ................................... 14 1.3.2 Ferroelectric MOFs ............................................................................................ 17 1.4 Summary .................................................................................................................... 26 CHAPTER 2 ....................................................................................................................... 28 EXPERIMENTAL TECHNIQUES AND SYNTHESIS ............................................ 28 2.1 Experimental techniques .................................................................................... 28 2.1.1 Single crystal and powder X-ray diffraction ........................................... 28 2.1.1.1 Single crystal X-ray diffraction.................................................................. 28 2.1.1.2 Synchrotron versus laboratory sources for X-ray diffraction ..... 29 2.1.2 Neutron diffraction ............................................................................................ 31 2.1.2 Magnetic susceptibility measurements using a SQUID magnetometer................................................................................................................. 34 2.1.3 Heat capacity measurements ........................................................................ 36 2.1.4 Dielectric properties (capacitance measurements) ............................ 38 2.2 Solvothermal synthesis ....................................................................................... 39 CHAPTER 3 ....................................................................................................................... 42 ORDER – DISORDER PHASE TRANSITION IN [(CH3)2NH2]Zn(HCOO)3 .. 42 3.1 Background............................................................................................................... 42 v 3.2 Synthesis .................................................................................................................... 43 3.3 Structure .................................................................................................................... 45 3.4 Structural phase transition ................................................................................ 46 3.5 Dielectric and heat capacity measurements ............................................... 48 3.6 Summary and conclusions ................................................................................. 51 3.7 Resulting publication and comments ............................................................ 52 CHAPTER 4 ....................................................................................................................... 53 MULTIFERROIC METAL ORGANIC FRAMEWORKS: [(CH3)2NH2]M(HCOO)3(M=Mn, Ni, Co, & Fe) ...................................................... 53 4.1 Background............................................................................................................... 53 4.2 Synthesis .................................................................................................................... 54 4.3 Crystal growth mechanism ................................................................................ 55 4.4 Structure .................................................................................................................... 57 4.4.1 Crystallographic data for DMAFeF .............................................................. 58 4.5 Magnetic properties of DMAMF ....................................................................... 61 4.5.1 Magnetic susceptibility .................................................................................... 61 4.6 Structural phase transition ................................................................................ 63 4.6.1 Temperature dependent X-ray diffraction data .................................... 63 vi 4.7 Low temperature structure ............................................................................... 64 4.8 Dielectric measurements .................................................................................... 70 4.9 Heat capacity measurements ............................................................................ 74 4.10 Summary and conclusions ............................................................................... 77 4.11 Resulting publications and comments ....................................................... 78 CHAPTER 5 ....................................................................................................................... 79 GLASSY BEHAVIOR OF (CH3)2NH2Zn(HCOO)3 .................................................. 79 5.1 Background............................................................................................................... 79 5.2 Debye law and remnant specific heat............................................................ 80 5.3 NMR measurements.............................................................................................. 82 5.4 Results and discussion ......................................................................................... 84 5.5 Summary and conclusions ................................................................................. 90 5.6 Resulting publications and comments .......................................................... 91 CHAPTER 6 ....................................................................................................................... 92 SUMMARY AND CONCLUSIONS............................................................................... 92 APPENDIX ......................................................................................................................... 95 CRYSTALLOGRAPHIC INFORMATION FILES ..................................................... 95 vii Dimethylammonium iron formate: ........................................................................ 95 Dimethylammonium zinc formate ....................................................................... 106 Dimethylammonium manganese formate ........................................................ 113 Dimethylammonium nickel formate ................................................................... 123 Low temperature dimethylammonium manganese formate ................... 134 LIST OF REFERENCES .............................................................................................. 144 BIOGRAPHICAL SKETCH .......................................................................................... 160 viii LIST OF TABLES Table 1: 32 point groups. Polar point groups have been highlighted in blue. ..................................................................................................................................... 10 Table 2: Comparison of single crystal and powder diffraction .................. 31 Table 3: Structure parameters for 1 from single crystal X-ray diffraction at room temperature.................................................................................................... 46 Table 4: Structure parameters for DMAFeF ....................................................... 58 Table 5: Atomic parameters of DMAFeF.............................................................. 59 Table 6: Anisotropic displacement parameters for DMAFeF, in Å2 ......... 59 Table 7: Selected geometric information for DMAFeF .................................. 59 Table 8: Structural parameters for the low temperature polar phase of DMAMnF ............................................................................................................................ 66 Table 9: Arrhenius parameters for the CH3 protons in DMAZnF in the PE and FE phases.................................................................................................................. 89 ix LIST OF FIGURES Figure 1: MOF-5, a porous cubic zinc terephthalate which is topologically analogous to ReO3. Gray spheres denote carbon, red oxygen, and white hydrogen, with ZnO4 tetrahedra in blue. ......................... 4 Figure 2: Schematic representation of coordination polymers and extended inorganic hybrids; (a) and (b) show 1-D and 2-D coordination polymers, respectively, while (c) shows a system that has inorganic connectivity in two dimensions and is connected in the third ..................... 6 Figure 3: Cubic perovskite structure. The small B cation (in black) is at the center of an octahedron of oxygen anions (in gray). The large A cations (white) occupy the unit cell corners......................................................... 9 Figure 4: Ferromagnets (ferroelectrics) form a subset of magnetically (electrically) polarizable materials such as paramagnets and antiferromagnets (paraelectrics and antiferroelectrics). The intersection (red hatching) represents materials that are multiferroic. (Adopted from ref. 17) ................................................................................................................................ 11 Figure 5: Views of the unit cell content of Rochelle salt (paraelectric phase) (left), KDP (paraelectric phase) (middle) and TGS (ferroelectric phase) (right) .................................................................................................................. 16 Figure 6: Molecular structure of crystal state of [CoCl3(H-MPPA)] and its 3D packing view along the b axis and electric hysteresis loop recorded at room temperature (adopted from ref. 116). ................................................... 18 Figure 7: Molecular structure of [Ni3(TBPLA)2( 3-O)](ClO4)4(H2O)5 where water and ClO4− are omitted for clarity117 ........................................... 20 Figure : Dielectric permittivity εr) of a single crystal of [Ni3(TBPLA)2( 3-O)](ClO4)4(H2O)5 as a function of temperature upon application of an electric field approximately parallel to the a (E//a), b(E//b), and c(E//c) crystal axes directions. The measurements were made at a high frequency of 1 MHz (adopted from ref. 117)...................... 21 x Figure 9: A schematic illustration of the molecular structure of RbI0.82MnII0.20MnIII0.80[FeII(CN)6]0.80 [FeIII(CN)6]0.14·H2O ................................. 22 Figure 10: (a) Crystal structure of [Mn3(HCOO)6](C2H5OH) viewed along the b-axis: Mn, pink; C, gray; O, blue; H, pale sky blue. The C and O atoms of guest C2H5OH molecules are shown by open circles. (b) The arrangement of guest ethanol molecules along the channel ...................... 23 Figure 11: (a) Temperature dependence of the magnetization of [Mn(HCOO)6](C2H5O( ( = Oe . b Dielectric constants εr) of [Mn(HCOO)6](C2H5OH) for the field E//a (blue), b (green), and c (pink). The red line represents εr (E//a) of the crystal with deuterated ethanol, [Mn(HCOO)6](C2H5OD). (c) The hysteresis loop of [Mn(HCOO)6](C2H5O( E//a . d The /εr vs T curve of [Mn(HCOO)6](C2H5OH). In the dielectric measurements, the relatively high speed of the temperature change − °/min was adopted to avoid the escaping of guest molecules .............................................................................. 25 Figure 12: Difference between the relative sizes of the cross-sections between X-ray and neutron for some elements. .............................................. 33 Figure 13: Scheme of a SQUID magnetometer. ................................................. 35 Figure 14: Cutaway view showing the PPMS -16T magnet and probe. Inset shows a heat capacity puck............................................................................ 38 Figure 15: Cutaway of a general purpose (high temperature) 23 mL Parr acid digestion bomb, used in the solvothermal synthesis of all the compounds described in this dissertation.......................................................... 40 Figure 16: Crystal structure of [(CH3)2NH2]Zn(HCOO)3 , 1. It has the same architecture as an ABX3 perovskite, with A=(CH3)2NH2+, B=Zn2+ and X=HCOO-. .................................................................................................................. 45 Figure 17: Synchrotron powder patterns collected with a wavelength of 0.608Å at APS: red data obtained at room temperature, black data at 100K. ................................................................................................................................... 48 Figure 18: Dielectric constant of 1 measured as a function of temperature. .................................................................................................................... 50 xi Figure 19: Heat capacity of 1 as function of temperature............................ 51 Figure 20: Optical images of [(CH3)2NH2]Mn(HCOO)3. .................................. 55 Figure 21: AFM image of a multiferroic MOF dimethylammonium manganese formate. Crystals grow layer by layer during the room temperature crystallization. Growth is perpendicular to the <012> plane. ................................................................................................................................... 56 Figure 22: Building block of [(CH3)2NH2]Mn(HCOO)3, DMMnF. The DMA cation (A) is at the center of an ReO3 type cavity, formed by manganese (B) and formate (X) ions. Nitrogen is disordered over three positions. 57 Figure 23: Temperature dependence of χM of DMAMnF at H = 1000 Oe from 2 to 300 K. 142........................................................................................................ 62 Figure 24: Magnetic susceptibility of DMAFeF ................................................. 63 Figure 25: PXRD pattern for DMAMnF, collected at the Advanced Photon Source, ANL = . Ǻ, BM-11) .......................................................................... 64 Figure 26: Rietveld refinement of PXRD data of DMANiF collected at 10 K with monoclinic unit cell of a=14.451(8) Å b=8.376(3) Å c=8.952(4) Å and β= . °. Pattern is in red color, simulated pattern is in blue and difference plot is in orange. .............................................................................. 66 Figure 27: Reietveld refinement of powder neutron data collected at NIST with the low temperature Cc phase of DMAMnF. Black is the experimental data, Red is simulated pattern, Blue is the Bragg positions and Green is the difference between experimental and simulated. ........ 70 Figure 28: Dielectric constant of DMAMnF as a function of temperature with no magnetic field and with that of 5 Tesla. The measurements were done at 1 kHz, using amplitude of 1V. .................................................................. 71 Figure 29: Dielectric constant of DMAMnF measured as a function of temperature and magnetic field. Bottom two plots reveal a magnetodielectic coupling. .......................................................................................................... 73 xii Figure 30: Heat capacity of DMAMnF as a function of temperature. The anomalies relating to electrical ordering and magnetic ordering are clearly visible................................................................................................................... 75 Figure 31: Effect of magnetic field on the magnetic phase transition in DMAMnF on cooling. .................................................................................................... 76 Figure 32: Temperature dependence of Q-Band EPR spectra of DMAMnF. ........................................................................................................................... 77 Figure 33: Temperature dependent of low-temperature specific heat (plotted as C/T3 versus T). ......................................................................................... 81 Figure 34: Crystal structure of [(CH3)2NH2]Zn(HCOO)3 at room temperature. The purple spheres represent the three dynamically disordered sites for the N atom of the dimethylammonium formate moiety. The freezing of these positions is proposed to be the mechanism underlying the ferroelectric transition at 156 K. ............................................. 83 Figure 35: Temperature dependence of the CH3 proton spin-lattice relaxation rate, T1-1, of DMAZnF. A, B and, C refer to the glass, ferroelectric (FE) and, paraelectric (PE) phases, respectively. Solid lines are the theoretical fits to the BPP equation. Arrows indicate the direction of the temperature scan. The inset shows the Arrhenius plot for this path. ..................................................................................................................... 85 Figure 36: Thermal cycles for paths II and III, wherein the spin-lattice relaxation rate jumps back to the main path (path I), are highlighted by arrows. The dashed lines are the projected paths had no jumps occurred. Solid (thick) lines are the theoretical fits to the BPP equation. ............................................................................................................................................... 86 xiii ABSTRACT Multiferroic materials are rare compounds featuring at least two ferroic properties with a majority of them displaying (anti)ferro – electricity or magnetism. Currently, the most famous compounds displaying such behavior are oxide perovskites. One of the most common mechanisms for ferroelectric behavior in perovskites, requires an empty d-orbital which usually means that the material is diamagnetic. Hence there is a need for multiferroic materials in which two independent mechanisms can determine the electric and magnetic ordering. I was able to achieve this using hybrid perovskites. Hybrid perovskites of general formula (CH3)2NH2M(HCOO)3 have a ReO3 type cage made up of formate and metal ions. The metal ions sit at the corners of the cubes and are connected to each other via coordination bonding with oxygen of the formate ion. The dimethylammonium cation is located at the center of this cavity. The amine hydrogen atoms make hydrogen bonds with the oxygen atoms of the metal formate framework. Because of this hydrogen bonding, the nitrogen of the ammonium cation is disordered over three equal positions at room temperature. Cooling down these materials below 180 K leads to a lowering in symmetry, a result of the ordering of nitrogen atoms. This phase transition is associated with a dielectric anomaly. Carefully done dielectric measurements show that the anomaly is a -type peak xiv usually associated with paraelectric to ferroelectric phase transition. Low temperature single crystal measurements aided by powder X-ray diffraction and neutron diffraction experiments show that low temperature phase crystallizes in monoclinic symmetry and Cc space group. Cc belongs to one of the 10 polar point groups which are requirements for ferroelectricity. Furthermore, magnetic fields seem to affect this dielectric anomaly, suggesting that these hybrid perovskites have a magnetodielectric effect. This phase transition was studied in detail by electron paramagnetic resonance, heat capacity, and 1H NMR relaxation time measurements. Close to 0 K, specific heat data suggest that there is a remnant specific heat, a classic signature of amorphous or glassy materials. NMR data shows that these hybrid materials are indeed glassy below 40 K with many confirmations with close underlying energies. This effect is related to the rotation of methyl motors. NMR results also show an anomaly at the same temperature where dielectric anomaly is present. Methyl protons slow down by a factor to suggest that dielectic anomaly is indeed due to the ordering of nitrogen atoms. xv CHAPTER 1 INTRODUCTION Hybrid inorganic-organic or metal-organic frameworks (MOFs) are a recently-identified class of crystalline material, consisting of metal ions linked together by organic bridging ligands, and are a new development on the interface between molecular coordination chemistry and materials science.1-10 A range of novel structures has been prepared which feature amongst the largest pores known for crystalline compounds, very high absorption capacities and complex sorption behavior not seen in aluminosilicate zeolites.3, 11-14 Most of the efforts in this field have been focused on discovering porous MOFs for gas storage applications, and not much attention has been given to other physical properties for which oxides are usually known for.15-16 In this dissertation, I focus on the research that I have conducted in one such field called multiferroics.17-18 I have demonstrated that it is possible to achieve multiferroic behavior in this upcoming class of MOF compounds.19-21 In this opening chapter, I will give an introduction to metal organic frameworks, multiferroics, and, briefly talk about ferroelectric metal organic frameworks. 1.1 Metal organic frameworks 1.1.1 General introduction Metal organic frameworks are crystalline materials built from inorganic and organic building blocks with infinite inorganic−organic connectivity in at least one dimension.1, 4, 6, 10, 22-27 Sometimes they are referred to as 1 hybrid inorganic-organic frameworks and a subset of which are inorganic−coordination polymers.28 These framework materials have recently developed into an important new class of solid-state materials with approximately 2800 ISI web of science papers published in the year 2009. This is, mainly, due to the infinite possibilities of new frameworks materials that can be created by varying the inorganic/organic ratio.16 These materials can also offer wide range of physics and chemistries. Furthermore, it is possible to tailor their properties by changing metal ions and/or organic ligands despite maintaining the structure topology. Hybrid frameworks exist for a wide range of metals and involve a diverse range of organic ligands. Most of the published work involves transition metals, including zinc, but there is a growing body of literature around rare-earth based systems, which are of interest for their optical properties.29-31 In addition, there has been a certain amount of effort with p-block elements, especially aluminium, gallium and tin, plus a recent growth of interest in magnesium, driven by the search for lightweight materials for hydrogen storage.32-34 In terms of organic ligands, much of the recent focus has been on connectivity through oxygen atoms of carboxylic acid groups.4, 35-36 Rigid dicarboxylic acids, such as benzene-1,4-dicarboxylic acid, have proved very versatile, as have the simple but more flexible aliphatic systems, such as succinic and glutaric acids.37-39 The simplest member of this family, oxalic acid, has been used extensively.40-42 As will be discussed later, 2 monocarboxylic acids can also form hybrids, and there has been some recent effort with formic and acetic acids.43-50 Nor is the field limited to carboxylic acids, since phosphonic acids and phenolic acids can also form hybrid frameworks.51-54 Beyond network formation involving M–O linkages, there has been a reasonable amount of work with other types of ligands, such as pyridyls and imidazoles, as well as mixed ligands that offer the possibility of more than one type of connection, e.g. M–O plus M–N or M–S.7-8, 22, 26, 55 Much remains to be explored in the area of these more complex linkages. 1.1.2 Open and dense frameworks Hybrid frameworks could be divided into two broad categories: open and dense frameworks. A majority of the publications in the field are based upon the open frameworks with potential applications in gas storage, gas separation, catalysis, and sensors. A vast range of coordination polymers or supramolecular architectures with different dimensionalities – 1-D, 2-D and 3-D – have been discovered in recent years.15 3-D open frameworks display some of the highest surface areas known and are widely regarded as the potential hydrogen storage materials for various energy related applications including the transportation industry. Some of the most striking examples of porous 3-D coordination polymers can be found in the work of Yaghi, O'Keeffe and co-workers, in which they have exploited bridging of simple Zn4O groups via rigid aromatic dicarboxylates such as benzene-1,4-dicarboxylic acid to build networks with remarkably low densities and high porosity, such as MOF-5.9 They have shown that 3 large families based upon the same architecture can be created by altering the length or other chemical details of the organic linker.56 In addition to architectures based upon the topologies of simple inorganic structures; there has also been success in building porous hybrids based upon known zeolite structures. These include zinc, cadmium and indium coordination polymers that adopt the ABW, BCT, MTN, RHO and SOD topologies.7 Imidazoles-based ligands are particularly effective for this purpose since they can mimic the Si–O–Si angles that are found in typical zeolites. Figure 1: MOF-5, a porous cubic zinc terephthalate which is topologically analogous to ReO3. Gray spheres denote carbon, red oxygen, and white hydrogen, with ZnO4 tetrahedra in blue. Focusing on dense hybrid frameworks, only recently has some attention been paid to these materials. They are frameworks with extended inor4 ganic, for example M-O-M, connectivity in at least one dimension (Figure 2) or with limited porosity, for example, cation templated hybrid frameworks. These materials show interesting magnetic, optical, electronic and dielectric properties. They exhibit rich diversity of behavior in these areas and present some exciting opportunities for the physics community. Cation-templated hybrid MOFs, described in this text at a later stage, are an important subclass of dense frameworks. They do not have extended inorganic connectivity; however, due to the template, amajority do not have any accessible pores. 5 Figure 2: Schematic representation of coordination polymers and extended inorganic hybrids; (a) and (b) show 1-D and 2-D coordination polymers, respectively, while (c) shows a system that has inorganic connectivity in two dimensions and is connected in the third Such extended inorganic hybrid materials not only open up a vast area of new chemical and structural permutations, but they also provide a basis for creating materials with properties that are traditionally found 6 in metal oxides. Thus it might be possible to make hybrid materials that are metallic, superconducting, or high temperature ferromagnets. 1.2 Ferroelectrics and multiferroics 1.2.1 Ferroelectric A ferroelectric material is one that undergoes a phase transition from a high-temperature phase that behaves as an ordinary dielectric (so that an applied electric field induces an electric polarization, which goes to zero when the field is removed) to a low-temperature phase that has a spontaneous polarization whose direction can be switched by an applied field57. Many properties of ferroelectric materials are analogous to those of ferromagnets, but with the electric polarization, P, corresponding to the magnetization, M; the electric field, E; corresponding to the magnetic field, H; and the electric displacement, D, corresponding to the magnetic flux density, B.58 For example, ferroelectric materials also have domains and show a hysteretic response of both polarization and electric displacement to an applied electric field. As a result, they also find applications in data storage. The onset of spontane- ous electric polarization coincides with a divergence in the static dielectric permeability, ε, because at Tc, an infinitesimally small exter- nal electric field will cause a large polarization. They find application as capacitors because their concentration of electric flux density results in high dielectric permeabilities. They are also used in electromechanical 7 transducers and actuators (because the change in electric polarization is accompanied by a change in shape). Early work on ferroelectric materials focused primarily on Rochelle salt,59 KNa(C4H4O6)·4H2O. Although studies of Rochelle salt were pivotal in establishing many of the basic properties of ferroelectric materials, the complex structure and large number of ions per unit cell made it difficult to elucidate a coherent theory of ferroelectricity from the results of experiments on this material.60-66 The most widely studied and widely used ferroelectrics today are perovskite-structure oxides, ABO3, which have the prototypical cubic structure shown in Figure 3. The cubic perovskite structure is characterized by a small cation, B, at the center of an octahedron of oxygen anions, with large cations, A, at the unit cell corners. Below the Curie temperature, there is a structural distortion to a lower-symmetry phase accompanied by the shift off-center of the small cation. The spontaneous polarization derives largely from the electric dipole moment created by this shift. The comparatively simple perovskite structure and the small number of atoms per unit cell have made detailed theoretical studies of perovskite ferroelectrics possible and resulted in a good understanding of the fundamentals of ferroelectricity. 8 Figure 3: Cubic perovskite structure. The small B cation (in black) is at the center of an octahedron of oxygen anions (in gray). The large A cations (white) occupy the unit cell corners. 1.2.1.1 Crystallography and ferroelectrics The crystal classification of a material has immediate implications for ferroelectric effects. There are 32 crystal classes 9 11 of them have a centre of symmetry (centrosymmetric) and cannot support ferroelectricity Of the remaining 21, the O-point group (432) also excludes ferroe lectricity. The remaining 20 classes all exhibit the piezoelectric effect Of these, 10 (Table 1) have a unique polar direction. Table 1: 32 point groups. Polar point groups have been highlighted in blue. 10 1.2.2 Multiferroic materials Figure 4: Ferromagnets (ferroelectrics) form a subset of magnetically (electrically) polarizable materials such as paramagnets and antiferromagnets (paraelectrics and antiferroelectrics). The intersection (red hatching) represents materials that are multiferroic. (Adopted from ref. 17) Multiferroics are rare materials that exhibit more than one primary ferroic order parameter simultaneously within a single phase.17, 67-76 These ferroic order parameters are ferroelasticity, ferroelectricity and ferromagnetism (See glossary of terms at the end of the section).77-78 However, the current trend is to exclude the requirement for ferroelasticity79-83 in practice, but to include the possibility of ferrotoroidic order84-85 (glossary of terms) in principle. Moreover, the classification of a multiferroic has been broadened to include antiferroic order (glossary of terms). 11 Magnetoelectric coupling73, 75, 86-89, on the other hand, may exist whatever the nature of magnetic and electrical order parameters, and can for example occur in paramagnetic ferroelectrics90-93 (Figure 4). Magnetoelectric coupling may arise directly between the two order parameters, or indirectly via strain.72, 94-97 Currently there is a high level of interest in magnetoelectrics and multiferroics. Given that there are indeed few multiferroic materials, whatever the microscopic reasons, the relentless drive towards ever better technology is aided by the study of novel materials. Aspirations here include transducers and magnetic field sensors, but tend to centre on the information storage industry. It was initially suggested that both magnetization and polarization could independently encode information in a single multiferroic bit. Four-state memory has recently been demonstrated98, but in practice it is likely that the two order parameters are coupled. 99 Coupling could in principle permit data to be written electrically and read magnetically. This is attractive, given that it would exploit the best aspects of 100-104 (FeRAM) and magnetic data storage, while avoiding the problems associated with reading FeRAM and generating the large local magnetic fields needed to write. 1.2.3 Glossary of terms Ferroics Ferroelectric materials possess a spontaneous polarization that is stable and can be switched hysteretically by an applied electric field. 12 Antiferroelectric materials possess ordered dipole moments that cancel each other completely within each crystallographic unit cell. Ferromagnetic materials possess a spontaneous magnetization that is stable and can be switched hysteretically by an applied magnetic field. Antiferromagnetic materials possess ordered magnetic moments that cancel each other completely within each magnetic unit cell. Ferroelastic materials display a spontaneous deformation that is stable and can be switched hysteretically by an applied stress. Ferrotoroidic materials possess a stable and spontaneous order parameter that is taken to be the curl of a magnetization or polarization. By analogy with the above examples, it is anticipated that this order parameter may be switchable. Ferrotoroidic materials have evaded unambiguous observation. Ferrimagnetic materials differ from antiferromagnets because the magnetic moment cancellation is incomplete in such a way that there is a net magnetization that can be switched by an applied magnetic field. Order parameter coupling Magnetoelectric coupling describes the influence of a magnetic (electric) field on the polarization (magnetization) of a material. 13 Piezoelectricity describes a change in strain as a linear function of applied electric field, or a change in polarization as a linear function of applied stress. Piezomagnetism105-107 describes a change in strain as a linear function of applied magnetic field, or a change in magnetization as a linear function of applied stress. Electrostriction108-109 describes a change in strain as a quadratic function of applied electric field. Magnetostriction110-112 describes a change in strain as a quadratic function of applied magnetic field. 1.3 Ferroelectric metal organic frameworks A summary of recent work is presented in this section describing noncentrosymmetric or homochiral metal-organic frameworks which belongs to 10 polar point groups with potential ferroelectric properties. It is necessary to give a brief introduction of three typical well-known ferroelectrics: Rochelle salt, KDP and triglycine sulfate (TGS).57 1.3.1 Rochelle salt, KDP, and triglycine sulfate (TGS). The well-known oldest ferroelectric crystal is Rochelle salt59(see Figure 5). The most outstanding property of Rochelle salt is that it exhibits two 14 curie points. The space group below 255 K and above 297 K is orthorhombic P21212, corresponding to the paraelectric phase while between the temperature range the space group is monoclinic P21, corresponding to the ferroelectric phase.113 The paraelectric–ferroelectric transition is of the order–disorder type. In the crystal structure, there are rows of tartrate ions parallel to the a axis, linked along the b axis by rows of alternating K and Na ions. Every tartrate ion is surrounded by six tartrate ions. K and Na ions act as a bridge among tartrate ions.114 The K ions adopt a bicapped trigonal prism geometry and the Na ions display a distorted octahedral geometry via the coordination with the O atoms from acetate, OH and water. The crystal structure of Rochelle salt is a combination of two kinds of different chains along the a axis. The main difference among the ferroelectric structure and the two paraelectric structures is in the orientation of each tartrate ion with respect to the crystallographic axes. It is assumed that the ferroelectricity is produced by two nonequivalent chains along the a axis, each with a different polarization vector parallel to the a axis. As well-known hydrogen-bonded ferroelectrics, the pure inorganic compound KDP has been the most intensively studied over the second half of the last century57. There are extensive hydrogen bonds in its structure that gives rise to a diamondoid network (see Figure 5). 15 Figure 5: Views of the unit cell content of Rochelle salt (paraelectric phase) (left), KDP (paraelectric phase) (middle) and TGS (ferroelectric phase) (right) KDP undergoes paraelectric–ferroelectric phase transition at 123 K. The paraelectric phase adopts the tetragonal space group I−42d (point group D2d) where the ferroelectric phase adopts the orthorhombic space group Fdd2 (polar point group C2v). The spontaneous polarization of KDP arises from the collective site-to-site transfer of protons in the O– H O bonds, along with the displacive deformation of PO4 − ions. Upon deuteration, KDP shows a huge isotopic effect of Curie temperature with an increase of about 90 K. TGS is another typical ferroelectric discovered by Matthias et al. in 1956115. It is synthesized from amino acid glycine and sulfuric acid. In the crystal structure, there are three types of glycine molecules, i.e., I, II and III (see Figure 5). The structural formula of TGS can be best written as [(H3N+CH2COOH)2(H3N+CH2COO−)·SO4 −], among which the glycinium ion H3N+CH2COOH corresponds to glycines I and II while the zwitterion H3N+CH2COO− to glycine III. The C, N and O atoms in glycine II and III lo16 cate almost in-plane while the N atom in glycine I deviates of ca. 0.27 Å from the OCO plane. The sulfate exhibits a distorted tetrahedral geometry. The glycines and sulfate ions are connected through hydrogen bonds. The direction of spontaneous polarization Ps is due to the orientation of the polar group NH3+ of glycine I molecule along the b axis. TGS displays a perfect hysteresis loop along the b axis and its Ps reaches 3.5 C cm− at room temperature. It shows a typical second order fer- roelectric phase transition at Curie temperature of 322 K. The paraelectric phase is monoclinic P21/m belonging to the centrosymmetrical class 2/m while the ferroelectric phase below the transition temperature is monoclinic P21 belonging to the polar point group 2. TGS crystal is one of the best materials for use as a sensitive element in room temperature infrared detectors and imaging systems due to its excellent ferroelectric and pyroelectric properties115. 1.3.2 Ferroelectric MOFs [Co(II)Cl3(H-MPPA)] is one of the successful ferroelectric examples, where its electric hysteresis loop reaches perfect spontaneous polarization status, since the exploration of potential ferroelectrics based on MOFs 116. It was prepared through the reaction of dichloride (R)-2methylpiperazine (MPPA) bi-cation with CoCl2. X-ray crystal structural determination clearly shows that the local coordination environment around Co center is a distorted tetrahedron composed of three terminal Cl atoms and one N atom from unprotonated N atom of MPPA (see Figure 6). One of the N atoms from the MPPA ligand is protonated and loses 17 its coordination ability. Thus, three H atoms (H1, H2A and H2B) form hydrogen bonds between three Cl atoms (Cl1, Cl2 and Cl3) to lead to the formation of 3D framework created through hydrogen bonds as shown in Figure 6. A careful investigation shows that three bond distances of Co–Cl are not equal to each other and display some differences (Co– Cl1 = 2.225 Å; Co–Cl1 = 2.283 Å; Co–Cl1 = 2.260 Å). As expected, the bond distance of Co1–N1 is in the normal range of Co–N bond lengths. The piperazine ring adopts a stable chair-type conformation. Figure 6: Molecular structure of crystal state of [CoCl3(H-MPPA)] and its 3D packing view along the b axis and electric hysteresis loop recorded at room temperature (adopted from ref. 116). [Co(II)Cl3(H-MPPA)] crystallizes in a chiral space group P21 which belongs to one of the ten polar point groups (C2), its ferroelectric property would occur in principle. Figure 6 shows that an electric hysteresis loop was indeed observed when the applied electric field was set at about 28 kV cm− . A spontaneous polarization (Ps ≈ 6.8 C cm− ) occurred in the measuring conditions and remanent polarization (Pr ≈ 6.2 C cm− ) was almost equal to that of Ps. Ps of 1 is twice that of TGS 18 (Ps = 3.5 C cm− ) and significantly larger than that of KDP. The direction of the spontaneous polarization in the ferroelectric phase might be perpendicular to the chains and to the Cl HN hydrogen bonds, analogous to KDP and other KDP-type ferroelectrics.116 [Ni3(TBPLA)2(μ3-O)](ClO4)4(H2O)5: Another H-bonded discrete homochiral ferroelectric MOF is Ni3(TBPLA)2( 3-O)(ClO4)4(H2O)5 (3) (TBPLA = (S)- , , -2,4,6-trimethylbenzene-1,3,5-triyl- tris(methylene)-tris-pyrrolidine-2-carboxylic acid), which is obtained by the hydrothermal reaction of Ni(ClO4)2·6H2O with TBPLA117. Frame- work crystallizes in a chiral space group P21 belonging to one of the ten polar point groups (C2). The TBPLA ligand is a zwitterionic neutral molecule similar to the amino acid in TGS, and acts as a hexadentate chelator with each of the ligand's bidentate carboxylate moieties coordinated to the Ni atoms (see Figure 7). The molecular charge is balanced by four free ClO4− anions and one 3-O atom. The TBPLA ligand takes an all- cis coordination mode resembling the shape of a parachute. Each Ni center displays a slightly distorted octahedron geometry which is composed of six O atoms, i.e., four of the O atoms from four different carboxylate groups and two from the oxo group and H2O. Similarly, 3D framework occurs in this framework through strong H-bond (see Figure 7). 19 Figure 7: Molecular structure of [Ni3(TBPLA)2( 3-O)](ClO4)4(H2O)5 where water and ClO4− are omitted for clarity117 Fu et. al reported that this framework displays large permittivity anisotropy along three crystallographic axes (See Figure 8). The dielectric anisotropy ratios of r//c/ r//b and r//c/ r//a are ca. 3.47 and 2.22, re- spectively, showing temperature-independence. Polarization − electric field hysteresis curve was of typical ferroelectrics; the spontaneous polarization, Ps, reaches a value of ca. 3.4 nC/cm2 at room temperature while the coercive field is relatively low, reaching ca. 0.8 kV/cm which is smaller than those typically found in ferroelectric polymers. 20 Figure 8: Dielectric permittivity εr) of a single crystal of [Ni3(TBPLA)2( 3O)](ClO4)4(H2O)5 as a function of temperature upon application of an electric field approximately parallel to the a (E//a), b(E//b), and c(E//c) crystal axes directions. The measurements were made at a high frequency of 1 MHz (adopted from ref. 117). RbI0.82MnII0.20MnIII0.80[FeII(CN)6]0.80 [FeIII(CN)6]0.14·H2O was reported by Ohkoshi et al. at low temperature118. It is arguable whether a cyano bridged compound could be considered a metal organic framework. The crystal structure resembles that of Prussian blue (see Figure 9). They used variable-temperature powder x-ray diffraction (PXRD) measurements reveal that the title compound displays phase transition at high temperature (276 K, a centrosymmetric space group F43m) and low temperature (184 K, an acentric space group F222 belonging to nonpolar point group D2). The magnetization vs. temperature plots of the low-temperature phase show ferromagnetism with a Curie temperature of 11 K. The P–E plot for the low-temperature phase at 77 K, when ap21 plying a field up to 100 kV cm− , shows an electric hysteresis loop with a Pr of 0.041 C cm− and an Ec of 17.5 kV cm− . The ferroelectricity may be related to mixing of FeII, FeIII, Fe vacancy, MnII, and Jahn–Tellerdistorted MnIII. One of the possible mechanisms of the ferroelectricity could be the creation of a local electric dipole moment because of an iron vacancy. In addition, the difference in ionic radii among four metal ions and MnIII Jahn–Teller distortion enhance the local structural distortion, for example, the deviation of M–CN–M linkages from a ° confi- guration. Probably, in such a deviated structure, polarization will be induced by the applied electric field, and the polarization can be held by the structural flexibility of the cyano-bridged 3D network. Figure 9: A schematic illustration of the molecular structure of I II Rb 0.82Mn 0.20MnIII0.80[FeII(CN)6]0.80 [FeIII(CN)6]0.14·H2O 22 [Mn3(HCOO)6](C2H5OH) 119-120: Research from Kobayashi group showed, for the first time, a guest induced ferroelectric phase transition in porous metal organic frameworks. More than often, depending on the size of the solvent, when porous MOFs are synthesized, their pores contain solvent molecules. Depending on the size and the interaction of the solvent molecules with the framework body, these solvent molecules are usually disordered at room temperature. Figure 10: (a) Crystal structure of [Mn3(HCOO)6](C2H5OH) viewed along the b-axis: Mn, pink; C, gray; O, blue; H, pale sky blue. The C and O atoms of guest C2H5OH molecules are shown by open circles. (b) The arrangement of guest ethanol molecules along the channel 23 Kobayashi et al. showed that porous Mn3(HCOO)3 is a ferrimangnet below 8.5 K. 119-120. The guest molecules are easily removed under vacuum and/or by heating. Framework shows a dielectric anomaly below 150 K when the framework was loaded with polar solvents, for example, H2O, CH3OH, or C2H5OH. This is due to the ordering of these polar guest molecules which are otherwise randomly disordered at room temperature. Figure 10 shows the structure of [Mn3(HCOO)6](C2H5OH) viewed along the b-axis and the arrangement of guest molecules along the channel. Figure 11 shows the magnetic and structural phase transition leading to the dielectric anomaly. As expected, dielectric anomaly is highly anisotropic. 24 Figure 11: (a) Temperature dependence of the magnetization of [Mn(HCOO)6](C2H5O( ( = Oe . b Dielectric constants εr) of [Mn(HCOO)6](C2H5OH) for the field E//a (blue), b (green), and c (pink). The red line represents εr (E//a) of the crystal with deuterated ethanol, [Mn(HCOO)6](C2H5OD). (c) The hysteresis loop of [Mn(HCOO)6](C2H5OH) E//a . d The /εr vs T curve of [Mn(HCOO)6](C2H5OH). In the dielectric measurements, the relatively high speed of the temperature change − °/min was adopted to avoid the escaping of guest molecules 25 1.4 Summary Multiferroics are rare compounds with more than one ferroic properties. Traditionally, metal oxides are known to show this rare but very interesting behavior. Recent years have seen the resurgence of the field mainly due to the long term technological applications. Metal organic frameworks, especially the dense MOFs, are capable of showing this behavior as they are structurally similar to oxides. Also, it is possible to make homochiral MOFs by starting with a chiral template or organic linker. Most of the known MOF ferroelectric materials fall into this category of homochiral MOFs. However, homochiral frameworks cannot be used for many typical multiferroic applications because they do not exhibit a paraelectric to ferroelectric phase transition. As discussed in section 1.3.2, some MOFs can also exhibit ferroelectric behavior by creating a local electric dipole moment because of a vacancy. But these are very uncommon. Guest induced ferroelectricity is an interesting concept via which almost all the porous frameworks could potentially be turned into ferroelectrics or into multiferroics if they are made up of paramagnetic ions. Low molecular weight polar guest molecules interact weakly with the framework lattice and are disordered at room temperature. Upon lowering the temperature, these molecules order giving rise to net polarization. However, as the authors pointed out the dielectric and polarization values are not reproducible. Volatile guest molecules tend to evaporate when approaching room temperature or on storing for long 26 time. Hence, there is a need for new class of multiferroic MOFs which are stable and can give reproducible results. 27 CHAPTER 2 EXPERIMENTAL TECHNIQUES AND SYNTHESIS 2.1 Experimental techniques 2.1.1 Single crystal and powder X-ray diffraction 2.1.1.1 Single crystal X-ray diffraction For sample preparation, a suitable single crystal is usually selected under a polarizing microscope and glued to a thin glass fiber with cyanoacrylate (Superglue) adhesive. Crystal structure determinations by single crystal X-ray diffraction were performed on a Bruker SMART-CCD diffractometer equipped with a normal focus, 2.4kW sealed tube X-ray source (Mo Kα radiation, = 0.71073Å) operating at 50kV and 40mA. A hemisphere of intensity data was collected at various temperatures. An empirical correction on the basis of symmetry equivalent reflections was applied using the SADABS program121. The structure was solved by direct methods using SHELXTL and difference Fourier syntheses122. The relevant details of structure determination are presented in different chapters. Full matrix least-squares refinement against |F2| was carried out using the SHELXTL package of programs122. The hydrogen atoms were found in the Fourier difference map; the proton remaining on the acid was restrained. The last cycles of refinement included atomic positions and anisotropic thermal parameters for all atoms except hydrogen, which used isotropic thermal parameters. At the end of the chapter are supplementary tables containing atom coordinates, bond lengths and 28 angles, anisotropic displacement parameters, hydrogen atom coordinates, and hydrogen bonding specifics. 2.1.1.2 Synchrotron versus laboratory sources for X-ray diffraction All the standard laboratory sources used for X-ray diffraction experiments generate radiation using the same physical principles but can vary in their technical details. In our case, we have been using a BraggBrentano geometry using a sealed tube generator. The tube of X-rays is made from a source of electrons and a metallic cathode put in the chamber under high vacuum. The source of electrons is a filament of tungsten heated by an electric current, which expels electrons by the thermic effect. A high voltage from 40kV to 60kV is applied between the source of electrons (cathode) and the metallic anode and accelerates the electrons. Due to the way in which radiation is produced, only a discrete number of wavelengths and a broad background are available. For conventional X-ray diffraction, we have been using Kα of copper. The generation of X-rays in a synchrotron radiation source involves a different technology. From mechanics and the Maxwell equations, it is well known that charged particles moving under the influence of an accelerating field emit electromagnetic radiation. This radiation can be used for diffraction purpose if the charged particles have a high acceleration corresponding to a speed close to the speed of light. This is realized in a synchrotron radiation facility where the charged particles (electrons or positrons) are kept circulating within an evacuated cavity 29 on a closed path (the ring) by a number of curved magnets (the bending magnets). The different beamlines used for the different experiments are tangential to the particle trajectory. The advantage of such facility is the very bright source which is available and the possibility to tune the wavelength to the value required for a particular experiment. Most of the powder X-ray work for this dissertation was done on PANalytical or Brucker machines at University of California, Santa Barbara and University of Cambridge respectively. Synchrotron data used in this work were collected at 11BM beamline (advanced photon source) at the Argonne national laboratory. Materials were characterized by both single and powder X-ray diffraction. Paraelectric and ferroelectric phases were solved using single Xray technique. Powder X-ray diffraction (PXRD) was usually used to check the purity of the sample. Synthesis conditions were optimized using PXRD. In case of low temperature phase, both powder and single crystal X-ray data were used along with neutron data to solve the structure. Rietveld refinements were performed wherever required to get unit cell parameters or to check the purity of a given sample. X’pert Highscore was used for preliminary Rietveld refinements for phase identification. Fullprof and GSAS were used for more advanced and difficult refinements. 30 Table 2: Comparison of single crystal and powder diffraction Single crystal diffraction Powder diffraction Determination of the crystal structure with high precision and accuracy Identification of compounds or mixtures of different compounds Information on ordering in crystals Investigations on homogeneity Information on thermal motion and dynamics in crystals Information on stress, strain and crystal size Very precise bond lengths Quantitative phase analysis Imprecise for cell parameters. Precise in fractional coordinates Determination of the crystal structure (Usually not as precise as from single crystal structure analysis) 2.1.2 Neutron diffraction Neutron beams are produced by nuclear reactions, such as nuclear fission or fusion, or by spallation of nuclei by accelerated particles. Since for the moment nuclear fusion cannot be controlled sufficiently to produce stable neutron sources, all neutron centers use nuclear reactors (fission) and spallation sources. Spallation is the process in which a 31 heavy nucleus emits a large number of nucleons as a result of being hit by a high-energy proton. A number of properties of the neutron make it very useful for the study of solids. Since, neutrons are uncharged particles and of small dimensions (about 10− the size of an atom), they have a very penetrating power. While the atomic scattering factors for X-rays increase through- out the periodic table due to increasing numbers of electrons, this is not the case for neutrons. For neutrons, although there is a small increase of nuclear scattering factor with the mass number of the element, it is largely hidden by resonance effects which vary in a seemingly arbitrary fashion from atom to atom. As a result, the neutron scattering factors for different nuclei are in general all of the same order within a factor 4. The difference between the relative size of cross-sections (scattering factor) for X-ray and neutron is illustrated in Figure 12. 32 Figure 12: Difference between the relative sizes of the cross-sections between X-ray and neutron for some elements. As a consequence, neutron diffraction is more sensitive to the light atoms like oxygen or hydrogen than X-ray diffraction. In this respect, these two techniques are complementary. Another main difference between X-ray and neutron diffraction is related to the size of the electron cloud/nucleus ratio. While the electron cloud has dimensions of about 1ºA, which is comparable with the X-ray wavelength, the radius of a nucleus is about 4 orders of magnitude smaller. As a result, the nucleus may be considered as a point scatterer and there will be no decrease with Θ of the neutron scattering factor. An additional property of the neutron is that it carries a spin and, consequently, once it interacts with the nuclei of the sample studied, it gives information about the magnetic properties. 33 Neutron data used in this thesis was collected on high resolution powder diffractometer BT-1 of NIST laboratory. 2.1.2 Magnetic susceptibility measurements using a SQUID magnetometer SQUIDs ("Superconducting Quantum Interferometer Device") are very sensitive sensors for magnetic fluxes, with the ability to measure very small magnetic fields. SQUIDs are used in several fields from electronics to biomagnetism. In addition to magnetic fluxes, other physical values can be measured if they can be adapted to the magnetic flux. Attainable sensitivities of flux densities (10− T), of electrical current (10− A) and of electrical resistance (10−12 Ω reflect the high accuracy of a SQUID. The working principle of a SQUID is based on the quantum interference of wave functions that describe the state of the superconducting charge carriers, the so-called Cooper pairs. Each Cooper pair can be treated as a single particle with a mass and charge twice that of a single electron, whose velocity is that of the center of mass of the pair. A SQUID is based on an interferometer loop in which two weak links (Josephson contacts) are established. A weak link is realized by interrupting a superconductor by a very thin insulating barrier. The function of the SQUID is to link the quantum mechanical phase difference of the Cooper pairs wave functions over a weak link with the magnetic flux penetrating the interferometer loop. 34 Figure 13: Scheme of a SQUID magnetometer. The components of a SQUID magnetometer (Figure 13) typically consist of the following: a detection coil, which senses changes in the external magnetic field and transforms them into an electrical current; an input coil which transforms the resulting current into a magnetic flux in the SQUID sensor; electronics which transform the applied flux into a room temperature voltage output; and acquisition hardware and software for acquiring, storing and analyzing data. Both the SQUID amplifier and the detection coils are superconducting devices. Thus some type of refrigerant (liquid helium or liquid nitrogen) or refrigeration device (cryocooler) is needed to maintain the SQUID and detection coil in the superconducting state. Additional signal conditioning electronics may be needed to improve signal-to-noise. The current work used a MPMS (Magnetic Property Measurement System based on SQUID) from Quantum Design having the following characteristics: Hmax=8T and ∆T=1.8 K-400 K. 35 2.1.3 Heat capacity measurements Heat capacities of different samples were measured on a Quantum Design PPMS (physical property measurement system) both with and without magnetic field using a specialized heat capacity puck. Magnetic fields of up to 9T were used. The heat capacity puck utilizes the standard PPMS 12-pin format for electrical connections, and it provides a small microcalorimeter platform for mounting the sample. Samples are mounted to this platform by a standard cryogenic grease or adhesive such as Apiezon N or H Grease. The sample platform is suspended by eight thin wires that serve as the electrical leads for an embedded heater and thermometer. The wires also provide a well-defined thermal connection between the sample platform and the puck. An additional thermometer embedded in the puck provides a highly accurate determination of the puck temperature, and a thermal shield aids in maintaining stable sample temperature and uniformity. To ensure that heat is not lost via exchange gas, the Heat Capacity option includes the PPMS High-Vacuum system, which maintains the sample chamber pressure near 0.01 mbar and is automatically controlled by the software. The heat capacity mounting station helps protect the sample platform and its suspending leads when mounting and removing a sample. A built-in vacuum line securely holds the platform in place so that samples may be mounted or removed without generating stress on the support36 ing wires. A single heat capacity measurement consists of several distinct stages. First, the sample platform and puck temperatures are stabilized at some initial temperature. Power is then applied to the sample platform heater for a predetermined length of time, causing the sample platform temperature to rise. When the power is terminated, the temperature of the sample platform relaxes toward the puck temperature. The sample platform temperature is monitored throughout both heating and cooling, providing (with the heater power data) the raw data of the heat capacity calculation. 37 Figure 14: Cutaway view showing the PPMS -16T magnet and probe. Inset shows a heat capacity puck. 2.1.4 Dielectric properties (capacitance measurements) Capacitance is a measure of the amount of electric charge (Q) stored (or separated) for a given electric potential (V). C = Q/V 38 In a capacitor, there are two conducting electrodes which are insulated from one to another. The charge on the electrodes is +Q and -Q, and V represents the potential difference between the electrodes. Capacitance is measured in the SI unit of the Farad, 1F=1C/V. The capacitance can be calculated if the geometry of the conductors and the dielectric properties of the insulator between the conductors are known. For example, the capacitance of a parallel plate capacitor constructed of two parallel plane electrodes of area A separated by a distance d is approximately equal to the following: C = (A/d) Where C is the capacitance in farads, is the permittivity of the insulator used, A is the area of each plane electrode, measured in m2 and d is the separation between the electrodes, measured in m. This equation is a good approximation if d is small compared to the other dimensions of the electrodes. This is this geometry that we have used to measure the capacitance and thus the dielectric constant of our different samples (see chapter 3 and 4). 2.2 Solvothermal synthesis All the metal organic frameworks described in this text were prepared by solvothermal route at temperatures ranging from 100 °C to 200 °C or at room temperature. In some cases a mixed approach was used: heating followed by room temperature crystallization. 39 Solvothermal synthesis is a batch method of synthesis where-in all reactants are placed in an autoclave and heated under autogenous (selfinduced) pressure at temperatures ranging from 100 °C to 200 °C. Steel autoclaves lined with a Teflon cup obtained from Parr Instrument Company (Figure 15) were used for solvothermal synthesis in the present work. All reagents were used as received. Figure 15: Cutaway of a general purpose (high temperature) 23 mL Parr acid digestion bomb, used in the solvothermal synthesis of all the compounds described in this dissertation. 40 There are many parameters which can be modified in a hydrothermal synthesis reaction in order to synthesize new or different phases. Often the first variable to modify is temperature. Broadly speaking, within the same metal/ligand family, low dimensional structures are formed at lower temperatures and more condensed phases are formed at higher temperatures, and the degree of hydration per metal center decreases with increasing reaction temperature. The effect of reaction time is also easily investigated. Kinetically accessible structures can be trapped if the reaction timescale is short (but long enough for a reaction to occur). Thermodynamically stable phases can be achieved if longer times are used. Metal:ligand ratios can be adjusted. The concentration of the reaction mixture is often used to control whether the sample is a powder or single crystals. The head space in the cup (directly related to the pressure) can also be varied. The pH of the reaction solution can be varied, generally in the acidic to weakly basic range, because if the solution is too basic then metal hydroxides are the majority phase formed. Templating molecules or structure directing agents (SDAs) also can be added. 41 CHAPTER 3 ORDER – DISORDER PHASE TRANSITION IN [(CH3)2NH2]Zn(HCOO)3 3.1 Background The discovery of Order – disorder phase transition in [(CH3)2NH2]Zn(HCOO)3 is described in this chapter. Materials that exhibit electrical ordering are of great interest because of their technological importance. The high permittivity123 dielectric constant, ε) properties of some of these electrically ordered materials have also made them important in development of dielectric resonators and filters for microwave communication systems. Many of these materials are oxides with the perovskite structure, such as lead zirconate titanate (PZT)124-128 and BaTiO367, 129-130 which have found applications in an entire set of technologies (actuators, sensors, transducers, memory elements, filtering devices, high performance insulators).126, 131-132 In the case of PZT, the remarkable electromechanical and electrical properties are associated with the morphotropic phase boundary, which is formed by doping antiferroelectric PbZrO3 with ferroelectric PbTiO3 and which occurs for the coexistence of tetragonal (P4mm symmetry FT), monoclinic (Cm symmetry FM), and rhombohedral (R3c symmetry FR) polar distortions of the perovskite structure.133 These properties are technically important, but concern about the environmental impact of Pb-based systems has 42 spurred considerable interest in the discovery of lead free ferro/antiferro-electric materials. Much of the recent attention in this field has been focused on developing devices based upon well-established inorganic compounds such as KH2PO4 (KDP), BaTiO3, PZT and LiNbO3;3 consequently reports of new electrically ordered systems have remained sparse. 3.2 Synthesis [(CH3)2NH2]Zn(HCOO)3, 1 (Figure 16), was synthesized in a reaction between zinc chloride and water in dimethylformamide (DMF). In a typical synthesis, 5 ml of DMF, 0.5 ml of water and 1 mmol of zinc chloride were heated overnight in a Teflon lined autoclave at 125oC. In-situ hydrolysis of DMF produces formic acid and dimethylammonium cation, which are the building blocks for 1. The autoclave was taken out after three days and was air−cooled on a metal rack. After, approximately hours the autoclave was opened and the reaction medium was transferred into two centrifuge tubes equally. After centrifugation supernatant was transferred into a clean glass beaker for room temperature crystallization. The beaker was covered with parafilm and few holes were created. It is important to make these holes in order for 1 to crystallize . After two to three days cubic crystals of 1 were recovered from the bottom of the glass beaker. 43 1 could also be synthesized in Teflon lines glass vials at 125 °C. Vials were taken out of the oven after approximately six hours, and supernatant was carefully transferred into another glass vial which was kept open. Overnight room temperature crystallization usually leads to the formation of flakes. Powder X-ray diffraction showed that these flakes are of compound 1. Keeping the vial closed leads to the formation of regular cubic morphology crystals of 1 after few months. 44 3.3 Structure Figure 16: Crystal structure of [(CH3)2NH2]Zn(HCOO)3 , 1. It has the same architecture as an ABX3 perovskite, with A=(CH3)2NH2+, B=Zn2+ and X=HCOO-. An analog of 1 was first prepared in 1973,134 but its relationship to the perovskite structure was not recognized until 2005.135 The structure of 1 at room temperature, as shown in Figure 16, was confirmed by single crystal X-ray diffraction. Important room temperature unit cell parameters for 1 are displayed in Table 3. 1 has the same architecture as that of ABX3 perovskite. Zinc (Zn2+) and formate (HCOO−) ions make a ReO3 45 type net. Dimethylammonium cation (CH3)2NH2+ lies at the center of this anionic net. Table 3: Structure parameters for 1 from single crystal X-ray diffraction at room temperature Formula sum C5 H11 N O6 Zn Formula weight 246.52 g/mol Crystal system trigonal Space-group R -3 c (167) Cell parameters a=8.1924(8) Å c=22.277(2) Å Cell ratio a/b=1.0000 b/c=0.3677 c/a=2.7192 Cell volume 1294.76(17) Å3 Z 6 Calc. density 1.89687 g/cm3 3.4 Structural phase transition We were struck by the observation that the dimethylammonium cation at the center of the ReO3-type cavity in 1 is disordered with nitrogen apparently existing in three different possible positions. This is a consequence of disordered hydrogen bonding between the hydrogen atoms of the NH2 group and oxygen atoms from the formate framework N….O ~ 46 2.9 Å). The knowledge that hydrogen bonding of this type can lead to ferroelectric (e.g. in KDP) or antiferroelectric (as in NH4H2PO4, ADP) transitions when ordering takes place on cooling led us to examine the dielectric and phase transition behavior in this system. The first evidence of a phase transition was noted when we saw splitting of spots while attempting to collect single crystal X-ray data at liquid nitrogen temperatures. Unfortunately, it was not possible to index the low temperature data set due to complex twinning. However, synchrotron X-ray powder data collected on beamline 11-BM at the Advanced Photon Source (ANL) gave clear indications of a phase transition. As shown in Figure 17, peaks at 100K were shifted to higher angles compared with the room temperature data as a consequence of lattice contraction on cooling. More importantly, at 100K the main peaks also had weak satellites due to the formation of a superlattice (features indicated by arrows, see inset in Figure 17). Although the features are weak, our conclusion is supported by the observation of analogous features on all the other peaks in PXRD data. This observation is consistent with ordering of the NH2 hydrogen atoms. It was not possible to solve the structure of low temperature phase because of complex twinning. Efforts were made to prepare deuterated sample to do neutron diffraction experiment as neutron would be much more sensitive to the ordering of deuterium. Because the deuterium of the DMA cation can easily exchange with hydrogen, this reaction was 47 carried out with the vial closed. Unfortunately, it was not possible to getpure compound from this reaction for a neutron experiment. Figure 17: Synchrotron powder patterns collected with a wavelength of 0.608Å at APS: red data obtained at room temperature, black data at 100K. 3.5 Dielectric and heat capacity measurements In order to determine if this phase transition is accompanied by a dielectric anomaly, as expected for a perovskite, the dielectric constant ε of 1 was measured as function of temperature. We used a pellet as sin48 gle crystals were too small to make silver paste contacts. ε showed a clear anomaly around 160K (Figure 18), in agreement with the synchrotron data. The maximum value of εr real part of ε was found to be ra- ther sample dependent, ranging from about 15 to 120, but the transition temperature was essentially reproducible. There was a clear hysteresis of about 10K, as is usual for pellet samples. The shape of the dielectric plot around 160 K suggests that 1 becomes antiferroelectric below 160K on cooling.136 The shape also resembles the antiferroelectric transition for ADP (at 148K).57 However a close look in the vicinity of phase transition suggests that the peak could also be a peak, characteristic of a ferroelectric phase transition (This point will be further discussed in chapter 4.). As seen in Figure 18, εr starts increasing as we approach room temperature, which is usual for pellet samples,120 but could also arise from ferroelectric domains. 49 Figure 18: Dielectric constant of 1 measured as a function of temperature. In order to probe the transition mechanism, specific heat of 1 over the temperature range 1.8 K – 300K was measured. A clear anomaly is seen around 156K, in both the increasing and decreasing temperature scans (Figure 19). The shape of the curve points to a second-order transition. It is worth reminding that while this shape points to a second order transition, the dielectric anomaly resembles a first order phase transition. The area under the Cp/T curve yielded a value of ΔS for the phase transition of 1.1 J/mol-K. For an order-disorder transition, ΔS = R ln(N), where N is the number of sites for the disordered system. However, for N= , the value of ΔS should be . J/mol-K, i.e. almost an order of magni- tude larger than the observed value. Clearly the transition is much more 50 complex than a simple 3-fold disorder model. This transition was further studied by 1H NMR and the results are presented in chapter 5. Figure 19: Heat capacity of 1 as function of temperature. 3.6 Summary and conclusions In conclusion, an order-disorder type ferroelectric phase transitions was discovered in [(CH3)2NH2]Zn(HCOO)3(1) at 156K. 1 also falls into the category of high-dielectric constant material with an εr value of ap- proximately 15. 1 was characterized by single crystal and powder X-ray 51 diffraction methods. Phase transitions were studied with synchrotron radiation, dielectric measurements, and heat capacity measurements. This type of ferroelectric ordering associated with order-disorder phase transition was unprecedented in hybrid frameworks and opened up an exciting new direction in rational synthetic strategies to create extended hybrid networks for applications in ferroic-related fields. 3.7 Resulting publication and comments Work resulted into a publication in the Journal of the American Chemical Society21. This chapter was adopted from the same publication. This work was also highlighted in Journal Nature’s news and views section19 and was also highlighted in Angew. Chem. Int. Ed.137 52 CHAPTER 4 MULTIFERROIC METAL ORGANIC FRAMEWORKS: [(CH3)2NH2]M(HCOO)3(M=Mn, Ni, Co, & Fe) 4.1 Background In this chapter we demonstrate that multiferroic behavior can be achieved in metal organic frameworks by using a combination of transition metal ions with hydrogen-bond ordering. Single-phase multiferroic materials in which magnetic and electrical ordering co-exist are very rare.58 This is because the two cooperative phenomena require very different molecular interactions that are difficult to incorporate in the same compound. In the case of ABX3 perovskites, for example, the conventional mechanism for ferroelectricity in classical systems such as BaTiO3 involves an off-centering of d0 cations on the B-site. This is incompatible with magnetic ordering which requires unpaired spins.58 The d0 requirement can be circumvented if the electrical ordering can be achieved in a different way. In the classical cases of BiMnO3 and BiFeO3, the electrical ordering is driven by off-centre displacements of the lone pair Bi3+ ions.58, 138-139 Similarly, in the case of nickel iodine boracite, Ni3B7O13I, the first ferromagnetic ferroelectric material to be discovered, the distorted iodine−oxygen octahedron provides the origin for the ferroelectricity.140 There are, of course, other ways in which ferroelectric ordering can be generated. In non-magnetic ferroelectrics such as NaCaF3, the driving force involves Coulomb interactions, rather than cova53 lency. On the other hand, in potassium hydrogen phosphate, KDP, hydrogen-bond ordering leads to ferroelectricity.141 In CHAPTER 3, we showed an order disorder structural phase transition at 160K in a cation-templated MOF with the ABX3 perovskite topology, [(CH3)2NH2]Zn(HCOO)3 (DMAZnF).21 In this chapter we show that this same class of materials can become multiferroic when the zinc is replaced by a transition metal ion. We also give crystallographic evidence of phase transitions mechanism and low temperature structure. 4.2 Synthesis Samples of [(CH3)2NH2]M(HCOO)3 (DMAMF = dimethylammonium metal formate), where M=Mn (Figure 22), Fe, Co, and Ni, were synthesized under solvothermal conditions at 140°C. Typically 5 mmol of metal chloride salts were dissolved in a 60 ml solution of 50 volume% DMF in water and transferred into a Teflon-lined autoclave. This was heated for 3 days at 140 0C. The autoclaves were air cooled and the supernatants were transferred into a glass beaker for room temperature crystallization. Within a further three days, cubic colorless crystals for Mn and Fe, red crystals for Co, and green crystals for Ni were obtained. DMAFeF has not previously been reported in the literature (Structure information is listed in Table 4, Table 5, Table 6, and Table 7). It was not possible to make phase pure sample of DMAFeF, but it was possible to separate big crystals manually under an optical microscope. The manganese analogue was easiest to make and also produced the biggest crystals. It was also easy to scale up the process to make gram quantities of the frame54 work. Hence, throughout this work DMAMnF has been considered as the representative of this family and full set of experiments were carried out on it 4.3 Crystal growth mechanism Shown in Figure 20 are the optical images of DMAMnF. The growth mechanism of these crystals is hypothesized to be layer by layer growth. In some cases, as seen in the top left optical image in Figure 20, if the crystals are growing on a flat surface, the bottom most surface would be flat. Figure 20: Optical images of [(CH3)2NH2]Mn(HCOO)3. 55 Further single crystals of DMAMnF were studied using atomic force microscopy (AFM) to understand the crystal growth mechanism. It was found to be layer by layer growth. Shown in Figure 21 is a cross-section of these layers in which steps of a few microns are clearly visible. Face indexing using the X-rays followed by the AFM results show that the growth is perpendicular to the <012> plane. Figure 21: AFM image of a multiferroic MOF dimethylammonium manganese formate. Crystals grow layer by layer during the room temperature crystallization. Growth is perpendicular to the <012> plane. 56 4.4 Structure In DMAMF, the DMA cation at the center of the ReO3-type cavity is disordered at room temperature with nitrogen distributed over three equivalent positions (Figure 22), as in the analogous zinc system (Figure 16). This is a consequence of disordered hydrogen bonding between the hydrogen atoms of the NH2 group and the oxygen atoms of the formate framework N…..O ~ . Ǻ . Figure 22: Building block of [(CH3)2NH2]Mn(HCOO)3, DMMnF. The DMA cation (A) is at the center of an ReO3 type cavity, formed by manganese (B) and formate (X) ions. Nitrogen is disordered over three positions. 57 4.4.1 Crystallographic data for DMAFeF Crystallographic data for a multiferroic MOF, DMAFeF, has been presented in the tables below. This as well as other datasets have been submitted to Cambridge strutural database and can be requested from there. Table 4: Structure parameters for DMAFeF Formula sum C2.5 H4.5 Fe0.5 N0.5 O3 Formula weight 117.49 g/mol Crystal system trigonal Space-group R -3 c (167) Cell parameters a=8.241(2) Å c=22.545(6) Å Cell ratio a/b=1.0000 b/c=0.3655 c/a=2.7357 Cell volume 1325.99(48) Å3 Z 12 Calc. density 1.76549 g/cm3 58 Table 5: Atomic parameters of DMAFeF Atom Wy Site S.O.F. ck. Fe 6b -3. O 36f 1 C1 18e .2 C2 12c 3. N 18e .2 0.33 H1 18e .2 H2 36f 1 x/a y/b z/c U [Å2] 0 -0.0084 0.1217 2/3 0.5804 0.231 0.788 1.00000 0.7830 0.7884 1/3 0.2471 0.898 0.358 0 0.0542 0.0833 0.0297 0.0833 0.0833 0.0120 0.059 0.29 Table 6: Anisotropic displacement parameters for DMAFeF, in Å2 Atom Fe O C1 C2 N U11 0.0195 0.0314 0.0249 0.066 0.032 U22 0.0195 0.0324 0.0249 0.066 0.032 U33 0.0299 0.0439 0.040 0.046 0.047 U12 0.0097 0.0168 0.012 0.0330 0.021 U13 0.0000 0.0062 0.0010 0.0000 -0.004 U23 0.0000 0.0049 0.0010 0.0000 0.004 Table 7: Selected geometric information for DMAFeF Atoms 1,2 Fe—Oi Fe—Oii Fe—Oiii Fe—Oiv Fe—O Fe—Ov O—C1 C1—Ovi d 1,2 [Å] 2.139(2) 2.139(2) 2.139(2) 2.139(2) 2.139(2) 2.139(2) 1.239(3) 1.239(3) Atoms 1,2 C1—H1 C2—Nvii C2—N C2—Nviii C2—H2 N—Nviii N—Nvii N—C2ix 59 d 1,2 [Å] 0.90(8) 1.403(7) 1.403(7) 1.403(7) 1.002(10) 1.23(2) 1.23(2) 1.403(7) Table 7 continued..... Atoms 1,2,3 Angle 1,2,3 Atoms 1,2,3 Angle 1,2,3 [°] [°] Oi—Fe—Oii 180.000 O—C1—Ovi 126.4(5) i iii O —Fe—O 90.53(10) O—C1—H1 116.8(2) ii iii vi O —Fe—O 89.47(10) O —C1—H1 116.8(2) i iv vii O —Fe—O 89.47(10) N —C2—N 52.1(8) Oii—Fe—Oiv 90.53(10) Nvii—C2—Nviii 52.1(8) iii iv viii O —Fe—O 89.47(10) N—C2—N 52.1(8) i vii O —Fe—O 90.53(10) N —C2—H2 84.(4) Oii—Fe—O 89.47(10) N—C2—H2 130.8(18) Oiii—Fe—O 90.53(10) Nviii—C2—H2 120.(8) iv viii vii O —Fe—O 180.00(11) N —N—N 60.000(2) Oi—Fe—Ov 89.47(10) Nviii—N—C2ix 64.0(4) ii v vii ix O —Fe—O 90.53(10) N —N—C2 64.0(4) iii v viii O —Fe—O 180.00(11) N —N—C2 64.0(4) Oiv—Fe—Ov 90.53(10) Nvii—N—C2 64.0(4) v ix O—Fe—O 89.47(10) C2 —N—C2 119.1(9) C1—O—Fe 127.4(3) Atoms 1,2,3,4 Tors. an. Atoms 1,2,3,4 Tors. an. 1,2,3,4 [°] 1,2,3,4 [°] O—Fe—O—C1 -28.6(2) Fe—O—C1—Ovi -176.5(2) viii O—Fe—O—C1 151.4(2) N—C2—N—N 67.6(3) O—Fe—O—C1 -119.08(15) N—C2—N—Nvii -67.6(3) O—Fe—O—C1 118.5(5) N—C2—N—C2ix 33.81(13) ix O—Fe—O—C1 60.92(15) N—C2—N—C2 -33.81(13) (i) 1-y, 2+x-y, z; (ii) -1+y, -x+y, -z; (iii) -1-x+y, 1-x, z; (iv) -x, 2-y, -z; (v) 1+x-y, 1+x, -z; (vi) 0, 0, 0; (vii) 1-y, x-y, z; (viii) 1-x+y, 1-x, z; (ix) 0, 0, 0. 60 4.5 Magnetic properties of DMAMF 4.5.1 Magnetic susceptibility Wang et. al. have shown that DMAMnF, DMACoF, and DMANiF are canted weak ferromagnets with Tc values of 8.5 K (Figure 23), 14.9 K, 35.6 K, respectively.142 They have also shown that for DMACoF and DMANiF, spin reorientation takes place at 13.1 K and 14.3 K, respectively. All of the samples show hysteresis loops below their critical temperatures. Using the model developed by Rushbrook and Wood for a Heisenberg antiferromagnet on a simple cubic lattice and/or the molecular field theory for antiferromagnetism, the magnetic coupling parameters J were estimated to be -0.23/-0.32 cm-1, -2.3 cm-1, and -4.85 cm-1 for Mn, Co, and Ni, analogues respectively. Their J values indicate that the dominant superexchange mechanism is antiferromagnetic. 61 Figure 23: Temperature dependence of χM of DMAMnF at H = 1000 Oe from 2 to 300 K. 142 Wang et al. also suggested that the spin canting in these compounds may originate from the noncentrosymmetric character of the threeatom formate bridge, CHOO-.142-143 In the present work, we have confirmed the findings of Wang et al. and also found that DMFeF is ferromagnetic below 20 K. It is important to note that it is possible to synthesize other weak ferromagnets simply by changing the central amine cation.144 62 Figure 24: Magnetic susceptibility of DMAFeF 4.6 Structural phase transition 4.6.1 Temperature dependent X-ray diffraction data Temperature dependent laboratory and synchrotron powder X-ray diffraction (PXRD) data for all samples gave clear indications of a phase change between room temperature and 100 K (Figure 25). The PXRD peaks for the DMAMFs at 100 K are shifted to higher angles compared with those at room temperature as a consequence of lattice contraction on cooling, and the main peaks in the PXRD pattern showed splitting as63 sociated with a lowering of symmetry. Attempts were made to solve the structure using synchrotron data but due to the complex twinning nature of the low temperature phase these attempts were unsuccessful. Figure 25: PXRD pattern for DMAMnF, collected at the Advanced Photon Source, ANL = . Ǻ, BM-11) 4.7 Low temperature structure Single crystal x-ray data were collected for DMAMnF at 110 K, well below the transition temperature, but because of twinning it was not possible to solve and refine the structure to a satisfactory standard. The low temperature data can be indexed in a monoclinic system and in principle in two possible space groups: C2/c (centrosymmetric) and Cc (non64 centrosymmetric). The monoclinic unit cell has been confirmed for all the samples by low temperature powder X-ray diffraction. When trying to refine the structure in the C2/c space group, a number of drawbacks were encountered: the agreement factors were worst than in the case of using the space group Cc; the results suggested disordered DMA cations with the nitrogen atom apparently in two different positions and with two very different N−C bond lengths . Å and . Å that make no chemical sense for such cation. Because of all these incongruities, the space group (C2/c) was ruled out. Meanwhile, the low temperature structure could be satisfactorily solved in the Cc space group with cell parameters of a=14.451(8) Å, b=8.376(3) Å, c=8.952(4) Å, β= . °. The most relevant structural information is summarized in Table 8 that also includes bond lengths and bond angles. In addition, we have to note that the crystal is twinned and that a racemic twin is observed at low temperature, with a Flack parameter of 0.43(7). 65 Figure 26: Rietveld refinement of PXRD data of DMANiF collected at 10 K with monoclinic unit cell of a=14.451(8) Å b=8.376(3) Å c=8.952(4) Å and β= . °. Pattern is in red color, simulated pattern is in blue and difference plot is in orange. Table 8: Structural parameters for the low temperature polar phase of DMAMnF Phase data Formula sum C5 H11 Mn N O6 Formula weight 236.09 g/mol Crystal system monoclinic Space-group C 1 c 1 (9) Cell parameters a=14.451(8) Å b=8.376(3) Å c=8.952(4) Å β= . Cell ratio a/b=1.7253 b/c=0.9357 c/a=0.6195 Cell volume 929.97(396) Å3 Z 4 Calc. density 1.68613 g/cm3 RAll 0.0649 66 ° Table 8 continued... Atom Wyck. Site x/a y/b Mn1 4a 1 0.69954 0.25162 O1 4a 1 0.75670 0.02930 O2 4a 1 0.75270 0.16110 O3 4a 1 0.54010 0.14140 O4 4a 1 0.65010 0.33650 O5 4a 1 0.36080 0.14010 O6 4a 1 0.65350 0.51940 C1 4a 1 0.44990 0.21050 H1 4a 1 0.45700 0.33900 C2 4a 1 0.72430 -0.02990 H2 4a 1 0.67400 -0.00200 C3 4a 1 0.66410 0.47790 H3 4a 1 0.69200 0.55500 N11 4a 1 0.89750 0.30860 H11A 4a 1 0.88750 0.41730 H11B 4a 1 0.84180 0.26590 C12 4a 1 0.89510 0.23970 H12A 4a 1 0.95670 0.28020 H12B 4a 1 0.82790 0.27120 H12C 4a 1 0.89890 0.12300 C11 4a 1 1.00270 0.27350 H11C 4a 1 1.00770 0.15890 H11D 4a 1 1.00660 0.33340 H11E 4a 1 1.06250 0.30540 z/c 0.78210 0.93350 0.60700 0.61640 0.96160 0.44830 1.14780 0.53100 0.52800 1.02810 1.05600 1.02220 0.97500 0.52080 0.50780 0.52970 0.36260 0.35670 0.25730 0.37130 0.68460 0.70970 0.78170 0.66910 U [Å2] 0.0210 0.0180 0.0200 0.0230 0.0230 0.0410 0.0410 0.0410 0.0350 0.0350 0.0350 Atom U11 U22 U33 U12 U13 U23 Mn1 0.0140 0.0121 0.0073 0.0004 0.0039 0.00053 O1 0.0211 0.0172 0.0049 0.0027 0.0057 0.00580 O2 0.0230 0.0210 0.0140 -0.0009 0.0130 0.00190 O3 0.0180 0.0200 0.0220 -0.0015 0.0090 0.00310 O4 0.0240 0.0150 0.0340 -0.0068 0.0160 -0.00900 O5 0.0130 0.0210 0.0210 -0.0010 0.0033 0.00590 O6 0.0320 0.0160 0.0450 -0.0059 0.0270 -0.01040 C1 0.0170 0.0182 0.0180 -0.0100 0.0080 0.00300 67 Table 8 continued... Atom U11 U22 U33 U12 U13 U23 C2 0.0211 0.0172 0.0049 0.0027 0.0057 0.0058 C3 0.0120 0.0190 0.0160 0.0040 0.0050 0.0033 N11 0.0160 0.0180 0.0240 -0.0006 0.0109 0.0028 C12 0.0330 0.0290 0.0220 -0.0030 0.0160 -0.0010 C11 0.0170 0.0200 0.0250 -0.0030 0.0050 0.0020 Selected geometric informations Atoms 1,2 d 1,2 [Å] Atoms 1,2 d 1,2 [Å] Mn1—O6i 2.178(5) O4—C3 1.275(8) Mn1—O4 2.186(6) O5—C1 1.255(10) iv Mn1—O1 2.200(5) O5—Mn1 2.216(5) Mn1—O3 2.203(5) O6—C3 1.259(9) Mn1—O2 2.203(5) O6—Mn1v 2.178(5) ii vi Mn1—O5 2.216(5) C2—O2 1.256(8) O1—C2 1.260(8) N11—C11 1.503(12) O2—C2iii 1.256(8) N11—C12 1.513(14) O3—C1 1.263(10) Atoms 1,2,3 Angle 1,2,3 [°] Atoms 1,2,3 Angle 1,2,3 [°] O6i—Mn1—O4 89.8(2) O3—Mn1—O5ii 179.3(2) i ii O6 —Mn1—O1 175.7(3) O2—Mn1—O5 89.30(19) O4—Mn1—O1 89.0(2) C2—O1—Mn1 126.6(4) O6i—Mn1—O3 94.6(2) C2iii—O2—Mn1 124.7(4) O4—Mn1—O3 90.4(2) C1—O3—Mn1 127.8(4) O1—Mn1—O3 89.56(18) C3—O4—Mn1 125.1(5) i iv O6 —Mn1—O2 91.7(2) C1—O5—Mn1 127.7(4) O4—Mn1—O2 178.3(2) C3—O6—Mn1v 126.4(5) O1—Mn1—O2 89.40(18) O5—C1—O3 124.7(4) vi O3—Mn1—O2 90.2(2) O2 —C2—O1 126.6(7) O6i—Mn1—O5ii 85.9(2) O6—C3—O4 124.8(7) ii O4—Mn1—O5 90.1(2) C11—N11—C12 111.3(7) ii O1—Mn1—O5 89.99(19) (i) x, 1-y, -0.5+z; (ii) 0.5+x, 0.5-y, 0.5+z; (iii) x, -y, -0.5+z; (iv) -0.5+x, 0.5-y, 0.5+z; (v) x, 1-y, 0.5+z; (vi) x, -y, 0.5+z. 68 Furthermore, Rietveld refinement of powder neutron data confirms the low temperature space group. Despite several attempts it was not possible to synthesize deuterated analogue of DMAMnF. High intensity data was collected at the NIST national laboratory. Despite the high background because of the hydrogenated sample, the fit to the low temperature Cc phase is remarkably good. 69 Figure 27: Reietveld refinement of powder neutron data collected at NIST with the low temperature Cc phase of DMAMnF. Black is the experimental data, Red is simulated pattern, Blue is the Bragg positions and Green is the difference between experimental and simulated. 4.8 Dielectric measurements As expected, this phase change is associated with a dielectric εr) ano- maly. Dielectric constant measurements were carried out on single crystals of DMAMnF, DMAFeF, and DMACoF as well as on a powder sample of the nickel phase. The dielectric constant of DMAMnF shows a clear anomaly close to 185 K on cooling (Figure 28). A clear hysteresis of about 10 K was seen when compared with the transition on heating. The 70 shape of the dielectric plot suggests that DMMnF is undergoing a paraelectric to antiferroelectric phase transition with εr values of around 25 and 9 respectively. This is a result of the structural phase transition due to the ordering of the nitrogen atoms. No other dielectric anomaly was observed while cooling the sample down to 1.8 K. The transition is of an Figure 28: Dielectric constant of DMAMnF as a function of temperature with no magnetic field and with that of 5 Tesla. The measurements were done at 1 kHz, using amplitude of 1V. order-disorder nature, rather than displacive, and the shape resembles the antiferroelectric transition for NH4H2PO4 (ADP).136 However the low temperature structure is a polar structure. Careful experiment does indeed show a −type peak as shown in Figure 29. Figure 29 also reveals a magneto-dielectric coupling in DMAMnF. Notice that rate of change sign 71 has changed from positive to negative for the dielectric constants of DMAMnF measured below the phase transition temperatures as a function of magnetic field. Similar hydrogen bond ordering is responsible for the ADP phase transition, which is at around 148 K. The dielectric constants for the paraelectric phases of DMFeF, DMCoF, and DMNiF were found to be approximately 45, 50, and 30, respectively; their transition temperatures on cooling were found to be 160 K, 165 K, and 180 K, respectively. As expected from their similar structures and the origin of the disorder, the shapes of the anomalies are essentially the same for the other three analogues. 72 Figure 29: Dielectric constant of DMAMnF measured as a function of temperature and magnetic field. Bottom two plots reveal a magneto-dielectic coupling. 73 4.9 Heat capacity measurements Dielectric constant findings were corroborated by specific heat measurements. The measurements were carried out on 20-30 single crystals by immersing them inside N-grease on a Quantum Design PPMS sample holder. Measurements were performed several times to ensure reproducibility and appropriate backgrounds were measured before each experiment. The specific heat of DMAMnF, which was measured as a function of temperature from 1.8 K to 300 K, shows clear anomalies at 183 K and 8.4 K corresponding to the transitions leading to electrical and magnetic ordering, respectively (Figure 30). Both the transition temperatures are in agreement with dielectric and magnetic susceptibility measurements. The area under the Cp/T curve around 183 K yielded a value for ΔS of 0.9 J/mol-K. For a complete order-disorder transition ΔS is expected to be given by Rln(N) where N is the number of sites in the disordered system. For N=3, ΔS would therefore be 9.1 J/mol-K, which is almost an order of magnitude larger than the observed value. This suggests that the transition is more complex than a simple 3-fold orderdisorder model. It appears, that as the sample is cooled through the transition, the compound becomes only partly ordered and the long range ordering takes place over a broad range of temperatures. 74 Figure 30: Heat capacity of DMAMnF as a function of temperature. The anomalies relating to electrical ordering and magnetic ordering are clearly visible. Detailed studies of the specific heat changes for DMAMF (M=Mn, Co, Ni) through the magnetic phase transition show that Tc decreases from 8.4 K to 6.7 K on increasing the magnetic field from 0 to 9 Tesla, (Figure 31). This is consistent for the predominantly antiferromagnetic behavior of these systems. Low temperature Q-Band EPR spectra for DMMnF (Figure 32) have shed further light on the magnetic phase transition. Measurements were made on single crystals of DMMnF to find if this magnetic transition was accompanied by a structural phase transition, since our PXRD facility did not enable us to reach these temperatures. As seen in Figure 32 the single EPR peak clearly splits into two, implying 75 two differently oriented domains below about 6 K. Thus the magnetic transition is accompanied by a structural change as well. Figure 31: Effect of magnetic field on the magnetic phase transition in DMAMnF on cooling. 76 Figure 32: Temperature dependence of Q-Band EPR spectra of DMAMnF. 4.10 Summary and conclusions In conclusion, we report four multiferroic metal organic frameworks, ((CH3)2NH2)M(HCOO)3, with M= Mn, Fe, Co, and Ni, which belong to the ABX3 type perovskite family with A = [(CH3)2NH2]+, B= M2+ and X= HCOO. The dimethylammonium cation is dynamically disordered in the rhombohedral paraelectric phase and the transition to the monoclinic ferroelectric phase involves hydrogen bond ordering of the DMA cations at temperatures in the range 160 K - 185 K. On further cooling, these materials become magnetically ordered (8 K-36 K), and below these temperatures the antiferroelectric order co-exists with weakly ferromagnetic order. Our findings illustrate a new approach to the creation of sys77 tems exhibiting multiferroic behavior whereby electrical order involves hydrogen bonding. These results suggest a highly promising new mechanism for this important behavior and opens up fresh opportunities for production of lead-free multiferroic structures tailored for specific technological applications. 4.11 Resulting publications and comments Work resulted into a publication in the Journal of the American Chemical Society.20 This chapter was adopted from the same publication. This work was highlighted in Journal Nature19, 145, and in Angew. Chem. Int. Ed.137 78 CHAPTER 5 GLASSY BEHAVIOR OF (CH3)2NH2Zn(HCOO)3 5.1 Background Glassy behavior related to orientational ordering is observed in fullerides and their rotor-stator complexes, as well as in many polymeric systems and plastic crystals.146-150 A knowledge of the orientational ordering is important because it influences the properties and phase diagrams of such systems. For example, the superconducting properties of A3C60 and Na2AC60 compounds are strongly influenced by the orientational state of the fulleride anions.151 In the case of C60, following a first order phase transition around 260 K, a more subtle phase transition is observed around 90 K.152 The later transition is attributed to the kinetics of molecular reorientation leading to glassy behavior. This glassy state is obtained when the thermal energy is not sufficient to overcome the potential energy barrier that separates the orientational configurations. Two energetically distinct orientations exist with the majority of the molecules being in the lower energy orientation below 90 K. Above 90 K, the population of the dominant orientation decreases with increasing temperature until, at the 260 K transition, there is a discontinuous change of the fractional occupancy from 0.63 to 0.5. In this chapter, we describe a comparable glassy behavior in a metal organic framework (MOF) with 79 the perovskite architecture, [(CH3)2NH2]Zn(HCOO)3 (DMAZnF). We also report a memory effect related to the temperature dependent relaxation in the same compound. 5.2 Debye law and remnant specific heat In previous chapters we reported a series of multifunctional metal organic frameworks exhibiting ferromagnetic and ferroelectric order, simultaneously.20-21 During the thermodynamic characterization, we observed an unusually large specific heat at lower temperatures for these materials. It is well known that at relatively low temperatures, in the range of 2 - 30 K, glasses also have a phonon heat capacity that is larger than the simple prediction of the Debye T3 law. This excess specific heat gives rise to a peak in C/T3 vs T and is generally ascribed to localized vibrations, domain wall motions of the glassy mosaic structure, or transverse phonon modes.153-155 These modes are usually seen in Raman scattering as low-frequency peaks. Because these low-frequency states are observed in glasses of all bonding types (metallic, ionic, covalent, etc.), they are thought to be a fundamental feature of glass dynamics.156 A number of crystalline materials also exhibit a low temperature peak in C/T3. This has been used to study the nature of vibrations and disorder in materials like quartz SiO2 and the pyrochlore Bi2Ti2O7.153 In the present case, plotting C/T3 for the DMAZnF also revealed a clearly defined broad peak at 25 K (Figure 33), well below its ferroelectric phase transition. This observation suggests that the ferroelectric ordering was not the only cooperative process below the 156 K transition temperature (Tc), and that there is also another kind of ordering process, such as 80 glass formation, taking place at a shorter length scale. This prompted us to study the kinetic behavior of the DMA cation in DMAZnF which is involved in the ferroelectric ordering in this compound. Figure 33: Temperature dependent of low-temperature specific heat (plotted as C/T3 versus T). 81 5.3 NMR measurements For recollection, DMAZnF has the same architecture as that of oxide perovskites. Metal atoms sit at the corners of a cube and are connected by formate ligands. The cavity of the cube is occupied by a dimethylammonium cation, the nitrogen of which is disordered over three distinct positions as a result of hydrogen bonding between the amine hydrogens and oxygens of the framework (Figure 34). Upon cooling, the compound goes under a phase transition, due to the ordering of nitrogen, leading to ferroelectric ordering. To study the kinetics we measured the NMR spin-lattice relaxation time (T1) of DMAZnF over a wide temperature range (4-250 K). The sample consisted of 20-30 sub-millimeter sized single crystals, synthesized as described in section.21, 142 The nuclear spin-lattice relaxation time, T1, of the CH3 protons was used as a probe of the local order and molecular dynamics time scale ≈ -10 s) of the (CH3)2NH2+ (DMA) unit. 82 Figure 34: Crystal structure of [(CH3)2NH2]Zn(HCOO)3 at room temperature. The purple spheres represent the three dynamically disordered sites for the N atom of the dimethylammonium formate moiety. The freezing of these positions is proposed to be the mechanism underlying the ferroelectric transition at 156 K. The CH3 proton resonance was chosen because it has a strong, sharp peak, due to the motional narrowing caused by the CH3 group rotation.157 The NH2 protons were undetectable, very likely because of broadening due to the 14N quadrupolar interaction. T1 was measured using a Tecmag Aries/Libra spectrometer with a home-built NMR probe at a field of . T . M(z for protons , using the standard π/ -τ-π/ saturation recovery procedure.158 Small temperature steps of 0.1 K were utilized around Tc (156 K). 83 5.4 Results and discussion Figure 35 summarizes the temperature dependence of the CH3 proton T1-1 (the spin-lattice relaxation rate). The graph has been divided into three regions (A, B and C) guided by natural breaks in the slope. In region C, DMAZnF is in the high-temperature, paraelectric (PE) phase. On lowering the temperature, T1-1 increases steadily to a maximum around Tc, whereafter it starts to decrease as DMAZnF enters the ferroelectrically ordered phase, regions A and B. In region A, T1-1 follows a different curve, implying a change in the spin-lattice relaxation pathway. This is because the motion is dominated by slowing of the methyl-group rotations below ~40 K. A similar observation has been reported by Clough et. al.157 in methyl malonic acid and related compounds. 84 Figure 35: Temperature dependence of the CH3 proton spin-lattice relaxation rate, T1-1, of DMAZnF. A, B and, C refer to the glass, ferroelectric (FE) and, paraelectric (PE) phases, respectively. Solid lines are the theoretical fits to the BPP equation. Arrows indicate the direction of the temperature scan. The inset shows the Arrhenius plot for this path. In the temperature range 65 K - 250 K, the spin-lattice relaxation time is completely reversible along the main path (Path I, Figure 35). This reversibility holds as long as the sample is not cooled below 40 K. When cooled below 40 K, T1 follows a different curve on warming. This important observation is discussed later. 85 Figure 36: Thermal cycles for paths II and III, wherein the spin-lattice relaxation rate jumps back to the main path (path I), are highlighted by arrows. The dashed lines are the projected paths had no jumps occurred. Solid (thick) lines are the theoretical fits to the BPP equation. Temperature dependence of T1 for the paraelectric phase (region C) and for path I in region B was analyzed using the Bloembergen-PurcellPound (BPP) formalism159, in which the relaxation rate is related to the correlation time τc. Correlation time is the characteristic time between significant fluctuations in the local magnetic field experienced by a spin due to molecular motions or reorientations of a molecule. Relaxation is caused by the molecular motion of the entity to which the proton is attached and so, we consider the homonuclear dipole-dipole interaction 86 between the protons in the methyl group in this case. The BPP equation159 for rigid rotor motion of a methyl group in a rigid solid is 2 1 9 0 T1 20 4r 3 2 c 4 c 1 2 2 1 4 2 2 c c where γ is the gyromagnetic ratio of 1H, r = 1.67 Å is the distance between CH3 hydrogens11, and ω is the 1H resonance frequency. It was assumed that the temperature dependence of τc follows an Arrhenius-like behavior with τc = τ0exp(Ea/RT), where τ0 is the single particle correlation time, Ea the activation energy for the dynamic process, and R the gas constant. τc was extracted by fitting the experimental T1 data to the BPP and Arrhenius equations in the C and B regions, treating Ea and τ0 as variables. T1 data within a few degrees of Tc were not included in the fitting procedure because of the cooperative phenomena that occur close to Tc. The resulting values of Ea and τ0 enabled us to calculate the correlation times for the protons in the CH3 group; these values are presented in the inset of Figure 35 as an Arrhenius plot of ln τc versus 1/T. It is clear that T1 follows Arrhenius-like behavior both above and below Tc. Table 9 summarizes the Arrhenius parameters obtained in the PE and FE phases over the reversible range, 65 - 250 K. As can be seen in Table 9, Ea remains essentially unchanged (8 ± 0.3 kJ/mol) for this path while τ0 increases by an order of magnitude as the material enters the ferroelectric phase. Consequently, τc shows an anomalous in87 crease below Tc, e.g. it increases from 3.0·10-10 s at 160 K to 1.7·10-9 s at 150 K. Such large anomalous slowing down of the motional fluctuations (hopping) of the DMA unit coincident with Tc implies that the FE transition results from a freezing of the DMA hopping motion between its three possible sites (shown in Fig. 2). In region B, T1 becomes multi-valued over the range 65 K - Tc, and the behavior depends on the cooling history. Figure 36 shows two sets of our T1 measurements (labeled paths II and III), made on raising the temperature after the sample was cooled down to about 4 K. In general, T1 shows sudden jumps at unpredictable temperatures depending on the thermal cycling range and cooling rate. The jumps from a given metastable path (such as II and III) occur at unpredictable temperatures, implying that the structures attained are very close in energy. This existence of several different local structures is also consistent with glassy behavior. 88 Table 9: Arrhenius parameters for the CH3 protons in DMAZnF in the PE and FE phases Phase τ0 (s) Ea (kJ/mol) PE 8.0 ± 0.1 (7.4 ± 0.5)·10-13 FE, Path I 7.9 ± 0.2 (2.8 ± 0.4)·10-12 FE, Path II (jump) 6±1 ~ 1·10-10 FE, Path III (jump) 9±1 ~ 4·10-12 FE, Path IV (no jump) 9.7 ± 0.3 (1.8 ± 0.4)·10-12 Paths for which the T1 curve remains smooth without any jumps, but different from the main path, occurred only when the sample was cooled rather quickly (>5 K/min). An Arrhenius analysis of one such a path, following the above BPP procedure, yielded Arrhenius parameters Ea=9.7±0.3 kJ/mol and τ0=(1.8±0.4)·10-12 89 s (Path IV in Table 9, not shown in Figure 36). For this case both τc and Ea increase significantly as compared to the slow cooling case (path I). Since T1 depends on the local geometry, these data show that the DMA moiety finds distinctly different local environments depending on the sample cooling history, a clear signature of a glassy phase. The relaxation rate, which decreases rapidly between 156 and 65 K, starts to decrease more slowly at about 40 K, implying that a new relaxation pathway begins to operate at this temperature and below. The T1-1 data can be decomposed into three component curves: one following that of pathway I, the second showing a maximum around 40 K, and a third essentially constant below about 10 K. The latter two pathways are analogous to the relaxation processes found in many methylcontaining solids. The second relaxation curve can be ascribed to thermally activated rotation and the third to a methyl group tunneling process. 5.5 Summary and conclusions In summary, we used the specific heat and 1H NMR T1 measurements to study the motional dynamics of the central amine moiety that is responsible for ferroelectric ordering of DMAZnF at 156 K. In particular, we were able to study the long-range and short-range ordering behavior using spin lattice relaxation rates. Both behaviors appear to be related to the motional dynamics of the DMA moiety. Below 156 K, the moiety starts becoming more ordered with decreasing temperature. Initially, 90 this involves ordering of the amine NH2 group. Further, below 40 K, rotations of the associated methyl groups start freezing, leading to multiple states with close underlying energies showing a glass-like effect. Local coordination environments in the framework remain unchanged as no other anomalies were observed in the specific heat. Warming up from 4 K, results in a memory effect, leading to different random paths in the temperature range of 65 -140 K due to the glass-like behavior of the framework below 40 K. To the best of our knowledge, this is the first report of a MOF showing glassy behavior and memory effect related to dynamics. These effects could potentially be used for manipulating other properties, such as gas absorption, catalysis, and electronic behavior, for which the MOFs are well known.15, 160 5.6 Resulting publications and comments This work has been adopted from a manuscript which will be submitted shortly. Work has been presented in American physical society and American chemical society meetings. 91 CHAPTER 6 SUMMARY AND CONCLUSIONS During the course of this dissertation, I worked on several projects related to the field of metal organic frameworks. I was able to synthesize a new family of nickel-1,4-cyclohexanedicarboxylate. This family was studied in detail and I found that, akin to zeolite synthesis, kinetic control could also be applied to the synthesis of metal organic frameworks. I also proposed a new method to make nanoparticles of MOFs by using nano-channels of anodized alumina template. This method was viable and 30-60 nm size nanorods of a nickel-1,4cyclohexanedicarboxylate framework.were synthesized I also spent considerable time of my PhD towards depositing a single monolayer of a two dimensional metal organic framework. This project was challenging as metal organic framework are usually synthesized at higher temperatures. However, I was able to make some beautiful nanostructures during my attempts to deposit a single monolayer of a MOF. During this PhD, I discovered approximately 15 new structures or phases of metal organic frameworks. These materials were thoroughly characterized and relevant properties were measured. Some of this work is still in progress and will likely result into further publications. For this dissertation, I have focused on frameworks with perovskite architecture. Perovskites are arguably the most important inorganic class 92 of materials with applications ranging from surfactants to superconductivity. I was able to synthesize six different metal organic frameworks with this famous topology, though four of them are previously know. I have deliberately left one of them out of this dissertation as it did not fall into the overall theme of multiferroic/multifunctional metal organic frameworks. Multiferroic materials are rare compounds featuring at least two ferroic properties with a majority of them displaying (anti)ferro – electricity or magnetism. Currently, the most famous compounds displaying such behavior are oxide perovskites. One of the most common mechanism for ferroelectric behavior requires an empty d-orbital which usually means that the material is diamagnetic. Hence there is a need for multiferroic materials in which two independent mechanisms can determinethe electric and magnetic ordering. I was able to achieve this using the hybrid perovskites. Hybrid perovskites of general formula (CH3)2NH2M(HCOO)3 have a ReO3 type cage made up of formate and metal ions. The metal ions sit at the corners of the cubes and they are connected to each other via coordination bonding with oxygen of the formate ion. The dimethylammonium cation is located at the center of this cavity. The amine hydrogen atoms make hydrogen bonds with the oxygen atoms of the metal formate framework. Because of this hydrogen bonding, the nitrogen of the ammonium cation is disordered over three equal positions at room tem93 perature. Cooling down these materials below 180 K, leads to a lowering in symmetry, a result of the ordering of nitrogen atoms. This phase transition is associated with a dielectric anomaly. Carefully done dielectric measurements show that the anomaly is a -type peak usually associated with paraelectric to ferroelectric phase transition. Low temperature single crystal measurements aided by powder X-ray diffraction and neutron diffraction experiments show that low temperature phase crystallizes in monoclinic symmetry and Cc space group. Cc belongs to one of the 10 polar point groups which are requirements for ferroelectricity. Furthermore, magnetic fields seem to affect this dielectric anomaly, suggesting that these hybrid perovskites have a magnetodielectric effect. This phase transition was studied in detail by electron paramagnetic resonance, heat capacity, and 1H NMR relaxation time measurements. Close to 0 K, specific heat data suggest that there is a remnant specific heat, a classic signature of amorphous or glassy materials. NMR data shows that these hybrid materials are indeed glassy below 40 K with many confirmations with close underlying energies. This effect is related to the rotation of methyl motors. NMR results also show an anomaly at the same temperature where dielectric anomaly is present. Methyl protons slow down by a factor to suggest that dielectic anomaly is indeed due to the ordering of nitrogen atoms. 94 APPENDIX CRYSTALLOGRAPHIC INFORMATION FILES Dimethylammonium iron formate: # Methyl Moiety X-C-H Angles are unusual because of the disorder data_Dimethylammoniumironformate _audit_creation_method SHELXL-97 _chemical_name_systematic _chemical_name_common Dimethylammoniumironformate _chemical_formula_moiety 'C9 H9 Fe3 O18, 3(C2 H6 N)' _chemical_formula_sum 'C15 H27 Fe3 N2.97 O18' _chemical_formula_weight 704.53 loop_ _atom_type_symbol _atom_type_description _atom_type_scat_dispersion_real _atom_type_scat_dispersion_imag _atom_type_scat_source 'C' 'C' 0.0033 0.0016 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'H' 'H' 0.0000 0.0000 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'N' 'N' 0.0061 0.0033 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'O' 'O' 0.0106 0.0060 95 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'Fe' 'Fe' 0.3463 0.8444 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' _symmetry_cell_setting Hexagonal _symmetry_space_group_name_H-M R-3c loop_ _symmetry_equiv_pos_as_xyz 'x, y, z' '-y, x-y, z' '-x+y, -x, z' 'y, x, -z+1/2' 'x-y, -y, -z+1/2' '-x, -x+y, -z+1/2' 'x+2/3, y+1/3, z+1/3' '-y+2/3, x-y+1/3, z+1/3' '-x+y+2/3, -x+1/3, z+1/3' 'y+2/3, x+1/3, -z+5/6' 'x-y+2/3, -y+1/3, -z+5/6' '-x+2/3, -x+y+1/3, -z+5/6' 'x+1/3, y+2/3, z+2/3' '-y+1/3, x-y+2/3, z+2/3' '-x+y+1/3, -x+2/3, z+2/3' 'y+1/3, x+2/3, -z+7/6' 'x-y+1/3, -y+2/3, -z+7/6' '-x+1/3, -x+y+2/3, -z+7/6' '-x, -y, -z' 96 'y, -x+y, -z' 'x-y, x, -z' '-y, -x, z-1/2' '-x+y, y, z-1/2' 'x, x-y, z-1/2' '-x+2/3, -y+1/3, -z+1/3' 'y+2/3, -x+y+1/3, -z+1/3' 'x-y+2/3, x+1/3, -z+1/3' '-y+2/3, -x+1/3, z-1/6' '-x+y+2/3, y+1/3, z-1/6' 'x+2/3, x-y+1/3, z-1/6' '-x+1/3, -y+2/3, -z+2/3' 'y+1/3, -x+y+2/3, -z+2/3' 'x-y+1/3, x+2/3, -z+2/3' '-y+1/3, -x+2/3, z+1/6' '-x+y+1/3, y+2/3, z+1/6' 'x+1/3, x-y+2/3, z+1/6' _cell_length_a 8.241(2) _cell_length_b 8.241 _cell_length_c 22.545(6) _cell_angle_alpha 90.00 _cell_angle_beta 90.00 _cell_angle_gamma _cell_volume _cell_formula_units_Z 120.00 1326.2(5) 2 _cell_measurement_temperature 273(2) 97 _cell_measurement_reflns_used ? _cell_measurement_theta_min ? _cell_measurement_theta_max ? _exptl_crystal_description _exptl_crystal_colour Cube colorless _exptl_crystal_size_max 0.2 _exptl_crystal_size_mid 0.1 _exptl_crystal_size_min 0.1 _exptl_crystal_density_meas ? _exptl_crystal_density_diffrn 1.765 _exptl_crystal_density_method _exptl_crystal_F_000 'not measured' 720 _exptl_absorpt_coefficient_mu 1.705 _exptl_absorpt_correction_type 'multi scan' _exptl_absorpt_correction_T_min ? _exptl_absorpt_correction_T_max ? _exptl_absorpt_process_details 'SADABS' _exptl_special_details _diffrn_ambient_temperature 273(2) _diffrn_radiation_wavelength 0.71073 _diffrn_radiation_type _diffrn_radiation_source MoK\a 'fine-focus sealed tube' _diffrn_radiation_monochromator graphite _diffrn_measurement_device_type 'CCD area Detector' _diffrn_measurement_method 'Omega scan' _diffrn_detector_area_resol_mean ? 98 _diffrn_standards_number ? _diffrn_standards_interval_count ? _diffrn_standards_interval_time ? _diffrn_standards_decay_% ? _diffrn_reflns_number 1107 _diffrn_reflns_av_R_equivalents 0.0560 _diffrn_reflns_av_sigmaI/netI 0.0493 _diffrn_reflns_limit_h_min -10 _diffrn_reflns_limit_h_max 10 _diffrn_reflns_limit_k_min -10 _diffrn_reflns_limit_k_max 7 _diffrn_reflns_limit_l_min -26 _diffrn_reflns_limit_l_max 22 _diffrn_reflns_theta_min 3.38 _diffrn_reflns_theta_max 26.71 _reflns_number_total _reflns_number_gt 301 228 _reflns_threshold_expression >2sigma(I) _computing_data_collection ? _computing_cell_refinement ? _computing_data_reduction ? _computing_structure_solution 'SHELXS-97 (Sheldrick, 1990)' _computing_structure_refinement 'SHELXL-97 (Sheldrick, 1997)' _computing_molecular_graphics ? _computing_publication_material ? _refine_special_details 99 ; Refinement of F^2^ against ALL reflections. The weighted R-factor wR and goodness of fit S are based on F^2^, conventional R-factors R are based on F, with F set to zero for negative F^2^. The threshold expression of F^2^ > 2sigma(F^2^) is used only for calculating R-factors(gt) etc. and is not relevant to the choice of reflections for refinement. Rfactors based on F^2^ are statistically about twice as large as those based on F, and R-factors based on ALL data will be even larger. ; _refine_ls_structure_factor_coef Fsqd _refine_ls_matrix_type full _refine_ls_weighting_scheme calc _refine_ls_weighting_details 'calc w=1/[\s^2^(Fo^2^)+(0.0503P)^2^+0.0000P] where P=(Fo^2^+2Fc^2^)/3' _atom_sites_solution_primary direct _atom_sites_solution_secondary difmap _atom_sites_solution_hydrogens geom _refine_ls_hydrogen_treatment _refine_ls_extinction_method mixed none _refine_ls_extinction_coef ? _refine_ls_number_reflns 301 _refine_ls_number_parameters _refine_ls_number_restraints 31 3 _refine_ls_R_factor_all 0.0561 _refine_ls_R_factor_gt 0.0403 100 _refine_ls_wR_factor_ref 0.0930 _refine_ls_wR_factor_gt 0.0883 _refine_ls_goodness_of_fit_ref 1.074 _refine_ls_restrained_S_all _refine_ls_shift/su_max _refine_ls_shift/su_mean 1.069 0.002 0.000 loop_ _atom_site_label _atom_site_type_symbol _atom_site_fract_x _atom_site_fract_y _atom_site_fract_z _atom_site_U_iso_or_equiv _atom_site_adp_type _atom_site_occupancy _atom_site_symmetry_multiplicity _atom_site_calc_flag _atom_site_refinement_flags _atom_site_disorder_assembly _atom_site_disorder_group Fe Fe 0.0000 1.0000 0.0000 0.0229(4) Uani 1 6 d S . . O O -0.0084(3) 0.7830(3) 0.05427(11) 0.0355(7) Uani 1 1 d . . . C1 C 0.1217(6) 0.7884(6) 0.0833 0.0298(12) Uani 1 2 d S . . C2 C 0.6667 0.3333 0.0297(3) 0.059(2) Uani 1 3 d SD . . N N 0.5804(14) 0.2471(14) 0.0833 0.035(3) Uani 0.33 2 d SPD . . H1 H 0.231(10) 0.898(10) 0.0833 0.059(19) Uiso 1 2 d S . . 101 H2 H 0.788(10) 0.358(19) 0.012(3) 0.29(6) Uiso 1 1 d D . . loop_ _atom_site_aniso_label _atom_site_aniso_U_11 _atom_site_aniso_U_22 _atom_site_aniso_U_33 _atom_site_aniso_U_23 _atom_site_aniso_U_13 _atom_site_aniso_U_12 Fe 0.0195(4) 0.0195(4) 0.0299(7) 0.000 0.000 0.0097(2) O 0.0314(14) 0.0324(15) 0.0439(15) 0.0049(12) -0.0062(12) 0.0168(12) C1 0.0249(19) 0.0249(19) 0.040(3) -0.0010(12) 0.0010(12) 0.012(2) C2 0.066(3) 0.066(3) 0.046(4) 0.000 0.000 0.0330(16) N 0.032(5) 0.032(5) 0.047(8) 0.004(3) -0.004(3) 0.021(5) _geom_special_details ; All esds (except the esd in the dihedral angle between two l.s. planes) are estimated using the full covariance matrix. The cell esds are taken into account individually in the estimation of esds in distances, angles and torsion angles; correlations between esds in cell parameters are only used when they are defined by crystal symmetry. An approximate (isotropic) treatment of cell esds is used for estimating esds involving l.s. planes. ; loop_ 102 _geom_bond_atom_site_label_1 _geom_bond_atom_site_label_2 _geom_bond_distance _geom_bond_site_symmetry_2 _geom_bond_publ_flag Fe O 2.139(2) 2_675 ? Fe O 2.139(2) 20_455 ? Fe O 2.139(2) 3_465 ? Fe O 2.139(2) 19_575 ? Fe O 2.139(2) . ? Fe O 2.139(2) 21_665 ? O C1 1.239(3) . ? C1 O 1.239(3) 16_454 ? C1 H1 0.90(8) . ? C2 N 1.403(7) 2_655 ? C2 N 1.403(7) . ? C2 N 1.403(7) 3_665 ? C2 H2 1.002(10) . ? N N 1.23(2) 3_665 ? N N 1.23(2) 2_655 ? N C2 1.403(7) 16_544 ? loop_ _geom_angle_atom_site_label_1 _geom_angle_atom_site_label_2 _geom_angle_atom_site_label_3 _geom_angle 103 _geom_angle_site_symmetry_1 _geom_angle_site_symmetry_3 _geom_angle_publ_flag O Fe O 180.0 2_675 20_455 ? O Fe O 90.53(10) 2_675 3_465 ? O Fe O 89.47(10) 20_455 3_465 ? O Fe O 89.47(10) 2_675 19_575 ? O Fe O 90.53(10) 20_455 19_575 ? O Fe O 89.47(10) 3_465 19_575 ? O Fe O 90.53(10) 2_675 . ? O Fe O 89.47(10) 20_455 . ? O Fe O 90.53(10) 3_465 . ? O Fe O 180.00(11) 19_575 . ? O Fe O 89.47(10) 2_675 21_665 ? O Fe O 90.53(10) 20_455 21_665 ? O Fe O 180.00(11) 3_465 21_665 ? O Fe O 90.53(10) 19_575 21_665 ? O Fe O 89.47(10) . 21_665 ? C1 O Fe 127.4(3) . . ? O C1 O 126.4(5) . 16_454 ? O C1 H1 116.8(2) . . ? O C1 H1 116.8(2) 16_454 . ? N C2 N 52.1(8) 2_655 . ? N C2 N 52.1(8) 2_655 3_665 ? N C2 N 52.1(8) . 3_665 ? N C2 H2 84(4) 2_655 . ? 104 N C2 H2 130.8(18) . . ? N C2 H2 120(8) 3_665 . ? N N N 60.000(2) 3_665 2_655 ? N N C2 64.0(4) 3_665 16_544 ? N N C2 64.0(4) 2_655 16_544 ? N N C2 64.0(4) 3_665 . ? N N C2 64.0(4) 2_655 . ? C2 N C2 119.1(9) 16_544 . ? loop_ _geom_torsion_atom_site_label_1 _geom_torsion_atom_site_label_2 _geom_torsion_atom_site_label_3 _geom_torsion_atom_site_label_4 _geom_torsion _geom_torsion_site_symmetry_1 _geom_torsion_site_symmetry_2 _geom_torsion_site_symmetry_3 _geom_torsion_site_symmetry_4 _geom_torsion_publ_flag O Fe O C1 -28.6(2) 2_675 . . . ? O Fe O C1 151.4(2) 20_455 . . . ? O Fe O C1 -119.08(15) 3_465 . . . ? O Fe O C1 118.5(5) 19_575 . . . ? O Fe O C1 60.92(15) 21_665 . . . ? Fe O C1 O -176.5(2) . . . 16_454 ? N C2 N N 67.6(3) 2_655 . . 3_665 ? 105 N C2 N N -67.6(3) 3_665 . . 2_655 ? N C2 N C2 33.81(13) 2_655 . . 16_544 ? N C2 N C2 -33.81(13) 3_665 . . 16_544 ? _diffrn_measured_fraction_theta_max 0.941 _diffrn_reflns_theta_full 26.71 _diffrn_measured_fraction_theta_full 0.941 _refine_diff_density_max 0.401 _refine_diff_density_min -0.487 _refine_diff_density_rms 0.092 Dimethylammonium zinc formate Crystal data and structure refinement for dimethylammonium zinc formate. Empirical formula C5 H11 N O6 Zn Formula weight 246.52 Temperature 273(2) K Wavelength 0.71073 A Crystal system, space group Hexagonal, R-3c Unit cell dimensions a = 8.1924(8) A alpha = 90 deg. b = 8.192 A beta = 90 deg. c = 22.277(2) A gamma = 120 deg. Volume 1294.81(18) A^3 Z, Calculated density 6, 1.897 Mg/m^3 106 Absorption coefficient 2.845 mm^-1 F(000) 756 Crystal size 0.25 x 0.1 x 0.05 mm Θ range for data collection 3.40 to 27.32 deg. Limiting indices 10<=h<=10, -8<=k<=10, -27<=l<=28 Reflections collected / unique 2979 / 318 [R(int) = 0.0230] Completeness to theta = 27.32 96.4 % Absorption correction Multi scan Refinement method Full-matrix least-squares on F^2 Data/restraints/parameters 318 / 2 / 31 Goodness-of-fit on F^2 1.145 Final R indices [I>2sigma(I)] R1 = 0.0236, wR2 = 0.0581 R indices (all data) R1 = 0.0277, wR2 = 0.0602 Largest diff. peak and hole 0.378 and -0.247 e.A^-3 107 Atomic coordinates ( x 10^4) and equivalent isotropic displacement parameters (A^2 x 10^3) for dimethylammonium zinc formate. U(eq) is defined as one third of the trace of the orthogonalized Uij tensor. ________________________________________________________________ x y z U(eq) ________________________________________________________________ Zn 0 O(1) -79(2) 2086(2) C(1) 1236(4) 3333 C(2) 6667 N 6667 0 0 3333 2462(11) 23(1) 538(1) 833 1376(2) 833 34(1) 30(1) 57(1) 43(2) ________________________________________________________________ 108 Bond lengths [Å] and angles [°] for dimethylammonium zinc formate _____________________________________________________________ Zn-O(1)#1 2.1149 Zn-O(1)#2 2.1149 Zn-O(1)#3 2.1149 Zn-O(1) 2.1149 Zn-O(1)#4 2.1149 Zn-O(1)#5 2.1149 O(1)-C(1) 1.2390 C(1)-O(1)#6 1.2390 C(1)-H(1) 0.8400 C(2)-N 1.4040 C(2)-N#7 1.4040 C(2)-N#8 1.4040 C(2)-H(2) 0.9980 N-N#7 1.2370 N-N#8 1.2370 N-C(2)#9 1.4040 O(1)#1-Zn-O(1)#2 91.02 O(1)#1-Zn-O(1)#3 180.00 O(1)#2-Zn-O(1)#3 88.98 O(1)#1-Zn-O(1) 88.98 O(1)#2-Zn-O(1) 180.00 109 O(1)#3-Zn-O(1) 91.02 O(1)#1-Zn-O(1)#4 88.98 O(1)#2-Zn-O(1)#4 88.98 O(1)#3-Zn-O(1)#4 91.02 O(1)-Zn-O(1)#4 91.02 O(1)#1-Zn-O(1)#5 91.02 O(1)#2-Zn-O(1)#5 91.02 O(1)#3-Zn-O(1)#5 88.98 O(1)-Zn-O(1)#5 88.98 O(1)#4-Zn-O(1)#5 180.00 C(1)-O(1)-Zn 127.02 O(1)#6-C(1)-O(1) 125.7 O(1)#6-C(1)-H(1) 117.17 O(1)-C(1)-H(1) 117.17 N-C(2)-N#7 52.3 N-C(2)-N#8 52.3 N#7-C(2)-N#8 52.3 N-C(2)-H(2) 87.9 N#7-C(2)-H(2) 117 N#8-C(2)-H(2) 138 N#7-N-N#8 60.0 N#7-N-C(2) 63.9 N#8-N-C(2) 63.9 N#7-N-C(2)#9 63.9 N#8-N-C(2)#9 63.9 C(2)-N-C(2)#9 118.9 110 _____________________________________________________________ Symmetry transformations used to generate equivalent atoms: #1 x-y,x,-z #2 -x,-y,-z #3 -x+y,-x,z #4 -y,x-y,z #5 y,-x+y,-z #6 x-y+1/3,-y+2/3,-z+1/6 #7 -y+1,x-y,z #8 -x+y+1,-x+1,z #9 y+1/3,x-1/3,-z+1/6 Anisotropic displacement parameters (A^2 x 10^3) for dimethylammonium zinc formate The anisotropic displacement factor exponent takes the form: -2 pi^2 [ h^2 a*^2 U11 + ... + 2 h k a* b* U12 ] _____________________________________________________________________ U11 U22 U33 U23 U13 U12 ____________________________________________________________________ Zn 23 23 23 0 0 12 O(1) 32 33 37 -11 -5 16 C(1) 28 27 34 1 1 14 C(2) 68 68 35 0 0 34 N 38 31 62 3 6 19 _____________________________________________________________________ Hydrogen coordinates ( x 10^4) and isotropic displacement parameters (A^2 x 10^3) for dimethylammonium zinc formate 111 ________________________________________________________________ x y z U(eq) ________________________________________________________________ H(2) 7100(200) H(1) 2260(40) 2550(160) 3333 1577(13) 833 350(50) 12(7) ________________________________________________________________ Torsion angles [°] for dimethylammonium zinc formate ________________________________________________________________ O(1)#1-Zn-O(1)-C(1) -152.22(15) O(1)#2-Zn-O(1)-C(1) -148(58) O(1)#3-Zn-O(1)-C(1) 27.78(15) O(1)#4-Zn-O(1)-C(1) 118.81(9) O(1)#5-Zn-O(1)-C(1) -61.19(9) Zn-O(1)-C(1)-O(1)#6 177.27(14) N#8-C(2)-N-N#7 67.68(19) N#7-C(2)-N-N#8 -67.68(19) N#7-C(2)-N-C(2)#9 -33.84(9) N#8-C(2)-N-C(2)#9 33.84(9) ________________________________________________________________ Symmetry transformations used to generate equivalent atoms: #1 x-y,x,-z #2 -x,-y,-z #3 -x+y,-x,z 112 #4 -y,x-y,z #5 y,-x+y,-z #6 x-y+1/3,-y+2/3,-z+1/6 #7 -y+1,x-y,z #8 -x+y+1,-x+1,z #9 y+1/3,x-1/3,-z+1/6 Dimethylammonium manganese formate _audit_creation_method SHELXL-97 _chemical_formula_sum 'C3 H9 Mn N O2' _chemical_formula_weight 146.05 loop_ _atom_type_symbol _atom_type_description _atom_type_scat_dispersion_real _atom_type_scat_dispersion_imag _atom_type_scat_source 'C' 'C' 0.0033 0.0016 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'H' 'H' 0.0000 0.0000 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'N' 'N' 0.0061 0.0033 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'O' 'O' 0.0106 0.0060 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'Mn' 'Mn' 0.3368 0.7283 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' _symmetry_cell_setting ? _symmetry_space_group_name_H-M "R -3 c" 113 loop_ _symmetry_equiv_pos_as_xyz 'x, y, z' '-y, x-y, z' '-x+y, -x, z' 'y, x, -z+1/2' 'x-y, -y, -z+1/2' '-x, -x+y, -z+1/2' 'x+2/3, y+1/3, z+1/3' '-y+2/3, x-y+1/3, z+1/3' '-x+y+2/3, -x+1/3, z+1/3' 'y+2/3, x+1/3, -z+5/6' 'x-y+2/3, -y+1/3, -z+5/6' '-x+2/3, -x+y+1/3, -z+5/6' 'x+1/3, y+2/3, z+2/3' '-y+1/3, x-y+2/3, z+2/3' '-x+y+1/3, -x+2/3, z+2/3' 'y+1/3, x+2/3, -z+7/6' 'x-y+1/3, -y+2/3, -z+7/6' '-x+1/3, -x+y+2/3, -z+7/6' '-x, -y, -z' 'y, -x+y, -z' 'x-y, x, -z' '-y, -x, z-1/2' '-x+y, y, z-1/2' 'x, x-y, z-1/2' 114 '-x+2/3, -y+1/3, -z+1/3' 'y+2/3, -x+y+1/3, -z+1/3' 'x-y+2/3, x+1/3, -z+1/3' '-y+2/3, -x+1/3, z-1/6' '-x+y+2/3, y+1/3, z-1/6' 'x+2/3, x-y+1/3, z-1/6' '-x+1/3, -y+2/3, -z+2/3' 'y+1/3, -x+y+2/3, -z+2/3' 'x-y+1/3, x+2/3, -z+2/3' '-y+1/3, -x+2/3, z+1/6' '-x+y+1/3, y+2/3, z+1/6' 'x+1/3, x-y+2/3, z+1/6' _cell_length_a 8.3279(8) _cell_length_b 8.3279(8) _cell_length_c 22.881(5) _cell_angle_alpha 90.00 _cell_angle_beta 90.00 _cell_angle_gamma 120.00 _cell_volume 1374.3(3) _cell_formula_units_Z 9 _cell_measurement_temperature 273(2) _exptl_crystal_description Cubic _exptl_crystal_colour light pink _exptl_crystal_density_diffrn 1.588 _exptl_crystal_density_method 'not measured' _exptl_crystal_F_000 675 115 _exptl_absorpt_coefficient_mu 2.059 _diffrn_ambient_temperature 273(2) _diffrn_radiation_wavelength 0.71073 _diffrn_radiation_type MoK\a _diffrn_radiation_source 'fine-focus sealed tube' _diffrn_radiation_monochromator graphite _diffrn_reflns_number 2288 _diffrn_reflns_av_R_equivalents 0.0294 _diffrn_reflns_av_sigmaI/netI 0.0178 _diffrn_reflns_limit_h_min -10 _diffrn_reflns_limit_h_max 8 _diffrn_reflns_limit_k_min -10 _diffrn_reflns_limit_k_max 10 _diffrn_reflns_limit_l_min -27 _diffrn_reflns_limit_l_max 28 _diffrn_reflns_theta_min 3.34 _diffrn_reflns_theta_max 26.41 _reflns_number_total 321 _reflns_number_gt 277 _reflns_threshold_expression >2sigma(I) _computing_structure_solution 'SHELXS-97 (Sheldrick, 1990)' _computing_structure_refinement 'SHELXL-97 (Sheldrick, 1997)' ; Refinement of F^2^ against ALL reflections. The weighted R-factor wR and goodness of fit S are based on F^2^, conventional R-factors R are 116 based on F, with F set to zero for negative F^2^. The threshold expression of F^2^ > 2sigma(F^2^) is used only for calculating R-factors(gt) etc. and is not relevant to the choice of reflections for refinement. R-factors based on F^2^ are statistically about twice as large as those based on F, and R- factors based on ALL data will be even larger. ; refine_ls_structure_factor_coef Fsqd _refine_ls_matrix_type full _refine_ls_weighting_scheme calc _refine_ls_weighting_details 'calc w=1/[\s^2^(Fo^2^)+(0.0716P)^2^+21.3666P] where P=(Fo^2^+2Fc^2^)/3' _atom_sites_solution_primary direct _atom_sites_solution_secondary difmap _atom_sites_solution_hydrogens geom _refine_ls_hydrogen_treatment mixed _refine_ls_extinction_method SHELXL _refine_ls_extinction_coef 0.0028(11) _refine_ls_extinction_expression 'Fc^*^=kFc[1+0.001xFc^2^\l^3^/sin(2\q)]^-1/4^' _refine_ls_number_reflns 321 _refine_ls_number_parameters 32 _refine_ls_number_restraints 3 _refine_ls_R_factor_all 0.0405 117 _refine_ls_R_factor_gt 0.0334 _refine_ls_wR_factor_ref 0.0865 _refine_ls_wR_factor_gt 0.0781 _refine_ls_goodness_of_fit_ref 0.609 _refine_ls_restrained_S_all 0.608 _refine_ls_shift/su_max 0.000 _refine_ls_shift/su_mean 0.000 loop_ _atom_site_label _atom_site_type_symbol _atom_site_fract_x _atom_site_fract_y _atom_site_fract_z _atom_site_U_iso_or_equiv _atom_site_adp_type _atom_site_occupancy _atom_site_symmetry_multiplicity _atom_site_calc_flag _atom_site_refinement_flags _atom_site_disorder_assembly _atom_site_disorder_group Mn Mn 0.0000 1.0000 0.0000 0.0263(4) Uani 1 6 d S . . O1 O -0.0103(3) 0.7792(3) 0.05449(8) 0.0417(6) Uani 1 1 d . . . C1 C 0.1174(5) 0.7840(5) 0.0833 0.0346(9) Uani 1 2 d S . . 118 C2 C 0.6667 0.3333 0.1362(3) 0.0626(17) Uani 1 3 d SD . . H1 H 0.223(5) 0.889(5) 0.0833 0.015(8) Uiso 1 2 d S . . H2 H 0.68(3) 0.445(12) 0.1571(7) 0.33(6) Uiso 1 1 d D . . N N 0.6667 0.4211(12) 0.0833 0.044(2) Uani 0.33 2 d SPD . . loop_ _atom_site_aniso_label _atom_site_aniso_U_11 _atom_site_aniso_U_22 _atom_site_aniso_U_33 _atom_site_aniso_U_23 _atom_site_aniso_U_13 _atom_site_aniso_U_12 Mn 0.0258(4) 0.0258(4) 0.0272(6) 0.000 0.000 0.0129(2) O1 0.0396(11) 0.0392(12) 0.0463(11) 0.0086(8) -0.0076(9) 0.0197(9) C1 0.0316(15) 0.0316(15) 0.040(2) 0.0008(8) -0.0008(8) 0.0157(17) C2 0.072(3) 0.072(3) 0.043(3) 0.000 0.000 0.0361(14) N 0.034(5) 0.031(4) 0.067(7) 0.003(2) 0.006(5) 0.017(3) _geom_special_details ; All esds (except the esd in the dihedral angle between two l.s. planes) are estimated using the full covariance matrix. The cell esds are taken into account individually in the estimation of esds in distances, angles and torsion angles; correlations between esds in cell parameters are only used when they are defined by crystal symmetry. An approximate 119 (isotropic) treatment of cell esds is used for estimating esds involving l.s. planes. ; loop_ _geom_bond_atom_site_label_1 _geom_bond_atom_site_label_2 _geom_bond_distance _geom_bond_site_symmetry_2 _geom_bond_publ_flag Mn O1 2.1878(18) 20_455 ? Mn O1 2.1878(18) 2_675 ? Mn O1 2.1878(18) . ? Mn O1 2.1878(18) 21_665 ? Mn O1 2.1878(18) 3_465 ? Mn O1 2.1878(18) 19_575 ? O1 C1 1.234(3) . ? C1 O1 1.234(3) 16_454 ? C1 H1 0.88(4) . ? C2 N 1.412(6) 3_665 ? C2 N 1.412(6) 2_655 ? C2 N 1.412(6) . ? C2 H2 0.998(10) . ? N N 1.265(17) 2_655 ? N N 1.265(17) 3_665 ? N C2 1.412(6) 16_544 ? loop_ 120 _geom_angle_atom_site_label_1 _geom_angle_atom_site_label_2 _geom_angle_atom_site_label_3 _geom_angle _geom_angle_site_symmetry_1 _geom_angle_site_symmetry_3 _geom_angle_publ_flag O1 Mn O1 180.00(8) 20_455 2_675 ? O1 Mn O1 89.26(8) 20_455 . ? O1 Mn O1 90.74(8) 2_675 . ? O1 Mn O1 90.74(8) 20_455 21_665 ? O1 Mn O1 89.26(8) 2_675 21_665 ? O1 Mn O1 89.26(8) . 21_665 ? O1 Mn O1 89.26(8) 20_455 3_465 ? O1 Mn O1 90.74(8) 2_675 3_465 ? O1 Mn O1 90.74(8) . 3_465 ? O1 Mn O1 180.0 21_665 3_465 ? O1 Mn O1 90.74(8) 20_455 19_575 ? O1 Mn O1 89.26(8) 2_675 19_575 ? O1 Mn O1 180.00(10) . 19_575 ? O1 Mn O1 90.74(8) 21_665 19_575 ? O1 Mn O1 89.26(8) 3_465 19_575 ? C1 O1 Mn 127.3(2) . . ? O1 C1 O1 126.9(4) 16_454 . ? O1 C1 H1 116.54(19) 16_454 . ? O1 C1 H1 116.54(19) . . ? 121 N C2 N 53.2(6) 3_665 2_655 ? N C2 N 53.2(6) 3_665 . ? N C2 N 53.2(6) 2_655 . ? N C2 H2 126(8) 3_665 . ? N C2 H2 133(6) 2_655 . ? N C2 H2 87.8(9) . . ? N N N 60.0 2_655 3_665 ? N N C2 63.4(3) 2_655 . ? N N C2 63.4(3) 3_665 . ? N N C2 63.4(3) 2_655 16_544 ? N N C2 63.4(3) 3_665 16_544 ? C2 N C2 117.7(8) . 16_544 ? loop_ _geom_torsion_atom_site_label_1 _geom_torsion_atom_site_label_2 _geom_torsion_atom_site_label_3 _geom_torsion_atom_site_label_4 _geom_torsion _geom_torsion_site_symmetry_1 _geom_torsion_site_symmetry_2 _geom_torsion_site_symmetry_3 _geom_torsion_site_symmetry_4 _geom_torsion_publ_flag O1 Mn O1 C1 152.20(19) 20_455 . . . ? O1 Mn O1 C1 -27.80(19) 2_675 . . . ? O1 Mn O1 C1 61.46(12) 21_665 . . . ? 122 O1 Mn O1 C1 -118.54(12) 3_465 . . . ? O1 Mn O1 C1 131(100) 19_575 . . . ? Mn O1 C1 O1 -176.96(19) . . . 16_454 ? N C2 N N 68.0(2) 3_665 . . 2_655 ? N C2 N N -68.0(2) 2_655 . . 3_665 ? N C2 N C2 34.00(11) 3_665 . . 16_544 ? N C2 N C2 -34.00(11) 2_655 . . 16_544 ? _diffrn_measured_fraction_theta_max 1.000 _diffrn_reflns_theta_full 26.41 _diffrn_measured_fraction_theta_full 1.000 _refine_diff_density_max 0.397 _refine_diff_density_min -0.230 _refine_diff_density_rms 0.067 Dimethylammonium nickel formate _audit_creation_method SHELXL-97 _chemical_formula_sum 'C5 H11 N Ni O6' _chemical_formula_weight 239.86 loop_ _atom_type_symbol _atom_type_description _atom_type_scat_dispersion_real _atom_type_scat_dispersion_imag _atom_type_scat_source 'C' 'C' 0.0033 0.0016 123 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'H' 'H' 0.0000 0.0000 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'N' 'N' 0.0061 0.0033 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'O' 'O' 0.0106 0.0060 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'Ni' 'Ni' 0.3393 1.1124 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' _symmetry_cell_setting Hexagonal _symmetry_space_group_name_H-M 'R -3 c' loop_ _symmetry_equiv_pos_as_xyz 'x, y, z' '-y, x-y, z' '-x+y, -x, z' 'y, x, -z+1/2' 'x-y, -y, -z+1/2' '-x, -x+y, -z+1/2' 'x+2/3, y+1/3, z+1/3' '-y+2/3, x-y+1/3, z+1/3' '-x+y+2/3, -x+1/3, z+1/3' 'y+2/3, x+1/3, -z+5/6' 'x-y+2/3, -y+1/3, -z+5/6' '-x+2/3, -x+y+1/3, -z+5/6' 'x+1/3, y+2/3, z+2/3' 124 '-y+1/3, x-y+2/3, z+2/3' '-x+y+1/3, -x+2/3, z+2/3' 'y+1/3, x+2/3, -z+7/6' 'x-y+1/3, -y+2/3, -z+7/6' '-x+1/3, -x+y+2/3, -z+7/6' '-x, -y, -z' 'y, -x+y, -z' 'x-y, x, -z' '-y, -x, z-1/2' '-x+y, y, z-1/2' 'x, x-y, z-1/2' '-x+2/3, -y+1/3, -z+1/3' 'y+2/3, -x+y+1/3, -z+1/3' 'x-y+2/3, x+1/3, -z+1/3' '-y+2/3, -x+1/3, z-1/6' '-x+y+2/3, y+1/3, z-1/6' 'x+2/3, x-y+1/3, z-1/6' '-x+1/3, -y+2/3, -z+2/3' 'y+1/3, -x+y+2/3, -z+2/3' 'x-y+1/3, x+2/3, -z+2/3' '-y+1/3, -x+2/3, z+1/6' '-x+y+1/3, y+2/3, z+1/6' 'x+1/3, x-y+2/3, z+1/6' _cell_length_a _cell_length_b 8.1101(14) 8.110 125 _cell_length_c 21.986(4) _cell_angle_alpha 90.00 _cell_angle_beta 90.00 _cell_angle_gamma 120.00 _cell_volume 1252.4(3) _cell_formula_units_Z 6 _cell_measurement_temperature 273(2) _exptl_crystal_description cube _exptl_crystal_colour green _exptl_crystal_size_max 0.1 _exptl_crystal_size_mid 0.1 _exptl_crystal_size_min 0.08 _exptl_crystal_density_diffrn 1.908 _exptl_crystal_density_method 'not measured' _exptl_crystal_F_000 744 _exptl_absorpt_coefficient_mu 2.323 _exptl_absorpt_correction_type 'emperical' _exptl_absorpt_correction_T_min 0.329 _exptl_absorpt_correction_T_max 0.432 _exptl_absorpt_process_details 'Psi scan' _exptl_special_details _diffrn_ambient_temperature 273(2) _diffrn_radiation_wavelength 0.71073 _diffrn_radiation_type MoK\a _diffrn_radiation_source 'fine-focus sealed tube' _diffrn_radiation_monochromator graphite 126 _diffrn_measurement_device_type 'CCD area detector' _diffrn_measurement_method 'Omega scan' _diffrn_reflns_number 1930 _diffrn_reflns_av_R_equivalents 0.0491 _diffrn_reflns_av_sigmaI/netI 0.0361 _diffrn_reflns_limit_h_min -9 _diffrn_reflns_limit_h_max 9 _diffrn_reflns_limit_k_min -7 _diffrn_reflns_limit_k_max 10 _diffrn_reflns_limit_l_min -27 _diffrn_reflns_limit_l_max 21 _diffrn_reflns_theta_min 3.44 _diffrn_reflns_theta_max 26.51 _reflns_number_total 291 _reflns_number_gt 227 _reflns_threshold_expression >2sigma(I) _computing_structure_solution 'SHELXS-97 (Sheldrick, 1990)' _computing_structure_refinement 'SHELXL-97 (Sheldrick, 1997)' ; Refinement of F^2^ against ALL reflections. The weighted R-factor wR and goodness of fit S are based on F^2^, conventional R-factors R are based on F, with F set to zero for negative F^2^. The threshold expression of F^2^ > 2sigma(F^2^) is used only for calculating R-factors(gt) etc. and is not relevant to the choice of reflections for refinement. R127 factors based on F^2^ are statistically about twice as large as those based on F, and R-factors based on ALL data will be even larger. ; _refine_ls_structure_factor_coef Fsqd _refine_ls_matrix_type full _refine_ls_weighting_scheme calc _refine_ls_weighting_details 'calc w=1/[\s^2^(Fo^2^)+(0.0680P)^2^+0.0000P] where P=(Fo^2^+2Fc^2^)/3' _atom_sites_solution_primary direct _atom_sites_solution_secondary difmap _atom_sites_solution_hydrogens geom _refine_ls_hydrogen_treatment mixed _refine_ls_extinction_method none _refine_ls_number_reflns 291 _refine_ls_number_parameters 29 _refine_ls_number_restraints 2 _refine_ls_R_factor_all 0.0532 _refine_ls_R_factor_gt 0.0405 _refine_ls_wR_factor_ref 0.1056 _refine_ls_wR_factor_gt 0.0994 _refine_ls_goodness_of_fit_ref 1.081 _refine_ls_restrained_S_all 1.078 _refine_ls_shift/su_max 0.000 _refine_ls_shift/su_mean 0.000 loop_ 128 _atom_site_label _atom_site_type_symbol _atom_site_fract_x _atom_site_fract_y _atom_site_fract_z _atom_site_U_iso_or_equiv _atom_site_adp_type _atom_site_occupancy _atom_site_symmetry_multiplicity _atom_site_calc_flag _atom_site_refinement_flags _atom_site_disorder_assembly _atom_site_disorder_group Ni Ni 1.0000 1.0000 0.0000 0.0228(4) Uani 1 6 d S . . O O 0.7925(4) 0.7865(4) 0.05342(12) 0.0324(7) Uani 1 1 d . . . C1 C 0.6667 0.7939(7) 0.0833 0.0298(13) Uani 1 2 d S . . C2 C 0.6667 0.3333 0.0288(4) 0.052(2) Uani 1 3 d SD . . N N 0.7536(17) 0.4203(17) 0.0833 0.041(4) Uani 0.33 2 d SPD . . H1 H 0.6667 0.896(10) 0.0833 0.050 Uiso 1 2 d S . . H2 H 0.614(6) 0.201(3) 0.0132(13) 0.050 Uiso 1 1 d D . . loop_ _atom_site_aniso_label _atom_site_aniso_U_11 _atom_site_aniso_U_22 _atom_site_aniso_U_33 129 _atom_site_aniso_U_23 _atom_site_aniso_U_13 _atom_site_aniso_U_12 Ni 0.0227(5) 0.0227(5) 0.0231(6) 0.000 0.000 0.0113(2) O 0.0322(16) 0.0323(16) 0.0340(14) 0.0051(12) 0.0083(12) 0.0170(12) C1 0.023(3) 0.034(2) 0.029(3) -0.0007(11) -0.001(2) 0.0116(14) C2 0.059(3) 0.059(3) 0.037(4) 0.000 0.000 0.0293(16) N 0.036(6) 0.036(6) 0.045(8) 0.003(3) -0.003(3) 0.014(6) _geom_special_details ; All esds (except the esd in the dihedral angle between two l.s. planes) are estimated using the full covariance matrix. The cell esds are taken into account individually in the estimation of esds in distances, angles and torsion angles; correlations between esds in cell parameters are only used when they are defined by crystal symmetry. An approximate (isotropic) treatment of cell esds is used for estimating esds involving l.s. planes. ; loop_ _geom_bond_atom_site_label_1 _geom_bond_atom_site_label_2 _geom_bond_distance _geom_bond_site_symmetry_2 130 _geom_bond_publ_flag Ni O 2.073(2) 20_565 ? Ni O 2.073(2) 2_765 ? Ni O 2.073(2) 21_655 ? Ni O 2.073(2) 3_675 ? Ni O 2.073(2) 19_775 ? Ni O 2.073(2) . ? O C1 1.241(4) . ? C1 O 1.241(4) 18_654 ? C1 H1 0.83(8) . ? C2 N 1.392(10) 3_665 ? C2 N 1.392(10) . ? C2 N 1.392(10) 2_655 ? C2 H2 0.998(10) . ? N N 1.22(2) 2_655 ? N N 1.22(2) 3_665 ? N C2 1.392(10) 16_544 ? loop_ _geom_angle_atom_site_label_1 _geom_angle_atom_site_label_2 _geom_angle_atom_site_label_3 _geom_angle _geom_angle_site_symmetry_1 _geom_angle_site_symmetry_3 _geom_angle_publ_flag 131 O Ni O 180.00(12) 20_565 2_765 ? O Ni O 91.05(10) 20_565 21_655 ? O Ni O 88.95(10) 2_765 21_655 ? O Ni O 88.95(10) 20_565 3_675 ? O Ni O 91.05(10) 2_765 3_675 ? O Ni O 180.00(12) 21_655 3_675 ? O Ni O 91.05(10) 20_565 19_775 ? O Ni O 88.95(10) 2_765 19_775 ? O Ni O 91.05(10) 21_655 19_775 ? O Ni O 88.95(10) 3_675 19_775 ? O Ni O 88.95(10) 20_565 . ? O Ni O 91.05(10) 2_765 . ? O Ni O 88.95(10) 21_655 . ? O Ni O 91.05(10) 3_675 . ? O Ni O 180.0 19_775 . ? C1 O Ni 127.1(3) . . ? O C1 O 125.2(5) 18_654 . ? O C1 H1 117.4(3) 18_654 . ? O C1 H1 117.4(3) . . ? N C2 N 52.1(9) 3_665 . ? N C2 N 52.1(9) 3_665 2_655 ? N C2 N 52.1(9) . 2_655 ? N C2 H2 82(2) 3_665 . ? N C2 H2 132.6(17) . . ? N C2 H2 111(2) 2_655 . ? N N N 60.000(1) 2_655 3_665 ? 132 N N C2 64.0(4) 2_655 16_544 ? N N C2 64.0(4) 3_665 16_544 ? N N C2 64.0(4) 2_655 . ? N N C2 64.0(4) 3_665 . ? C2 N C2 119.1(10) 16_544 . ? loop_ _geom_torsion_atom_site_label_1 _geom_torsion_atom_site_label_2 _geom_torsion_atom_site_label_3 _geom_torsion_atom_site_label_4 _geom_torsion _geom_torsion_site_symmetry_1 _geom_torsion_site_symmetry_2 _geom_torsion_site_symmetry_3 _geom_torsion_site_symmetry_4 _geom_torsion_publ_flag O Ni O C1 -61.10(15) 20_565 . . . ? O Ni O C1 118.90(15) 2_765 . . . ? O Ni O C1 -152.2(3) 21_655 . . . ? O Ni O C1 27.8(3) 3_675 . . . ? O Ni O C1 -131(58) 19_775 . . . ? Ni O C1 O 177.5(2) . . . 18_654 ? N C2 N N -67.6(3) 3_665 . . 2_655 ? N C2 N N 67.6(3) 2_655 . . 3_665 ? N C2 N C2 -33.81(14) 3_665 . . 16_544 ? 133 N C2 N C2 33.81(14) 2_655 . . 16_544 ? _diffrn_measured_fraction_theta_max 0.990 _diffrn_reflns_theta_full 26.51 _diffrn_measured_fraction_theta_full 0.990 _refine_diff_density_max 0.899 _refine_diff_density_min -0.541 _refine_diff_density_rms 0.123 Low temperature dimethylammonium manganese formate _audit_creation_method SHELXL-97 _chemical_formula_sum 'C5 H11 Mn N O6' _chemical_formula_weight 236.09 loop_ _atom_type_symbol _atom_type_description _atom_type_scat_dispersion_real _atom_type_scat_dispersion_imag _atom_type_scat_source 'C' 'C' 0.0033 0.0016 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'H' 'H' 0.0000 0.0000 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'N' 'N' 0.0061 0.0033 134 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'O' 'O' 0.0106 0.0060 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' 'Mn' 'Mn' 0.3368 0.7283 'International Tables Vol C Tables 4.2.6.8 and 6.1.1.4' _symmetry_cell_setting 'monoclinic' _symmetry_space_group_name_H-M 'Cc' loop_ _symmetry_equiv_pos_as_xyz 'x, y, z' 'x, -y, z+1/2' 'x+1/2, y+1/2, z' 'x+1/2, -y+1/2, z+1/2' _cell_length_a 14.451(8) _cell_length_b 8.376(3) _cell_length_c 8.952(4) _cell_angle_alpha 90.00 _cell_angle_beta 120.879(7) _cell_angle_gamma 90.00 _cell_volume 930.0(7) _cell_formula_units_Z 4 _cell_measurement_temperature 103(2) _exptl_crystal_size_max 0.18 _exptl_crystal_size_mid 0.14 _exptl_crystal_size_min 0.08 135 _exptl_crystal_density_diffrn 1.686 _exptl_crystal_density_method 'not measured' _exptl_crystal_F_000 484 _exptl_absorpt_coefficient_mu 1.419 _exptl_absorpt_correction_T_min 0.7843 _exptl_absorpt_correction_T_max 0.8974 _diffrn_ambient_temperature 103(2) _diffrn_radiation_wavelength 0.71073 _diffrn_radiation_type MoK\a _diffrn_radiation_source 'fine-focus sealed tube' _diffrn_radiation_monochromator graphite _diffrn_reflns_number 3697 _diffrn_reflns_av_R_equivalents 0.0506 _diffrn_reflns_av_sigmaI/netI 0.0671 _diffrn_reflns_limit_h_min -18 _diffrn_reflns_limit_h_max 18 _diffrn_reflns_limit_k_min -11 _diffrn_reflns_limit_k_max 11 _diffrn_reflns_limit_l_min -11 _diffrn_reflns_limit_l_max 11 _diffrn_reflns_theta_min 2.93 _diffrn_reflns_theta_max 28.76 _reflns_number_total 2035 _reflns_number_gt 1841 _reflns_threshold_expression >2sigma(I) _computing_structure_solution 'SHELXS-97(Sheldrick, 2008)' 136 _computing_structure_refinement 'SHELXL-97(Sheldrick, 2008)' ; Refinement of F^2^ against ALL reflections. The weighted R-factor wR and goodness of fit S are based on F^2^, conventional R-factors R are based on F, with F set to zero for negative F^2^. The threshold expression of F^2^ > 2sigma(F^2^) is used only for calculating R-factors(gt) etc. and is not relevant to the choice of reflections for refinement. Rfactors based on F^2^ are statistically about twice as large as those based on F, and R-factors based on ALL data will be even larger. ; _refine_ls_structure_factor_coef Fsqd _refine_ls_matrix_type full _refine_ls_weighting_scheme calc _refine_ls_weighting_details 'calc w=1/[\s^2^(Fo^2^)+(0.1010P)^2^+3.5096P] where P=(Fo^2^+2Fc^2^)/3' _atom_sites_solution_primary direct _atom_sites_solution_secondary difmap _atom_sites_solution_hydrogens geom _refine_ls_hydrogen_treatment mixed _refine_ls_extinction_method SHELXL _refine_ls_extinction_coef 0.002(2) _refine_ls_extinction_expression 'Fc^*^=kFc[1+0.001xFc^2^\l^3^/sin(2\q)]^-1/4^' 137 _refine_ls_abs_structure_details 'Flack H D (1983), Acta Cryst. A39, 876-881' _refine_ls_abs_structure_Flack 0.43(7) _refine_ls_number_reflns 2035 _refine_ls_number_parameters 125 _refine_ls_number_restraints 2 _refine_ls_R_factor_all 0.0649 _refine_ls_R_factor_gt 0.0614 _refine_ls_wR_factor_ref 0.1723 _refine_ls_wR_factor_gt 0.1693 _refine_ls_goodness_of_fit_ref 1.086 _refine_ls_restrained_S_all 1.086 _refine_ls_shift/su_max 0.001 _refine_ls_shift/su_mean 0.000 loop_ _atom_site_label _atom_site_type_symbol _atom_site_fract_x _atom_site_fract_y _atom_site_fract_z _atom_site_U_iso_or_equiv _atom_site_adp_type _atom_site_occupancy _atom_site_symmetry_multiplicity _atom_site_calc_flag _atom_site_refinement_flags 138 _atom_site_disorder_assembly _atom_site_disorder_group Mn1 Mn 0.69954(17) 0.25162(10) 0.7821(3) 0.0119(3) Uani 1 1 d . . . O1 O 0.7567(4) 0.0293(5) 0.9335(5) 0.0148(7) Uani 1 1 d . . . O2 O 0.7527(3) 0.1611(5) 0.6070(5) 0.0178(10) Uani 1 1 d . . . O3 O 0.5401(4) 0.1414(6) 0.6164(7) 0.0207(10) Uani 1 1 d . . . O4 O 0.6501(4) 0.3365(5) 0.9616(7) 0.0238(12) Uani 1 1 d . . . O5 O 0.3608(4) 0.1401(5) 0.4483(7) 0.0209(11) Uani 1 1 d . . . O6 O 0.6535(4) 0.5194(6) 1.1478(8) 0.0278(12) Uani 1 1 d . . . C1 C 0.4499(7) 0.2105(6) 0.5310(13) 0.0178(9) Uani 1 1 d . . . H1 H 0.457(9) 0.339(7) 0.528(16) 0.021 Uiso 1 1 d . . . C2 C 0.7243(6) -0.0299(7) 1.0281(8) 0.0148(7) Uani 1 1 d . . . H2 H 0.674(7) -0.002(9) 1.056(11) 0.018 Uiso 1 1 d . . . C3 C 0.6641(5) 0.4779(8) 1.0222(8) 0.0168(12) Uani 1 1 d . . . H3 H 0.692(6) 0.555(10) 0.975(10) 0.020 Uiso 1 1 d . . . N11 N 0.8975(4) 0.3086(6) 0.5208(7) 0.0191(9) Uani 1 1 d . . . H11A H 0.8875 0.4173 0.5078 0.023 Uiso 1 1 calc R . . H11B H 0.8418 0.2659 0.5297 0.023 Uiso 1 1 calc R . . C12 C 0.8951(11) 0.2397(8) 0.3626(18) 0.027(3) Uani 1 1 d . . . H12A H 0.9567 0.2802 0.3567 0.041 Uiso 1 1 calc R . . H12B H 0.8279 0.2712 0.2573 0.041 Uiso 1 1 calc R . . H12C H 0.8989 0.1230 0.3713 0.041 Uiso 1 1 calc R . . C11 C 1.0027(8) 0.2735(11) 0.6846(15) 0.023(2) Uani 1 1 d . . . H11C H 1.0077 0.1589 0.7097 0.035 Uiso 1 1 calc R . . H11D H 1.0066 0.3334 0.7817 0.035 Uiso 1 1 calc R . . H11E H 1.0625 0.3054 0.6691 0.035 Uiso 1 1 calc R . . 139 loop_ _atom_site_aniso_label _atom_site_aniso_U_11 _atom_site_aniso_U_22 _atom_site_aniso_U_33 _atom_site_aniso_U_23 _atom_site_aniso_U_13 _atom_site_aniso_U_12 Mn1 0.0140(4) 0.0121(4) 0.0073(4) 0.00053(19) 0.0039(3) 0.0004(2) O1 0.0211(17) 0.0172(17) 0.0049(13) 0.0058(11) 0.0057(12) 0.0027(13) O2 0.023(2) 0.021(2) 0.014(2) -0.0019(17) 0.013(2) -0.0009(18) O3 0.018(2) 0.020(2) 0.022(3) 0.0031(18) 0.009(2) -0.0015(17) O4 0.024(2) 0.015(2) 0.034(3) -0.009(2) 0.016(2) -0.0068(19) O5 0.013(2) 0.021(3) 0.021(2) 0.0059(18) 0.0033(19) -0.0010(16) O6 0.032(3) 0.016(2) 0.045(3) -0.0104(19) 0.027(2) -0.0059(19) C1 0.017(2) 0.0182(19) 0.018(2) 0.003(5) 0.0080(17) -0.010(5) C2 0.0211(17) 0.0172(17) 0.0049(13) 0.0058(11) 0.0057(12) 0.0027(13) C3 0.012(3) 0.019(3) 0.016(3) 0.0033(19) 0.005(2) 0.0040(19) N11 0.016(2) 0.018(2) 0.024(2) 0.0028(19) 0.0109(19) -0.0006(17) C12 0.033(5) 0.029(4) 0.022(5) -0.001(3) 0.016(4) -0.003(3) C11 0.017(4) 0.020(3) 0.025(5) 0.002(3) 0.005(3) -0.003(3) _geom_special_details 140 ; All esds (except the esd in the dihedral angle between two l.s. planes) are estimated using the full covariance matrix. The cell esds are taken into account individually in the estimation of esds in distances, angles and torsion angles; correlations between esds in cell parameters are only used when they are defined by crystal symmetry. An approximate (isotropic) treatment of cell esds is used for estimating esds involving l.s. planes. ; loop_ _geom_bond_atom_site_label_1 _geom_bond_atom_site_label_2 _geom_bond_distance _geom_bond_site_symmetry_2 _geom_bond_publ_flag Mn1 O6 2.178(5) 2_564 ? Mn1 O4 2.186(6) . ? Mn1 O1 2.200(5) . ? Mn1 O3 2.203(5) . ? Mn1 O2 2.203(5) . ? Mn1 O5 2.216(5) 4 ? O1 C2 1.260(8) . ? O2 C2 1.256(8) 2_554 ? O3 C1 1.263(10) . ? O4 C3 1.275(8) . ? 141 O5 C1 1.255(10) . ? O5 Mn1 2.216(5) 4_454 ? O6 C3 1.259(9) . ? O6 Mn1 2.178(5) 2_565 ? C2 O2 1.256(8) 2 ? N11 C11 1.503(12) . ? N11 C12 1.513(14) . ? loop_ _geom_angle_atom_site_label_1 _geom_angle_atom_site_label_2 _geom_angle_atom_site_label_3 _geom_angle _geom_angle_site_symmetry_1 _geom_angle_site_symmetry_3 _geom_angle_publ_flag O6 Mn1 O4 89.8(2) 2_564 . ? O6 Mn1 O1 175.7(3) 2_564 . ? O4 Mn1 O1 89.0(2) . . ? O6 Mn1 O3 94.6(2) 2_564 . ? O4 Mn1 O3 90.4(2) . . ? O1 Mn1 O3 89.56(18) . . ? O6 Mn1 O2 91.7(2) 2_564 . ? O4 Mn1 O2 178.3(2) . . ? O1 Mn1 O2 89.40(18) . . ? O3 Mn1 O2 90.2(2) . . ? 142 O6 Mn1 O5 85.9(2) 2_564 4 ? O4 Mn1 O5 90.1(2) . 4 ? O1 Mn1 O5 89.99(19) . 4 ? O3 Mn1 O5 179.3(2) . 4 ? O2 Mn1 O5 89.30(19) . 4 ? C2 O1 Mn1 126.6(4) . . ? C2 O2 Mn1 124.7(4) 2_554 . ? C1 O3 Mn1 127.8(4) . . ? C3 O4 Mn1 125.1(5) . . ? C1 O5 Mn1 127.7(4) . 4_454 ? C3 O6 Mn1 126.4(5) . 2_565 ? O5 C1 O3 124.7(4) . . ? O2 C2 O1 126.6(7) 2 . ? O6 C3 O4 124.8(7) . . ? C11 N11 C12 111.3(7) . . ? _diffrn_measured_fraction_theta_max 0.885 _diffrn_reflns_theta_full 28.76 _diffrn_measured_fraction_theta_full 0.885 _refine_diff_density_max 1.673 _refine_diff_density_min -0.761 _refine_diff_density_rms 0.164 143 LIST OF REFERENCES 1. Rosi NL, Eckert J, Eddaoudi M, Vodak DT, Kim J, O'Keeffe M, Yaghi OM. Hydrogen storage in microporous metal-organic frameworks. Science 2003;300(5622):1127-29. 2. Li HL, Laine A, O'Keeffe M, Yaghi OM. Supertetrahedral sulfide crystals with giant cavities and channels. Science 1999;283(5405):1145-47. 3. El-Kaderi HM, Hunt JR, Mendoza-Cortes JL, Cote AP, Taylor RE, O'Keeffe M, Yaghi OM. Designed synthesis of 3D covalent organic frameworks. Science 2007;316(5822):268-72. 4. Eddaoudi M, Kim J, Rosi N, Vodak D, Wachter J, O'Keeffe M, Yaghi OM. Systematic design of pore size and functionality in isoreticular MOFs and their application in methane storage. Science 2002;295(5554):469-72. 5. Cote AP, Benin AI, Ockwig NW, O'Keeffe M, Matzger AJ, Yaghi OM. Porous, crystalline, covalent organic frameworks. Science 2005;310(5751):1166-70. 6. Chen BL, Eddaoudi M, Hyde ST, O'Keeffe M, Yaghi OM. Interwoven metal-organic framework on a periodic minimal surface with extra-large pores. Science 2001;291(5506):1021-23. 7. Park KS, Ni Z, Cote AP, Choi JY, Huang RD, Uribe-Romo FJ, Chae HK, O'Keeffe M, Yaghi OM. Exceptional chemical and thermal stability of zeolitic imidazolate frameworks. Proceedings of the National Academy of Sciences of the United States of America 2006;103(27):10186-91. 8. Hayashi H, Cote AP, Furukawa H, O'Keeffe M, Yaghi OM. Zeolite a imidazolate frameworks. Nature Materials 2007;6(7):501-06. 9. Li H, Eddaoudi M, O'Keeffe M, Yaghi OM. Design and synthesis of an exceptionally stable and highly porous metal-organic framework. Nature 1999;402(6759):276-79. 144 10. Chae HK, Siberio-Perez DY, Kim J, Go Y, Eddaoudi M, Matzger AJ, O'Keeffe M, Yaghi OM. A route to high surface area, porosity and inclusion of large molecules in crystals. Nature 2004;427(6974):523-27. 11. Rowsell JLC, Spencer EC, Eckert J, Howard JAK, Yaghi OM. Gas adsorption sites in a large-pore metal-organic framework. Science 2005;309(5739):1350-54. 12. Sudik AC, Cote AP, Wong-Foy AG, O'Keeffe M, Yaghi OM. A metalorganic framework with a hierarchical system of pores and tetrahedral building blocks. Angewandte Chemie-International Edition 2006;45(16):2528-33. 13. Chen BL, Ockwig NW, Millward AR, Contreras DS, Yaghi OM. High H-2 adsorption in a microporous metal-organic framework with open metal sites. Angewandte Chemie-International Edition 2005;44(30):4745-49. 14. Ferey G, Mellot-Draznieks C, Serre C, Millange F. Crystallized frameworks with giant pores: Are there limits to the possible? Accounts of Chemical Research 2005;38(4):217-25. 15. Rao CNR, Cheetham AK, Thirumurugan A. Hybrid inorganicorganic materials: a new family in condensed matter physics. Journal of Physics-Condensed Matter 2008;20(8):21. 16. Cheetham AK, Rao CNR. There's room in the middle. Science 2007;318(5847):58-59. 17. Eerenstein W, Mathur ND, Scott JF. Multiferroic magnetoelectric materials. Nature 2006;442(7104):759-65. and 18. Fiebig M. Revival of the magnetoelectric effect. Journal of Physics D: Applied Physics 2005;38(8):R123. 19. Ramesh R. Emerging 2009;461(7268):1218-19. routes to multiferroics. Nature 20. Jain P, Ramachandran V, Clark RJ, Zhou HD, Toby BH, Dalal NS, Kroto HW, Cheetham AK. Multiferroic Behavior Associated with an Order-Disorder Hydrogen Bonding Transition in Metal-Organic 145 Frameworks (MOFs) with the Perovskite ABX3 Architecture. Journal of the American Chemical Society 2009;131(38):13625-27. 21. Jain P, Dalal NS, Toby BH, Kroto HW, Cheetham AK. Orderdisorder antiferroelectric phase transition in a hybrid inorganic-organic framework with the perovskite architecture. Journal of the American Chemical Society 2008;130(32):10450-+. 22. Banerjee R, Phan A, Wang B, Knobler C, Furukawa H, O'Keeffe M, Yaghi OM. High-throughput synthesis of zeolitic imidazolate frameworks and application to CO2 capture. Science 2008;319(5865):939-43. 23. Eddaoudi M, Kim J, Vodak D, Sudik A, Wachter J, O'Keeffe M, Yaghi OM. Geometric requirements and examples of important structures in the assembly of square building blocks. Proceedings of the National Academy of Sciences of the United States of America 2002;99(8):490004. 24. Britt D, Tranchemontagne D, Yaghi OM. Metal-organic frameworks with high capacity and selectivity for harmful gases. Proceedings of the National Academy of Sciences of the United States of America 2008;105(33):11623-27. 25. Yang SH, Lin X, Blake AJ, Walker GS, Hubberstey P, Champness NR, Schroder M. Cation-induced kinetic trapping and enhanced hydrogen adsorption in a modulated anionic metal-organic framework. Nature Chemistry 2009;1(6):487-93. 26. Wang B, Cote AP, Furukawa H, O'Keeffe M, Yaghi OM. Colossal cages in zeolitic imidazolate frameworks as selective carbon dioxide reservoirs. Nature 2008;453(7192):207-U6. 27. Rowsell JLC, Yaghi OM. Metal-organic frameworks: a new class of porous materials. Microporous and Mesoporous Materials 2004;73(12):3-14. 28. Cheetham AK, Rao CNR, Feller RK. Structural diversity and chemical trends in hybrid inorganic-organic framework materials. Chemical Communications 2006(46):4780-95. 146 29. Rueff JM, Barrier N, Boudin S, Dorcet V, Caignaert V, Boullay P, Hix GB, Jaffres PA. Remarkable thermal stability of Eu(4phosphonobenzoate): structure investigations and luminescence properties. Dalton Transactions 2009(47):10614-20. 30. Souza ER, Silva IGN, Teotonio EES, Felinto M, Brito HF. Optical properties of red, green and blue emitting rare earth benzenetricarboxylate compounds. Journal of Luminescence 2010;130(2):283-91. 31. Chen WT, Xu YP, Luo QY, Fang XN, Chen HL. [{Er(NC5H4COOH)(H2O)2}2(H5O2)(HgCI5)(HgCI4)2(H2O)2]n - Synthesis, crystal structure and properties. Zeitschrift Fur Anorganische Und Allgemeine Chemie 2008;634(3):529-33. 32. Kam KC, Young KLM, Cheetham AK. Chemical and structural diversity in chiral magnesium tartrates and their racemic and Meso analogues. Crystal Growth & Design 2007;7(8):1522-32. 33. Senkovska I, Hoffmann F, Froba M, Getzschmann J, Bohlmann W, Kaskel S. New highly porous aluminium based metal-organic frameworks: Al(OH)(ndc) (ndc=2,6-naphthalene dicarboxylate) and Al(OH)(bpdc) (bpdc=4,4'-biphenyl dicarboxylate). Microporous and Mesoporous Materials 2009;122(1-3):93-98. 34. Panella B, Hones K, Muller U, Trukhan N, Schubert M, Putter H, Hirscher M. Desorption studies of hydrogen in metal-organic frameworks. Angewandte Chemie-International Edition 2008;47(11):2138-42. 35. Yaghi OM, Li HL, Groy TL. Construction of porous solids from hydrogen-bonded metal complexes of 1,3,5-benzenetricarboxylic acid. Journal of the American Chemical Society 1996;118(38):9096-101. 36. Eddaoudi M, Li HL, Reineke T, Fehr M, Kelley D, Groy TL, Yaghi OM. Design and synthesis of metal-carboxylate frameworks with permanent microporosity. Topics in Catalysis 1999;9(1-2):105-11. 37. Guillou N, Livage C, Drillon M, Ferey G. The chirality, porosity, and ferromagnetism of a 3D nickel glutarate with intersecting 20-membered 147 ring channels. Angewandte 2003;42(43):5314-17. Chemie-International Edition 38. Livage C, Egger C, Ferey G. Hydrothermal versus nonhydrothermal synthesis for the preparation of organic-inorganic solids: The example of cobalt(II) succinate. Chemistry of Materials 2001;13(2):410-14. 39. Chen JX, Ohba M, Zhao DY, Kaneko W, Kitagawa S. Polynuclear core-based nickel 1,4-cyclohexanedicarboxylate coordination polymers as temperature-dependent hydrothermal reaction products. Crystal Growth & Design 2006;6(3):664-68. 40. Liu HC, Chen IH, Huang A, Huang SC, Hsu KF. Five related metalorganic frameworks constructed from Ln2(SO4)2(H2O)n2+ units and oxalate or acetate ligands. Dalton Transactions 2009(18):3447-56. 41. Zhao XY, Liang DD, Liu SX, Sun CY, Cao RG, Gao CY, Ren YH, Su ZM. Two Dawson-templated three-dimensional metal-organic frameworks based on oxalate-bridged binuclear cobalt(II)/nickel(II) SBUs and bpy linkers. Inorganic Chemistry 2008;47(16):7133-38. 42. Zhong RQ, Zou RQ, Pandey DS, Kiyobayashi T, Xu Q. A novel 3D microporous metal-organic framework of cadmium(II) oxalate with diamondoid network. Inorganic Chemistry Communications 2008;11(9):951-53. 43. Wang XY, Wang ZM, Gao S. A pillared layer MOF with aniontunable magnetic properties and photochemical 2+2 cycloaddition. Chemical Communications 2007(11):1127-29. 44. Hu KL, Kurmoo M, Wang ZM, Gao S. Metal-Organic Perovskites: Synthesis, Structures, and Magnetic Properties of C(NH2)3M-II(HCOO)3 (M=Mn, Fe, Co, Ni, Cu, and Zn; C(NH2)3=Guanidinium). Chemistry-a European Journal 2009;15(44):12050-64. 45. Lin JM, Guan YF, Wang DY, Dong W, Wang XT, Gao S. Syntheses, structures and properties of seven isomorphous 1D Ln3+ complexes Ln(BTA)(HCOO)(H2O)3(H2)BTA = bis(tetrazoly)amine, Ln = Pr, Gd, Eu, Tb, Dy, Er, Yb) and two 3D Ln3+ complexes Ln(HCOO)3 (Ln = Pr, Nd). Dalton Transactions 2008(44):6165-69. 148 46. Wang XY, Wei HY, Wang ZM, Chen ZD, Gao S. Formate - The analogue of azide: Structural and magnetic properties of M(HCOO)(2)(4,4 '-bpy)center dot nH(2)O (M=Mn, Co, Ni; n=0, 5). Inorganic Chemistry 2005;44(3):572-83. 47. Wang ZM, Zhang B, Zhang YJ, Kurmoo M, Liu T, Gao S, Kobayashi H. A family of porous magnets, M-3(HCOO)(6) (M = Mn, Fe, Co and Ni). Polyhedron 2007;26(9-11):2207-15. 48. Fu F, Li DS, Wu YP, Gao XM, Du M, Tang L, Zhang XN, Meng CX. A versatile V-shaped tetracarboxylate building block for constructing mixed-ligand Co(II) and Mn(II) complexes incorporating various Ndonor co-ligands. Crystengcomm 2010;12(4):1227-37. 49. Arai L, Nadeem MA, Bhadbhade M, Stride JA. A 2D cobalt based coordination polymer constructed from benzimidazole and acetate ion exhibiting spin-canted antiferromagnetism. Dalton Transactions 2010;39(14):3372-74. 50. Zhang L, Chen WW, Ge YY, Ling Y, Ouyang XP, Li J, Du M. Aniondirected supramolecular assembly of cobalt(II)-fluconazole coordination polymers: Structural diversity, fluorescent and magnetic properties. Inorganica Chimica Acta 2010;363(5):866-76. 51. Ma KR, Zhang DJ, Zhu YL. Structure and Characterization of a Novel 3D Lead Phosphonate Metal-Organic Framework with Cationic Layer Based on Weak Pb-O(N) Contact. Australian Journal of Chemistry 2010;63(3):452-57. 52. Demadis KD, Papadaki M, Aranda MAG, Cabeza A, Olivera-Pastor P, Sanakis Y. Stepwise Topotactic Transformations (1D to 3D) in Copper Carboxyphosphonate Materials: Structural Correlations. Crystal Growth & Design 2010;10(1):357-64. 53. Zhou TH, Yi FY, Li PX, Mao JG. Synthesis, Crystal Structures, and Luminescent Properties of Two Series' of New Lanthanide (III) AminoCarboxylate-Phosphonates. Inorganic Chemistry 2010;49(3):905-15. 54. Jones S, Liu HX, Schmidtke K, O'Connor CC, Zubieta J. A bimetallic oxide framework, {Cu(bpy)}2Mo4O10(O3PCH2C6H4CH2PO3)2, constructed 149 from novel {Mo4O10(O3Pr)4}n4n- chains. Communications 2010;13(2):298-301. Inorganic Chemistry 55. Morris W, Doonan CJ, Furukawa H, Banerjee R, Yaghi OM. Crystals as molecules: Postsynthesis covalent functionalization of zeolitic imidazolate frameworks. Journal of the American Chemical Society 2008;130(38):12626-+. 56. Rosi NL, Eddaoudi M, Kim J, O'Keeffe M, Yaghi OM. Advances in the chemistry of metal-organic frameworks. Paper presented at: CrystEngComm 2002 Meeting; Jun 29-Jul 01, 2002; Britol, England. 57. Lines ME, Glass AM. Principles and applications of ferroelectrics and related materials. Oxford University Press, Oxford 2001. 58. Hill NA. Why are there so few magnetic ferroelectrics? . Journal of Physical Chemistry B 2000;104:23. 59. Solans X, GonzalezSilgo C, RuizPerez C. A structural study on the Rochelle salt. Journal of Solid State Chemistry 1997;131(2):350-57. 60. Valasek J. Piezo-electric and allied phenomena in Rochelle salt. Physical Review 1921;17(4):475-81. 61. Sawyer CB, Tower CH. Rochelle salt as a dielectric. Physical Review 1930;35(3):0269-73. 62. Sandy F, Jones RV. Dielectric relaxation of rochelle salt. Physical Review 1968;168(2):481-&. 63. Mueller H. Properties of Rochelle salt. Physical Review 1940;57(9):829-39. 64. Mitsui T, Furuichi J. Domain strcuture of rochelle salt and KH2PO4. Physical Review 1953;90(2):193-202. 65. Mitsui T. Theory of the ferroelectric effect in rochelle salt. Physical Review 1958;111(5):1259-67. 66. Mason WP. Theory of the ferroelectric effect and clamped dielectric constant of rochelle salt. Physical Review 1947;72(9):854-65. 150 67. Zheng H, Wang J, Lofland SE, Ma Z, Mohaddes-Ardabili L, Zhao T, Salamanca-Riba L, Shinde SR, Ogale SB, Bai F, Viehland D, Jia Y, Schlom DG, Wuttig M, Roytburd A, Ramesh R. Multiferroic BaTiO3-CoFe2O4 nanostructures. Science 2004;303(5658):661-63. 68. Wang J, Neaton JB, Zheng H, Nagarajan V, Ogale SB, Liu B, Viehland D, Vaithyanathan V, Schlom DG, Waghmare UV, Spaldin NA, Rabe KM, Wuttig M, Ramesh R. Epitaxial BiFeO3 multiferroic thin film heterostructures. Science 2003;299(5613):1719-22. 69. Sergienko IA, Dagotto E. Role of the Dzyaloshinskii-Moriya interaction in multiferroic perovskites. Physical Review B 2006;73. 70. Neaton JB, Ederer C, Waghmare UV, Spaldin NA, Rabe KM. Firstprinciples study of spontaneous polarization in multiferroic BiFeO3. Physical Review B 2005;71(1). 71. Kimura T, Kawamoto S, Yamada I, Azuma M, Takano M, Tokura Y. Magnetocapacitance effect in multiferroic BiMnO3. Physical Review B 2003;67(18). 72. Ramesh R, Spaldin NA. Multiferroics: progress and prospects in thin films. Nature Materials 2007;6(1):21-29. 73. Cheong SW, Mostovoy M. Multiferroics: a magnetic twist for ferroelectricity. Nature Materials 2007;6:13-20. 74. Hur N, Park S, Sharma PA, Ahn JS, Guha S, Cheong SW. Electric polarization reversal and memory in a multiferroic material induced by magnetic fields. Nature 2004;429(6990):392-95. 75. Eerenstein W, Mathur ND, Scott JF. Multiferroic magnetoelectric materials. Nature 2006;442:759-65. and 76. Hill NA. Why are there so few magnetic ferroelectrics? Journal of Physical Chemistry B 2000;104(29):6694-709. 77. Ban ZG, Alpay SP, Mantese JV. Fundamentals of graded ferroic materials and devices. Physical Review B 2003;67(18). 151 78. Schmid H. Some symmetry aspects of ferroics and single phase multiferroics. Journal of Physics-Condensed Matter 2008;20(43). 79. Tanaka K. A thermomechanical sketch of shape memory effect one-dimensional tensile behavior. Res Mechanica 1986;18(3):251-63. 80. Sapriel J. Domain-wall orientations in ferroelastics. Physical Review B 1975;12(11):5128-40. 81. Aizu K. Possible species of ferromagnetic, ferroelectric, and ferroelastic crystals. Physical Review B 1970;2(3):754-&. 82. Hwang SC, Lynch CS, McMeeking RM. Ferro electric/ferroelastic interactions and a polarization switching model. Acta Metallurgica Et Materialia 1995;43(5):2073-84. 83. Kubel F, Schmid H. Structure of a ferroelectric and ferroelastic monodomain crystal of the perovskite BiFeO3. Acta Crystallographica Section B-Structural Science 1990;46:698-702. 84. Van Aken BB, Rivera JP, Schmid H, Fiebig M. Observation of ferrotoroidic domains. Nature 2007;449:702-05. 85. Spaldin NA, Fiebig M, Mostovoy M. The toroidal moment in condensed-matter physics and its relation to the magnetoelectric effect. Journal of Physics-Condensed Matter 2008;20(43). 86. Lottermoser T, Lonkai T, Amann U, Hohlwein D, Ihringer J, Fiebig M. Magnetic phase control by an electric field. Nature 2004;430(6999):541-44. 87. Fiebig M, Lottermoser T, Frohlich D, Goltsev AV, Pisarev RV. Observation of coupled magnetic and electric domains. Nature 2002;419(6909):818-20. 88. Ramirez AP. Colossal magnetoresistance. Journal of PhysicsCondensed Matter 1997;9(39):8171-99. 89. Fiebig M. Revival of the magnetoelectric effect. Journal of Physics D-Applied Physics 2005;38(8):R123-R52. 152 90. Ponomarev BK. Magneto-electrical properties of rare earth molybdates. Ferroelectrics 2002;280:261-83. 91. Vergara LI, Cao J, Rogado N, Wang YQ, Chaudhury RP, Cava RJ, Lorenz B, Musfeldt JL. Magnetoelastic coupling in multiferroic Ni3V2O8. Physical Review B 2009;80(5). 92. Finger T, Senff D, Schmalzl K, Schmidt W, Regnault LP, Becker P, Bohaty L, Braden M. Electric-field control of the chiral magnetism of multiferroic MnWO4 as seen via polarized neutron diffraction. Physical Review B 2010;81(5). 93. Shen X, Xu CH, Li CH, Zhang Y, Zhao Q, Yang HX, Sun Y, Li JQ, Jin CQ, Yu RC. Pressure effects on multiferroic LuFe2O4. Applied Physics Letters 2010:102909 (3 pp.). 94. Sander D. The correlation between mechanical stress and magnetic anisotropy in ultrathin films. Reports on Progress in Physics 1999;62(5):809-58. 95. Bochi G, Ballentine CA, Inglefield HE, Thompson CV, Ohandley RC. Evidence for strong surface magnetoelastic anisotropy in epitaxial Cu/Ni/Cu(001) sandwiches. Physical Review B 1996;53(4):R1729-R32. 96. Sablik MJ, Jiles DC. Coupled magnetoelastic theory of magnetic and magnetostrictive hysteresis. IEEE Transactions on Magnetics 1993;29(4):2113-23. 97. O'Donnell J, Rzchowski MS, Eckstein JN, Bozovic I. Magnetoelastic coupling and magnetic anisotropy in La0.67Ca0.33MnO3 films. Applied Physics Letters 1998;72(14):1775-77. 98. Gajek M, Bibes M, Fusil S, Bouzehouane K, Fontcuberta J, Barthelemy AE, Fert A. Tunnel junctions with multiferroic barriers. Nature Materials 2007;6(4):296-302. 99. Ascher E, Rieder H, Schmid H, Stossel H. Some properties of ferromagnetoelectric nickel-iodine boracite Ni3B7O13I. Journal of Applied Physics 1966;37(3):1404-&. 153 100. Scott JF, Dearaujo CAP. Ferroelectric 1989;246(4936):1400-05. 101. Scott JF. Applications 2007;315(5814):954-59. of modern memories. Science ferroelectrics. Science 102. Auciello O, Scott JF, Ramesh R. The physics of ferroelectric memories. Physics Today 1998;51(7):22-27. 103. Evans JT, Womack R. An experimental 512-bit nonvolatile memory with ferroelectric storage cell. Ieee Journal of Solid-State Circuits 1988;23(5):1171-75. 104. Parker LH, Tasch AF. Ferroelectric materials for 64 mb and 256 mb drams. Ieee Circuits and Devices Magazine 1990;6(1):17-26. 105. Turov EA. May magnetoelectric effect with week ferromagnetism and piezomagnetism exist in antiferromagnets. Uspekhi Fizicheskikh Nauk 1994;164(3):325-32. 106. Borovikromanov AS. Piezomagnetism in the antiferromagnetic fluorides of cobalt and manganese. Soviet Physics Jetp-Ussr 1960;11(4):786-93. 107. Moriya T. Piezomagnetism in CoF2. Journal of Physics and Chemistry of Solids 1959;11(1-2):73-77. 108. Pelrine RE, Kornbluh RD, Joseph JP. Electrostriction of polymer dielectrics with compliant electrodes as a means of actuation. Sensors and Actuators a-Physical 1998;64(1):77-85. 109. Zhang QM, Bharti V, Zhao X. Giant electrostriction and relaxor ferroelectric behavior in electron-irradiated poly(vinylidene fluoridetrifluoroethylene) copolymer. Science 1998;280(5372):2101-04. 110. Lee EW. Magnetostriction and magnetomechanical effects. Reports on Progress in Physics 1955;18:184-229. 111. Callen E, Callen HB. Magnetostriction forced magnetostriction and anomalous thermal expansion in ferromagnets. Physical Review 1965;139(2A):A455-&. 154 112. James RD, Wuttig M. Magnetostriction of martensite. Philosophical Magazine a-Physics of Condensed Matter Structure Defects and Mechanical Properties 1998;77(5):1273-99. 113. Zhou GX, Wu JH, Wang AK, Fenglei, He WC. Investigation of Ferroelectric Phase Transition of Rochelle Salt. Ferroelectrics 2008;366:67-73. 114. Beevers CA, Hughes W. Crystal structure of Rochelle salt. Nature 1940;146:96-96. 115. Matthias BT, Miller CE, Remeika JP. Ferroelectricity of glycine sulfate. Physical Review 1956;104(3):849-50. 116. Ye H-Y, Fu D-W, Zhang Y, Zhang W, Xiong R-G, Huang SD. Hydrogen-Bonded Ferroelectrics Based on Metal−Organic Coordination. Journal of the American Chemical Society 2008;131(1):42-43. 117. Fu D-W, Song Y-M, Wang G-X, Ye Q, Xiong R-G, Akutagawa T, Nakamura T, Chan PWH, Huang SD. Dielectric Anisotropy of a Homochiral Trinuclear Nickel(II) Complex. Journal of the American Chemical Society 2007;129(17):5346-47. 118. Ohkoshi S-i, Tokoro H, Matsuda T, Takahashi H, Irie H, Hashimoto K. Coexistence of ferroelectricity and ferromagnetism in a rubidium manganese hexacyanoferrate. Angewandte Chemie International Edition 2007;46(18):3238-41. 119. Cui H, Zhou B, Long LS, Okano Y, Kobayashi H, Kobayashi A. A porous coordination-polymer crystal containing one-dimensional water chains exhibits guest-induced lattice distortion and a dielectric anomaly. Angewandte Chemie-International Edition 2008;47(18):3376-80. 120. Cui HB, Wang ZM, Takahashi K, Okano Y, Kobayashi H, Kobayashi A. Ferroelectric porous molecular crystal, [Mn3(HCOO)(6)](C2H5OH), exhibiting ferrimagnetic transition. Journal of the American Chemical Society 2006;128(47):15074-75. 121. Sheldrick GM. SADABS User Guide, University of Göttingen: Göttingen, Germany. 1995. 155 122. Sheldrick GM. SHELXTL-97, A Program for Crystal Structure Solution and Refinement, Version 5.1; University of Göttingen: Göttingen, Germany. 1997. 123. Compounds with an r value greater than that of silicon nitride (r 7) are usually classified as high-dielectric constant materials. 124. Guo R, Cross LE, Park SE, Noheda B, Cox DE, Shirane G. Origin of the high piezoelectric response in PbZr1-xTixO3. Physical Review Letters 2000;84(23):5423-26. 125. Noheda B, Gonzalo JA, Cross LE, Guo R, Park SE, Cox DE, Shirane G. Tetragonal-to-monoclinic phase transition in a ferroelectric perovskite: The structure of PbZr0.52Ti0.48O3. Physical Review B 2000;61(13):8687-95. 126. Haertling GH. Ferroelectric ceramics: History and technology. Journal of the American Ceramic Society 1999;82(4):797-818. 127. Scott JF, Kammerdiner L, Parris M, Traynor S, Ottenbacher V, Shawabkeh A, Oliver WF. Switching kinetics of lead zirconate titanate sub-micron thin-film memories. Journal of Applied Physics 1988;64(2):787-92. 128. Scott JF, Araujo CA, Melnick BM, McMillan LD, Zuleeg R. Quantitative measurement of space-charge effects in lead zirconatetitanate memories. Journal of Applied Physics 1991;70(1):382-88. 129. Merz WJ. Domain formation and domain wall motions in ferroelectric BaTiO3 single crystals. Physical Review 1954;95(3):690-98. 130. Cohen RE. Origin of ferroelectricity in perovskite oxides. Nature 1992;358(6382):136-38. 131. Rijnders G, Blank DHA. Materials science - Build your own superlattice. Nature 2005;433(7024):369-70. 132. Ho Nyung L, Christen HM, Chisholm MF, Rouleau CM, Lowndes DH. Strong polarization enhancement in asymmetric three-component ferroelectric superlattices. Nature 2005;433(7024):395-9. 156 133. Noheda B, Cox DE. Bridging phases at the morphotropic boundaries of lead oxide solid solutions. Phase Transitions 2006;79(12):5-20. 134. Sletten E, Jensen LH. The crystal structure of dimethylammonium copper(II) formate, NH2(CH2)2[Cu(OOCH)3]. Acta Crystallographica Section B-Structural Science 1973;B 29(SEP15):1752-56. 135. Clausen HF, Poulsen RD, Bond AD, Chevallier MAS, Iversen BB. Solvothermal synthesis of new metal organic framework structures in the zinc-terephthalic acid-dimethyl formamide system. Journal of Solid State Chemistry 2005;178(11):3342-51. 136. Gough SR, Ripmeester JA, Dalal NS, Reddoch AH. Thermal hysteresis at the low temperature phase transition of ammonium dihydrogen phosphate, ammonium dihydrogen arsenate, their deuterated analogs, and of potassium dihydrogen phosphate and the effect of chromium impurity ions on the transition temperature. Journal of Physical Chemistry 1979;83(6):664-69. 137. Rogez G, Viart N, Drillon M. Multiferroic Materials: The Attractive Approach of Metal-Organic Frameworks (MOFs). Angewandte ChemieInternational Edition 2010;49(11):1921-23. 138. Lebeugle D, Colson D, Forget A, Viret M, Bataille AM, Gukasov A. Electric-field-induced spin flop in BiFeO3 single crystals at room temperature. Physical Review Letters 2008;100(22):227602. 139. Moreira dos Santos A, Parashar S, Raju AR, Cheetham AK, Rao CNR. Evidence for the likely occurrence of magnetoferroelectricity in the simple perovskite, BiMnO3. Solid State Commun. 2002;122(1-2):49-52. 140. Ascher E, Rieder H, Schmid H, Stossel H. Some Properties of Ferromagnetoelectric Nickel-Iodine Boracite, Ni3B7O13. Journal of Applied Physics 1966;37(3):1404-05. 141. Slater JC. Theory of the transition in KH2PO4. Journal of Chemical Physics 1941;9(1):16-33. 157 142. Wang XY, Gan L, Zhang SW, Gao S. Perovskite-like metal formates with weak ferromagnetism and as precursors to amorphous materials. Inorganic Chemistry 2004;43(15):4615-25. 143. Wang XY, Wang ZM, Gao S. Constructing magnetic molecular solids by employing three-atom ligands as bridges. Chemical Communications 2008(3):281-94. 144. Wang ZM, Zhang B, Otsuka T, Inoue K, Kobayashi H, Kurmoo M. Anionic NaCl-type frameworks of [Mn-II(HCOO)3-], templated by alkylammonium, exhibit weak ferromagnetism. Dalton Transactions 2004(15):2209-16. 145. Materials chemistry: 2009;462(7276):961-61. Marvellous metal-organics. Nature 146. Olson JR, Topp KA, Pohl RO. Specific-heat and thermalconductivity of solid fullerenes. Science 1993;259(5098):1145-48. 147. Angell CA. Formation of glasses from liquids and biopolymers. Science 1995;267(5206):1924-35. 148. Pekker S, Kovats E, Oszlanyi G, Benyei G, Klupp G, Bortel G, Jalsovszky I, Jakab E, Borondics F, Kamaras K, Bokor M, Kriza G, Tompa K, Faigel G. Rotor-stator molecular crystals of fullerenes with cubane. Nature Materials 2005;4(10):764-67. 149. Oh DH, Lee YH. Orientational ordering of solid C-70. Physical Review Letters 1995;75(23):4230-33. 150. Angell CA. Relaxation in liquids, polymers and plastic crystals strong fragile patterns and problems. Journal of Non-Crystalline Solids 1991;131:13-31. 151. Laszlo F, Laszlo M. Electronic properties of doped fullerenes. Reports on Progress in Physics 2001(5):649. 152. Matsuo T, Suga H, David WIF, Ibberson RM, Bernier P, Zahab A, Fabre C, Rassat A, Dworkin A. The heat-capacity of solid C-60. Solid State Communications 1992;83(9):711-15. 158 153. Melot BC, Tackett R, O'Brien J, Hector AL, Lawes G, Seshadri R, Ramirez AP. Large low-temperature specific heat in pyrochlore Bi2Ti2O7. Physical Review B 2009;79(22). 154. Lubchenko V, Wolynes PG. The origin of the boson peak and thermal conductivity plateau in low-temperature glasses. Proceedings of the National Academy of Sciences of the United States of America 2003;100(4):1515-18. 155. Shintani H, Tanaka H. Universal link between the boson peak and transverse phonons in glass. Nature Materials 2008;7(11):870-77. 156. Safarik DJ, Schwarz RB, Hundley MF. Similarities in the C[sub p]/T[sup 3] Peaks in Amorphous and Crystalline Metals. Physical Review Letters 2006;96(19):195902-4. 157. Clough S, Hill JR. Temperature-dependence of methyl-group tunnelling rotation frequency. Journal of Physics C-Solid State Physics 1974;7(1):L20-L21. 158. Achey RM, Kuhns PL, Reyes AP, Moulton WG, Dalal NS. C-13 NMR and relaxation studies of the nanomagnet Mn-12-acetate. Physical Review B 2001;64(6):7. 159. Bloembergen N, Purcell EM, Pound RV. Relaxation eggects in nuclear magnetic resonance absorption. Physical Review 1948;73(7):679-712. 160. Yaghi OM, O'Keeffe M, Ockwig NW, Chae HK, Eddaoudi M, Kim J. Reticular synthesis and the design of new materials. Nature 2003;423(6941):705-14. 159 BIOGRAPHICAL SKETCH Education Florida State University, Fl, USA, Aug. 2005 – April 2010 Ph.D. in Chemistry and Biochemistry Indian Institute of Technology, Madras (IIT-M), India , 2000 - 2004 B.Tech in Chemical Engineering (First class) Thesis: Investigations on the Use of Nanoparticles for Environmental remediation Honors and awards Best poster prize, Florida ACS meeting, Tampa, USA 2010 H.H.Sheikh Saqr Al Qasimi Fellowship, University of Cambridge, UK 2008 – 2009 Visiting fellowship, ICMR, Univ. of California, Santa Barbara, USA 2006 – 2007 Congress of Graduate Studies award, Florida State University, FL, USA December 2007 International center for materials research bursary award, UCSB, USA December 2006 Overseas Research Scholarship (ORS), University of Leeds, UK De- cember 2005 (Declined) King’s Gold medal, Best student overall performance, Senior year, )ndia May 1999 160 Merit certificate, Regional Mathematics Olympiad, India 1998 Merit certificate and Internship, Homi Bhabha Centre, TIFR, India May 1997 Teaching experience General Chemistry Laboratory, FSU, USA, Fall 2007 Taught the class and administered all grades Teaching assistant, Intr. to Thermodynamics, FSU, USA, Fall 2005 Supervision, group problem sessions and administered all the grades Research, supervision and entrepreneurial experiences Director, Founder of PM9, 2007-2008 Technology and business development director at Nanotechnology software Simulation Company which completed exclusive software licensed to our strategic partner. Guest Editor, Special Issue on CNTs, Journal of Nanoengineering and Nanosystems, 2009 Organizer and Committee member, 2008 International symposium organized by Cambridge students, Also the member of the Cambridge CNT society Research Assistant, 2006 161 Florida State University, FL, USA Visiting Researcher, 2006 – 2007 Materials Research Laboratory, University of California, Santa Barbara, CA, USA Visiting Researcher, May 2008 – Dept. of Materials Science, University of Cambridge, UK Mentor, April 2007 – June 2007 California Nano System Institute, University of California, Santa Barbara, CA, USA Supervised 3rd year undergraduate student, taught various instruments and lab skills, research resulted into a conference talk Mentor Dept. of Materials Science, University of Cambridge, UK, July 2009 – Dec 2009 Conceived the project idea and supervised a visiting postgraduate student from Chulalongkorn University, Thailand. Journal publications and patents 1. Jain P., et al. (2009) Multiferroic Behavior Associated with an Order-Disorder Hydrogen Bonding Transition in Metal-Organic Frameworks (MOFs) with the Perovskite ABX3 Architecture. J. Am. Chem. Soc. 131(38):13625-13627. (Highlighted in nature research 162 highlights: Marvelous metal-organics, doi: 10.1038/462961c; and Angew. Chem. Int. Ed. Research highlights: Multiferroic Materials: The Attractive Approach of Metal-Organic Frameworks, doi: 10.1002/anie.200906660) 2. Jain P. and Spear R. (2009) Guest editorial. Special issue on carbon nanotubes. Proc. IMechE Vol. 222 Part N: J. Nanoengineering and Nanosystems. 3. Jain P., Dalal NS, Toby BH, Kroto HW, & Cheetham AK (2008) Order-disorder antiferroelectric phase transition in a hybrid inorganic-organic framework with the perovskite architecture. J. Am. Chem. Soc. 130(32):10450-10451. (Highlighted in nature news & views article Emerging Routes to Multiferroics, doi: 10.1038/4611218A) 4. Jain P., and Pradeep T. (2005) Potential of silver nanoparticlecoated polyurethane foam as an antibacterial water filter. Biotechnology and Bioengineering, 90 (2005) 59-63. 5. Nair AS et. al. (2005) Nanoparticles-chemistry, new synthetic approaches, gas phase clustering and novel applications. Pramana, Journal of Physics, (65), 4, 631-40. 6. 7. )ndian Patent, no. urethane foam /che/ , Silver nanoparticle coated Poly- SR measurements of the hybrid organic-inorganic multiferroics [(CH3)2NH2]M(HCOO)3, M =Ni;Co;Mn. P. J. Baker, T. Lancaster, I. Franke, W. Hayes, S. J. Blundell, and P. Jain. (Submitted to Phys Rev B) 163 8. Glassy behaviour in a metal organic framework. Prashant Jain, Tiglet Besara, Naresh Dalal, Philip Kuhns, Arneil Reyes, Harold W. Kroto and Anthony K. Cheetham. (Submitted to PNAS) 9. A porous magnet with three dimensional metal-oxygen-metal and metal-ligand-metal connectivity. P. Jain, N. S. Dalal, H. W. Kroto, and A. K. Cheetham (In preparation) 164