Nano Metal Oxides for Li-Ion Batteries
Juchen Guo and Chunsheng Wang
University of Maryland
Nanoscale and nanostructured metal oxides have drawn tremendous interests from the researchers working in the field of energy storage and energy conversion technologies in recent years. In
this chapter, the state of the art of nano-metal oxide materials in Liion batteries will be discussed in attempt of a comprehensive overview.
Lithium-ion battery has been a very importance category of
rechargeable batteries since its first commercialization by Sony in
1991. It has been widely used in portable consumer electronics such
as laptop computers, digital camera, small power tools, etc. However, its potential is not limited to such small devices due to several
unique merits: Li-ion battery has the highest energy density among
all types of rechargeable batteries that are currently on the market. It
also has relatively low self discharge rate. Because of these virtues,
interests in Li-ion batteries keep growing for defense, aerospace,
smart grid system and automotive applications. To satisfy the de-
2
mands of these emerging applications, the next generation of Li-ion
batteries must achieve a holistic and striking advancement from the
current technology, specifically in four criteria - energy density, discharging and charging rate (power density), safety feature, and cycle
stability. The energy density, power density and cycle stability of Liion batteries are mainly determined by electrode materials and structures. Enhancement of the safety feature ultimately depends on development of non-flammable electrolyte and solid electrolyte to replace the current liquid electrolyte consisting of highly flammable
organic solvents. The use of nano metal oxides (nanoscale or
nanostructured) as anode materials, cathode materials, and electrolyte additives has greatly enhanced the performance of Li-ion batteries due to their unique chemical and structural properties.
14.1 Classification of Electrode Materials for Li-Ion
Batteries
Fig. 1 Schematic of Li-ion battery with graphite anode and LixMO2 cathode in the
state of discharge
Before going into further discussion, it is necessary to briefly
introduce how Li-ion battery works. For instance, the most common
cathode material is lithium cobalt oxide (LiCoO2), and anode material is graphite as shown in Figure 1. Typical electrolyte consists of
lithium salts like lithium hexafluorophosphate (LiPF6) or lithium tetrafluoroborate (LiBF4) dissolved in organic solvent such as mixture
of propylene carbonate and diethyl carbonate. During the battery
3
charging process, Li atoms in LiCoO2 become ions, migrating to
graphite anode across the electrolyte and inserting into the gaps between the graphene layers. The reverse process takes place in the
battery discharge: Li atoms stored in the layered graphite become
ions, migrating to the LiCoO2 cathode and inserting into layers of
octahedral lattices formed by cobalt and oxygen atoms. This type of
lithiation/delithiation mechanism is referred as intercalation reaction
in which Li is stored in layer-structured materials such as graphite
and lithium cobalt oxide. Nowadays, the intercalation mechanism
has been generalized to refer to all topotactic reactions of Li-ions inserting into the interior of the lattice of the host materials of which
the structures are not limited to be layered. Another lithiation/delithiation mechanism is based on reversible redox reactions
between metal oxide and Li (Li+), and it is referred as conversion reaction. According to conversion mechanism, lithiation takes place
through reduction of metal oxide by Li to produce metal and lithium
oxide, and delithiation takes place through oxidation of the formed
metal by lithium oxide. Beside these two mechanisms, in a few binary inter-metallic AB compounds, Li will reversibly displace A to
form LixB, and the formed LixB has a strong structural relationship
with parent AB compound. This mechanism is referred as displacement reaction. All current metal oxide electrode materials for Li-ion
batteries can be sorted into these three categories, except tin dioxide
(SnO2) based materials of which the lithiation/delithiation process
combines conversion and alloying reactions. Therefore, for the purpose of articulation, all the metal oxide electrode materials will be
4
discussed with respect to their different lithiation/delithiation mechanisms.
14.2 Advantage & Disadvantage of Nano-Electrode
Materials
The advantages of nano electrode materials come from their
nanometer characteristic length and their tremendously large surface
area. Generally speaking, the smaller size can shorten the Liion/electron transport pathways, and enhance the phase transformation. The large surface area can also speed up the charge transfer
reaction kinetics due to the increased contact area with electrolyte.
Enhanced Li insertion/extraction kinetics can lead to higher rate performance, even novel lithiation/delithiation mechanism. Higher surface area also can enhance the capacity through the surface Li storage mechanism [1]. Moreover, nano electrode material can better
accommodate the mechanical strain induced by the concomitant
volume change in the lithiation/delithiation process, thus improving
the cycle stability.
Unfortunately, the disadvantages of nano electrode materials
are also from their nano characteristic scale and large surface area.
The nanoscale materials will lower the packing density of the electrode thus resulting in low overall energy density of the batteries.
Also, the large surface area will promote larger amount of side reactions at the electrolyte/electrode interfaces. Therefore, the development of nano electrode materials should focus on the direction to the
5
optimized properties balancing the advantages and the disadvantages.
14.3 Nano Metal Oxide Anode Materials
14.3.1 Intercalation Metal Oxides
Materials with layered structure (graphite for anode and
LiCoO2 for cathode) are the natural choice as the Li host material
[2], but not the only ones. Materials with tunneled structures (such
as spinel) can also be used as Li storage host with intercalation
mechanism. Among them, Li4Ti5O12 and TiO2 are the two most intensively studied metal oxide anode materials.
The concept of using the B2O4 framework of an AB2O4 (A =
Li) spinel material as host structure for Li-ions storage was originally proposed by Thackeray et al. in 1980s [3]. Lithium titanium oxide, Li4Ti5O12, a ceramic material having a defect tunneled
([Li1/3Ti5/3]O4) structure, was initially proposed as an anode material
by Colbow et al. in 1989 [4] and tested by Ferg et al. [5] and Ohzuku
et al. [6] in early 1990s. Li4Ti5O12 can be lithiated over the composition range of Li4+xTi5O12 (0 < x < 3) at about 1.55 V potential versus
Li/Li+, and its theoretical lithiation capacity is 175 mAh g-1. Despite
its moderate lithiation capacity, the particular advantage of Li4Ti5O12
comparing to other spinel anodes was that it is a “zero-strain” intercalation material. The defect Li1/3Ti5/3O4 spinel framework exhibits
minimal volume change during Li-ions insertion and extraction so
that the crystal structure is better retained, thus resulting in better
cycle life. Another character of Li4Ti5O12 is its lithiation voltage of
6
1.55 V versus Li/Li+, which is considered to have two-faced effects.
On one hand, the 1.55 V lithiation voltage is higher than the decomposition voltage of the organic solvents in the electrolyte. Therefore
using Li4Ti5O12 as the anode material can eliminate the formation of
Solid Electrolyte Interface (SEI) film, which a considerable cost efficiency factor. Also, the higher lithiation voltage significantly reduces the possibility of the lithium metal plating at the anode, so that
the safety can be enhanced. On the other hand, using Li4Ti5O12 anode sacrifices the full cell working voltage because of its higher
lithiation voltage compared to graphite (0.1 to 0.2 V versus Li/Li+).
Since pure Li4Ti5O12 is an electric insulator, the advantage of
nanoscale Li4Ti5O12 is the extraordinary enhancement of Li insertion/extraction kinetics. The mean Li-ion diffusion time in an ideal
anode particle can be approximately expressed using the following
equation, if assuming Fickian diffusion.
L is the diffusion distance and D is the Li-ion diffusivity in the material. Based on this equation, the advantage of nanoscale electrode
material is obvious: the resultant short diffusion distance can reduce
the diffusion time significantly. For instance, if the particle size is
reduced to 100 nanometers from 1 micrometer, Li-ion diffusion time
can be decreased 100 times. Another advantage of nanoscale electrode materials for charge transfer kinetics enhancement is their
large surface area which results in large contact surface between
electrode and electrolyte. As an electrically insulating material, the
7
electronic conductivity of Li4Ti5O12 increases during the lithiation
reaction from the outer surface directing inward, which is not critically problematic for lithiation, since the Li+/e- transport takes place
at the outer layer anyway. During delithiation, as Li being extracted,
the conductivity starts to decrease from the outer layer of the
Li4Ti5O12 particle. Therefore, the delithiation process has worse kinetics than lithiation. Fast separation of Li+ and e- is critical to
achieve fast charge/discharge rate, which can be achieve by reduce
the Li+/e- transport pathway by using nanoscale Li4Ti5O12 materials.
Because of these advantages, nanoscale Li4Ti5O12 anode materials have been extensively studied. Among them, Kim and Cho
[7] reported synthesis and electrochemical performance of Li4Ti5O12
nanorods. The diameter of the reported Li4Ti5O12 nanorods is about
100 nm diameter as shown in Figure 2a. The notable merit of this
material is its very promising discharge rate capacity. As shown in
Figure 2b, the reversible first discharge capacity was 165 mAh g-1
under cycling rate of 0.l C (16 mA g-1), and no capacity fading was
observed up to 30 cycles between 1 and 2.5 V. At rates of 0.5 C, the
first capacity at 0.5 C was identical to that at 0.1 C. Very small capacity decreases with increasing current were observed at 5 and 10 C
(1600 mA g-1) rates, the capacity retention was 95 and 93%, showing 157 and 155 mAh g-1, respectively. As a comparison, the electrochemical performance of Li4Ti5O12 particles with 700 nm diameter is distinctly worse. Though this cannot be used as the direct
evidence of the superiority of nanorods over nanoparticles due to
their different characteristic size, it clear demonstrate the significant
8
advantage of nanoscale materials by enhancing charge transfer kinetics.
Fig. 2 TEM image of the Li4Ti5O12 nanorods, (b) rate capacity test of the Li4Ti5O12
nanorods at different C rates [7]
In light of the great promise of Li4Ti5O12 as Li intercalation
anode materials, researcher naturally began to investigate titanium
dioxides as candidates of anode materials because of their higher
theoretical lithiation capacity. The Li intercalation reaction to TiO2
can be generally expressed as the following reaction:
xLi+ + TiO2 + xe- ↔ LixTiO2
Full lithiation should lead to the formation of lithium titanium oxide
in formula of LiTiO2 (x = 1) with 335 mAh g-1 theoretical capacity.
This reaction takes place in the voltage range from 1.5 to 1.8 V.
Therefore, like Li4Ti5O12, using TiO2 as the anode materials can
avoid anode passivation and also enhance the safety feather. The investigation on TiO2 was actually not a recent idea: it started in 1980s
and continued in 1990s [8-11]. However, the sluggish performance
of the earlier TiO2 materials had merely attracted lukewarm attention. The TiO2 research really took off in virtue of the development
of nanotechnology. To date, there have been four types of titanium
dioxides being reported to have lithiation capacity, and they are rutile, brookite, anatase and bronze (TiO2(B)). These polymorphs are
the only known naturally occurring TiO2 forms to date, even bronze
is rare. Rutile is the most common and the most thermodynamically
9
stable form of TiO2. Anatase and brookite can be converted to rutile
upon heating in a temperature range of 700-1000 °C. The basic
physical and structural properties of these TiO2 polymorphs are
listed in Table 14.1 [12].
Table 14.1 Data for TiO2 polymorphs for anode materials [12]
The main problem of TiO2 polymorphs as anode materials is
their poor Li+ and electron conductivity so that the Li lithiation/delithiation reaction kinetics was largely hindered. Recent studies suggested that the TiO2 lithiation/delithiation reaction kinetics,
ultimately the rate performance, are closely related to its crystal
structural properties such as site occupation, local coordination and
energetic [13-15]. For instance, the thermodynamically stable positions for Li insertion in rutile are the octahedral sites in the ab
planes. It has been proved that the Li+ diffusion in rutile is anisotropic: the theoretical diffusion coefficient of Li-ion along ab plane
is 8 orders of magnitude lower than that along the c axis (10-14 cm2 s1
and 10-6 cm2 s-1, respectively) [16-22]. The repulsive interaction
between the Li-ions diffusing along the c axis may slow down the
diffusion, and the Li-ion pairs in the ab plane may also block the Liion diffusion along the c axis [18, 22]. Therefore, the low Li insertion capacity of rutile is mainly restrained by poor Li-ion transport
kinetics. Recent studies suggested that the lithiation capacity of rutile could be increased by reducing the structural size. Jiang et al. reported full lithiation in the first cycle using nano-sized needlelike ru-
10
tile particles (15 nm) for the first time [23]. Also, 0.7 Li per unit of
rutile can be extracted in the first delithiation. Reducing the rutile
particle size has three-fold advantages. Firstly, it decreases the Li+
and electron diffusion pathway. Secondly, the mechanical strain during Li insertion is reduced. Finally, because of the enormously enhanced surface area, Li surface storage capacity is increased [24].
Other remarkable rutile works include the rutile nanorods (10 nm ×
40 nm) reported by Hu et al. [24] and nanowires (10 nm × 200 nm)
reported by Baudrin et al. [25] The later rutile nanowires demonstrated much superior capacity than bulk rutile and even nano-size
rutile particles as shown in Figure 3.
Fig. 3 (a) Galvanostatic cycling curves of rutile TiO2 samples using a 30 mAh g-1
current between 3 V and 1 V at 20 °C; (b) the capacity retention for these samples
Although the brookite has been less reported for its Li storage capacity compared to other TiO2 polymorphs, the reported performance of brookite indicated strong dependence on the particle
size. The 10 nm sized brookite particles delivered reversible capacity of 170 mAh g-1 for more than 40 cycles, reported by Reddy et al
[26, 27]. For anatase, the Li+ diffusion in it is more facile comparing
to rutile because of its looser lattice structure. Upon the Li uptake into anatase, its original lattice structure of tetragonal body-centered
I41/amd space group changes to orthorhombic pmn21 space group
when 0.5 Li per unit of anatase is inserted [28]. Also, the lithiation
11
results in 4 % volume expansion thus causing rapid capacity fade for
bulk anatase material [29]. Reducing the anatase particle size again
can shorten the Li-ion diffusion pathway and increase the Li surface
storage capacity due to the large surface area [30, 31]. For example,
Gao et al. reported first discharge and charge capacities of 340 and
200mAh g-1, respectively, for the anatase nanotubes with 10-15 nm
diameters and 200-400 nm lengths [32].
Fig. 4(a) TEM image of TiO2(B) wires [33]; (b) TEM image of TiO2(B) tubes
[34]; (c) variation of potential with Li content for TiO2(B) nanowires and TiO2(B)
nanotubes cycled under identical conditions [34]
TiO2(B) (bronze) is rare in nature so that all reported TiO2(B)
anode material to date was synthesized. The advantage of bronze
comparing to other TiO2 polymorphs is its more open lattice structure which facilitates the Li insertion. Armstrong et al. synthesized
TiO2(B) nanowires (20-40 nm diameter and 2-10 µm length) [33]
and nanotubes (10-20 nm outer diameter, 5-8 nm inner diameter and
~ 1 µm length) [34] as shown in Figure 16.4a and 4b, respectively.
The TiO2(B) nanowires demonstrated superior lithiation capacity
(Li0.91TiO2, 305 mAh g-1 specific capacity) to the bulk material
(Li0.71TiO2, 240 mAh g-1 specific capacity). During the lithiation
process, there is no detectable volume change taking place due to the
more open lattice structure. Comparing to nanoscale TiO2(B) particles with similar diameter, even both showed similar first cycle lithiation capacity, the capacity retention of the nanowires was far more
12
better. The TiO2(B) nanotubes showed marginally higher lithiation
capacity (Li0.98TiO2, 325 mAh g-1 specific capacity) than the nanowires. However, the TiO2(B) nanowires demonstrated better kinetics in spite of lager diameter. As shown in Figure 16.4c, the plateaus
of the charge/discharge curves of TiO2(B) nanowires are flatter and
closer to each other, which indicates small overpotential. The irreversible capacity of the nanowires is also smaller.
TiO2 polymorphs have demonstrated very attractive electrochemical properties as anode materials, such as higher lithiation
voltage avoiding electrode passivation and enhancing safety feature.
The nanoscale TiO2 further improved the charge transfer reaction
kinetics by shortening the Li+ and electron transport pathway. However, there are still a few intrinsic disadvantages of TiO2 that may
need further investigation. As it has relatively higher lithiation potential versus Li/Li+ redox couple, the full cells with TiO2 anode and
typical cathode are subject to lower cell voltage. However, exceptions may be possible if a high potential cathode material can be
found. One example is TiO2(B) nanotubes/Li[Ni0.5Mn1.5]O4 cell reported by Armstrong et al [35], which could achieve a 3 V overall
cell potential. The other serious problem of nanoscale TiO2 materials
is the continuously irreversible capacity on every cycle, except one
report by Armstrong et al [33]. The irrecoverable capacity is mainly
attributed to the electric insulating nature of the TiO2. As previously
mentioned in this chapter, the electric insulation can hurt Li extraction more than insertion. Because the outer layer of the particle become electric insulating, it will be more difficult to extract all insert-
13
ed Li. The current development indicates that even the dimension of
TiO2 has been reduced to scale of tens of nanometers, the transport
pathway was still not efficient enough for fast electron and Li+ separation to completely deplete the inserted Li. This problem can definitely jeopardize the real application of TiO2 as Li-ion battery anode.
One solution is to incorporate electric conductive nano-sized composite into TiO2 to form nanostructured material. One great example
is that Guo et al. recently reported a mesoporous RuO2-anatase TiO2
composite [36]. The RuO2 nanoparticles formed an electric conductive network in the mesoporous TiO2 structure so that the electrochemical performance was enhanced. Liu and coworkers reported a
hybrid nanostructure of rutile TiO2 and graphene [37]. Both works
demonstrated reduced irreversible capacity and largely improved
fast charge/discharge performance.
Other reported intercalation metal oxides include oxides of
vanadium, niobium from Group 5B and molybdenum, tungsten from
Group 6B in the Periodic Table of the Elements. The concept of using these oxides as Li-ion battery electrode taking the advantage of
their layered lattice structures was proposed by Whittingham et al. in
the 1970s [38]. Binary vanadium oxides with octahedral or distorted
octahedral coordination are known for all oxidation states between
V5+ and V2+. The typical high lithiation-delithiation voltages of most
of the vanadium oxides makes them suitable as cathode materials.
One exception is VO2(B), a vanadium dioxide formula having monoclinic metastable shear structure. Its advantage as Li storage material is its structural stability arising from an increased edge sharing
14
and the consequent resistance to lattice shearing during cycling [39].
VO2(B) received particular interest as an anode material for aqueous
electrolyte Li-ion batteries because of its proper electrode potential
of 2.5V versus Li/Li+ [40]. Flower-like VO2(B) nanoparticles have
been synthesized by Zhang et al [41], and tested as anode material
coupled with LiMn2O4 cathode. The flowerlike VO2(B) demonstrated superior electrochemical properties to VO2(B) nanobelt and carambola-like nanoparticles [41]. However, the Li-ion batteries with
aqueous phase electrolyte based on VO2(B) suffers very low energy
density which is about 75 mAh g-1 at the first cycle. It can be attributed to the cell voltage restrict to avoid H2O decomposition. Beside VO2(B), some vanadium oxide based compounds such as LiVO2 [42], LiV3O8 [43], MnV2O6 [44], RVO4 (R = In, Cr, Fe) [45]
and LiMVO4 (M = Cd, Co, Zn, Ni, Cu and Mg) [46] were also studied as anode materials. The niobium oxides have similar properties
as vanadium oxides. Ternary niobium oxide such as Ag nanoparticle-doped LiNbO3 [47] was investigated as the anode materials, as
well as KNb5O13 and K6Nb10.8O30 [48]. LiNbO3 demonstrated low
lithiation voltage (< 0.5 V) and high first cycle capacity. However,
the first delithiation capacity is only 12% to 13% of the first lithiation one. These niobium oxides demonstrated capacities between
100 and 200 mAh g-1 within the voltage range of 1.0 to 1.5 V versus
Li/Li+. Though there has not been nanoscale or nanostructured niobium oxides reported to date, it can be speculated that these types of
material can possess enhanced electrochemical performance.
15
The molybdenum dioxide (MoO2) and tungsten dioxide
(WO2) as Li-ion battery anode material were systematically investigated by Auborn and Barberio in 1987 for the first time [49]. MoO2
nano-particles were synthesized by Yang et al. from reduction of
Molybdenum trioxide (MoO3) [50]. This rutile-like MoO2 material
demonstrated a reversible capacity of 318 mAh g-1 for 20 cycles at 5
mA cm-2 current density. Also, 85% of the reversible capacity was
within the range of 1.0 to 2.0 V. The same research group also synthesized MoO2 tremella-like nanoparticles consisting of nanosheets,
which showed reversible capacity about 600 mAh g-1 at 0.5 mA cm-2
current density [51]. Superior electrochemical performance was
achieved by Dillon and coworkers based on the nanoscale MoOx
consisting of Mo, MoO2 and MoO3 phases [52]. Reversible capacity
of 600 mAh g-1 over 50 cycles at C/5 charge/discharge rate. MoO3
and tungsten trioxide (WO3) are also promising Li intercalation materials for their layered structure. The lithiation/delithiation potential
of WO3 is around 4 V so that it is a cathode material [53]. On the
other hand, MoO3 has proper Li intercalation potential as anode material and relatively high theoretical capacity of 1117 mAh g-1.
MoO3 has an orthorhombic crystal structure composed of distorted
MoO6 octahedral layers. The reported electrochemical performance
of the nanoscale MoO3 materials varies depending on different morphologies. Lithiated MoO3 nanobelt (200 nm wide and 2-6 µm long)
was reported by Mai et al [54]. Compared with non-lithiated MoO3
nanobelt, the lithiated one showed lower lithiation capacity, but better cycle stability and less lithiation-delithiation hysteresis. Howev-
16
er, the reported capacity (~ 250 mAh g-1) was significantly lowered
than the theoretical capacity and the plateaus of the lithiationdelithiation voltage plot are above 2.25 V which was not ideal for
anode due to the resultant low full cell potential. Recently, similar
MoO3 nanobelt with a uniform carbon coating was reported by Hassan et al [55]. The reported result was very attractive: the carboncoated MoO3 nanobelt could retain capacity of 1064 mAh g-1 after
50 cycles with 0.1C between 3.0 and 0.05 V, and no trend of fade
was observed. The first cycle lithiation capacity (~1300 mAh g-1)
exceeded the theoretical capacity which could be attributed to the
formation of the solid electrolyte interphase (SEI) film or the surface
Li storage. Also, the volume change induced MoO3 pulverization
was observed from the SEM image. MoO3 nanoparticles (~ 20 nm)
were synthesized by Lee and coworkers [56]. These MoO3 nanoparticles demonstrated superior cycle stability and great capacity:
Above 600 mAh g-1 capacity could be delivered after 150 cycles between 3 V and 0.005V with C/2 charge/discharge rate. The performance was compared to micron-sized MoO3 particles of which the
performance is far inferior. Therefore, the excellent performance of
MoO3 nanoparticles can be attributed to their nano size.
As summery for the intercalation metal oxide anode materials, they all possess layered or tunneled structures. Typical lithiation
reaction always occurs with concomitant lattice volume expansion
which has negative influence on the cycle stability. The lithiation
capacity of intercalation metal oxides is limited by the availability of
the lattice sites and suppressed by the redox competition with other
17
phases. Furthermore, most of the intercalation metal oxides have low
Li+ diffusivity and electric conductivity. Therefore, the slow
ion/electron transport kinetics is really the bottleneck to achieve full
capacity and fast charge/discharge rate. The advantages of nanoscale
materials mainly are the shortened Li+ and electron transport pathway and the enhanced surface area. As the result, the kinetics can be
greatly enhanced. Higher grain interface area in nanoscale materials
can also enhance the storage of the Li. The problem of the current
intercalation metal oxide anode materials is the irreversible capacity
(low coulombic efficiency), which can still remain even the material
size is reduced to ten of nanometers. This observation may indicate
that reducing size is not the panacea, the conductivity must also be
enhanced. The current solution for this problem is conductive layer
coating and conductive composite doping.
14.3.2 Conversion Metal Oxide Materials
In 2000, Poizot et al. reported a new lithiation-delithiation
mechanism of Li storage in transition metal oxides which can be
used as anode materials [57]. This new mechanism is different from
the aforementioned Li insertion/extraction, and can generally be expressed as
2xLi + MOx ↔ M + xLi2O
(M = Fe, Ni, Co, Cu, Mn, Cr, Ru, Zn)
18
During the lithiation (metal oxide reduction) reaction, the metal oxide is reduced by lithium at a certain potential. In the delithiation
(metal oxide oxidation) reaction, metal is oxidized by Li2O to their
original valence state. This mechanism is referred as conversion reaction. The lithiation through metal oxide reduction has actually
been well recognized and investigated for a long time. For instance,
Li and manganese dioxide (MnO2) is one anode/cathode pair for
primary Li battery. However, this reaction was considered as irreversible until the investigation of Poizot et al. The detailed study
shows that the lithiation resulted in 2-5 nm metal grains embedded
in an amorphous Li2O matrix [57]. This nanostructure greatly reduces the Li+ and electron transport pathway, and facilitates moving Li+
through the Li2O phase and electrons through the metal phase, thus
making reversible lithiation/delithiation possible. Therefore, this
conversion mechanism is indeed one excellent example of the applications enabled by the nanotechnology.
However, the delithiation capacity is not completely matched
with the lithiation capacity. Most of the results of conversion metal
oxide anode materials showed considerable amount of irreversible
capacity in the first cycle. The only exception is ruthenium dioxide
reported by Balaya et al. [58], because RuO2 has unusually high
electric conductivity. However, RuO2 is not a practical anode material because of its rarity. The cause of the irreversibly capacity is the
insufficient Li+ and electron conductivity for complete delithiation.
Another common problem for metal oxide anode materials caused
by the same reason is the large hysteresis of charge/discharge volt-
19
age profile. Ideal electrode should have voltage hysteresis as small
as possible to have high energy density efficiency. The work of Li et
al. clearly demonstrated that reducing the particle size of the metal
oxide could effectively lower the potential hysteresis [59].
Since the original study by Poizot et al, numerous investigations on nanostructured metal oxides with conversion mechanism
have been carried out. To date, the most commonly investigated
metals include iron, cobalt, nickel, copper, manganese, and chromium. All valence states of these metal oxides can theoretically be
used as anode materials. However, the conversion of high valence
metal oxides is complex comparing to the low valence ones with
rock-salt like structure. Larcher and coworkers demonstrated the Liinserted intermediates in forms of LixCo3O4 and LixFe2O3 for conversion of Co3O4 and α-Fe2O3, respectively [60, 61]. Both Co3O4
and α-Fe2O3 possess tunneled spinel structures, thus Li initially inserting into these materials following the intercalation mechanism.
This process had been long recognized. However, Larcher et al.
found out that further lithiation could result in deep structural modification to the rock-salt structure. Finally the metallic phase was
formed as nano-grains dispersed in Li2O matrix. Similar process
could be applied to Fe3O4. The formation of the Li-intercalated intermediate phase is closely related to the material size [61]. For instance, 1 Li could be taken into LixFe2O3 when nano-sized α-Fe2O3
was used, whereas x is only about 0.05 for micron-sized α-Fe2O3.
For anode application, the metal oxides should have high capacities
which make higher valence metal oxides be the better choice such as
20
Cr2O3, Mn2O3, and Fe2O3. They also should have low potentials, in
terms of which the merit is in order of Cr2O3 > Mn2O3 > Fe2O3
based on theoretical calculation [62]. The spherical Cr2O3 nanoparticle reported by Hu et al. exhibited a lithiation voltage lower than 0.5
V versus Li/Li+ and an initial lithiation capacity of 1200-1400 mAh
g-1which is higher than its theoretical capacity of 1058 mAh g-1 [63].
The excess capacity can be attributed to the surface Li storage
mechanism. The average delithiation voltage of Cr2O3 is about 1.2 V
which is also much lower than that of most of the other metal oxides. Therefore, Cr2O3 seems like a better suitable conversion metal
oxide anode than the others.
Fig. 5(a) SEM image of the α-Fe2O3 nanotube arrays; (b) TEM image and SAED
pattern of α-Fe2O3 nanotubes; (c) cycle performance at C/5 rate for α-Fe2O3 nanotube arrays and carbon coated α-Fe2O3 nanotube arrays
Beside nanospheres, a wide variety of nanoscale metal oxides have been synthesized and tested as anode materials in the last
decade. The geometries include nanotube or nanowire arrays [6474], nanoflakes [75], nanospindles [76], flower-like [77, 78], hollow
sea-urchin-like nanoparticles [79], and mesoporous structures [80,
81]. Among them, Chen and coworkers reported the synthesis and
electrochemical performance of α-Fe2O3 (hematite) nanotubes as anode material [64]. The reported α-Fe2O3 nanotubes demonstrated
very high initial lithiation capacity. The α-Fe2O3 nanoflakes reported
by Reddy et al. demonstrated stable charge-discharge capacity above
21
600 mAh g-1 up to 80 cycles despite of the 70% irreversible capacity
at the first cycle [75]. Recently, Liu et al. reported carbon-coated αFe2O3 nanotube arrays with impressive capacity retention as shown
in Figure 16.5 [74]. Lou et al. reported a mesoporous nanoneedle
structure of Co3O4 as shown in Figure 16.6 [81]. The mesoporous
structure could arguably enhance the charge transfer kinetics and cycle stability, thus resulting in promising electrochemical performance. Beside the aforementioned usual metal oxides, carbon coated
ZnO nanorod arrays were also investigated by Liu et al. as anode
material [82].
Fig. 6 (a) SEM image of the mesoporous Co3O4 nanoneedles; (b) cycle performance at current density of 150 mAh g-1 for mesoporous Co3O4 nanoneedles prepared from different temperatures
Despite some attractive characters of the metal oxide anode
materials, there are still some intrinsic disadvantages of these materials. Firstly, most of them have relatively high lithiation potential
(above 1 V versus Li/Li+) which will cause low overall cell voltage.
Secondly, most of the reported delithiation capacities of these metal
oxides can only be achieved in a wide potential window, typically
from a near-zero lower limit to upper limit of 3 V. Obviously not entire such capacities can be accounted for real-life battery applications. Beside these intrinsic problems, there are also some formidable technical difficulties including large irreversible capacity (low
coulombic efficiency) and large charge/discharge hysteresis (typical-
22
ly about 1 V) both of which are due to the poor electronic properties.
A number of techniques have been used to enhance the kinetics
through improving the electronic properties, including carbon coating and metal doping [77, 83]. However, substantial improvement
has not been achieved. Therefore, metal oxide anode materials still
remain as a concept rather than realistic choice for Li-ion batteries.
14.3.3 Displacement Metal Oxide Materials
The concept of displacement mechanism is to displace one
metal A from a binary inter-metallic AB by lithium reduction. The
AB proves a host framework for the inserting and extracting metal A
and Li, respectively. Therefore, the intense volume change by direct
alloying can be limited. To date, there has been only one reported
metal oxide, namely Cu2.33V4O11, obeying the displacement mechanism [84]. In this material, Cu inserted in [V4O11]n layered structures. 5.6 Li per Cu2.33V4O11 can be reversibly inserted and extracted
into the layered structure via displacement reaction. The total capacity of Cu2.33V4O11 is about 270 mAh g-1, However, the lithiation
potential is pretty high at 2.5 V which makes it more suitable as a
cathode material.
14.3.4 Tin Dioxides Based Anode Materials
SnO2 is another well-investigated anode material. Unlike
other metal oxide anode materials, the lithiation/delithiation process
of SnO2 is a combination of conversion and allaying mechanisms
23
which can be described as follows: In the first lithiation reaction,
SnO2 is irreversibly reduced to metallic Sn by Li:
4Li+ + 4e- + SnO2 → 2Li2O + Sn
Further lithiation obeys the reversible allaying reaction:
xLi+ + xe- + Sn ↔ LixSn
Therefore, SnO2 conversion only takes place as the initial part of the
first lithiation. The following cycles follow the allaying/dealloying
reaction between Sn and Li. Sn has very high lithiation capacity: In
theory as many as 4.4 Li can be inserted in 1 Sn. Such high capacity
will induce severe volume change which can result in particle pulverization, thus causing rapid capacity fade. The advantage of using
SnO2 as anode material instead of Sn is that the initial conversion
reaction will produce nanoscale Sn grains dispersed in the Li2O matrix. The Li2O matrix is inert in the alloying/dealloying reactions,
and can function as the cushion structure to accommodate the Sn
volume change. In addition to the small grain size, Sn is an electronic conductor which can facilitate high capacity and fast
charge/discharge rate. Therefore, using SnO2 as anode materials can
significantly enhance the cycle stability of the anode. However, it is
achieved on the sacrifice of large irreversible capacity in the first cycle. The reported nanoscale SnO2 anode materials include nanospheres [85, 86], nanowires [87, 88], flower-like nanoparticles [89],
and porous cage-like nanospheres [90]. Figure 16.7 shows the morphology and performance of the porous cage-like SnO2 anode materials reported by Yu and coworkers.
24
Fig. 7 (a) SEM images of thin film of SnO2 based porous spheres; (b) cyclability
of SnO2 based composite film of porous spheres
14.4 Nano Metal Oxide Cathode Materials
Lithium transition metal oxides and lithium transition metal
phosphates represent the most successful cathode electrode materials
for Li-ion batteries. When using lithium metal anode, some metal
oxides such as MnO2, V2O5 can be used as cathodes. The power and
cycling life of low-potential cathodes have been greatly improved by
simple shrinking particle size from micro- to nano-scale due to short
diffusion length, high electrode/electrolyte interface, and fast phase
transformation. However, high contact area between electrode and
electrolyte in nano-scale high-potential cathodes also promote decomposition of the electrolyte and formation of a solid electrolyte
interface layer on the surface of the particles, resulting in fading of
cycle life especially at high temperature [91, 92]. For Li-Mn-O cathode, the use of small particles also increases undesirable dissolution
of Mn. Surface coating with a nanolayer of inert oxides (SnO2,
Al2O3, MgO, ZrO2) can alleviate Mn dissolution and SEI formation
but also decreases the reaction rate, scarifying the benefit of nanoscale particle.
14.4.1 Nanoscale Cathode Materials
25
A great improvement in rate performance and cycling stability of V2O5 nanotubes [93] and nanowires [94] and LiCoO2 nanowires have been reported [95]. High-quality single crystalline cubic
spinel LiMn2O4 nanowires were synthesized by Hosono et al. [96]
using Na0.44MnO2 nanowires as a self-template. These single crystalline spinel LiMn2O4 nanowires show high thermal stability and excellent performance at high rate charge-discharge with excellent cycle stability. Spinel LiMn2O4 nanorods have an average diameter of
130 nm and length of 1.2 μm were also synthesized by Cui’s group
[97] using a simple solid-state reaction. The LiMn2O4 nanorod
cathodes have a high charge storage capacity at high power rates
compared with commercially available powders.
Nano LiFePO4 cathodes have been extensively investigated
in term of rate performance and cycling stability. LiFePO4 has a
gravimetric capacity of 170 mAh g-1, low cost, high thermal and
chemical stability, less reactive with electrolyte due to low potential,
and very flat discharge potential, which make this cathode as promising cathode for hybrid electric vehicle batteries. The lithiation and
delithiation of bulk LiFePO4 involves a phase transformation between LixFePO4 (x = 0.032) and Li1-yFePO4 (y = 0.038) at 3.48V [98,
99] and Li ion transport mainly along the (010) direction. However,
the miscibility gap and equilibrium phase transformation potential
are highly size-dependent. This miscibility gap is reduced to values
of y = 0.12 and x = 0.06 when particle size decreases to 40 nm, as
shown in Figure 8 [100]. Values of y = 0.17 and x = 0.12 are ob-
26
tained for 34 nm particles [101]. The dramatic shrinking of the miscibility gap at nano-scale particle size is clear seen in Figures 16.8
and 16.9. Stoichiometric 30-40 nm particles of LiFePO4 exhibit twophase behavior over 70% of composition range, while highly defective materials with the same particle size demonstrates solid-solution
behavior over the entire composition range [102]. The size dependence of miscibility gap has been explained by the increasing contribution of elastic energy induced by the formation of coherent twophase interphase in small particle. The coexistence of two crystallographic phases within one particle leads to a phase boundary energy
penalty, due to the difference in lattice parameters of the phases.
This strain-induced energy can destabilize a two-phase coexistence
in small particles, decreasing the energy gain from phase transformation and narrowing the miscibility gap.
Fig. 8 OCV curves measured for LixFePO4 at room temperature with various
mean particles sizes of 200, 80, and 40 nm. Reproduced from reference [100] with
permission
Fig. 9 Temperature-dependent of LiFePO4 with different particle sizes. Reproduced from reference [102] with permission
Fig. 10 Equilibrium potentials of LiFePO4 with different particle sizes measured
by GITT [105]
The particle size of LiFePO4 not only changes the miscibility
gap, but also affects the equilibrium potential and potential hystere-
27
sis [104, 105]. The particle size changes the equilibrium phase diagram of LiFePO4, as demonstrated in Figure 16.9 [103]. Our results
demonstrates that equilibrium discharge potential of 40nm LiFePO4
is 8 mV higher than bulk LiFePO4, as evidenced in Figure 16.10.
The narrowed miscibility gap and increased equilibrium discharge
potential of nano-LiFePO4 greatly reduces the accommodation energy of phase transformation (Figure 16.11) and increases the interface
mobility of phase transformation (Figure 16.12). Therefore, use of
nano-scale LiFePO4 not only reduces the Li-ion diffusion path, but
also enhances the phase transformation kinetics, resulting in a great
increase in rate performance of LiFePO4.
Fig. 11 Discharge accommodation energies of LiFePO4 with different particle
size [105]
Fig. 12 Interface mobilities of (a) bulk and (b) nano LiFePO4 obtained from phase
transformation GITT [105]
14.4.2 Nanostructured Cathode Materials
Although use of nano-scale cathode materials can enhances
the power of cathode, the tap density and energy density drop drastically as the particle size decreases [106]. So the use of nano-scale
materials might lead to high power but could result in very low volumetric energy storage. To avoid low volumetric energy density and
28
high reactive surface, but retain the advantage of the nano-scale, attention has turned to nanostructured cathode materials. Nanostructured cathode for Li-ion battery has been reviewed by Wang and
Cao [107]. The benefit of use nanostructured cathode materials was
evidenced from LiMnO2 cathode. Li can be lithiated/delithiated in
LixMnO2 spinel over the range of 0 < x < 2. Cycling is usually confined to the range 0 < x < 1 to avoid the transformation of cubic
LiMn2O4 to tetragonal Li2Mn2O4, which leads to a marked loss of
capacity. However, the lattice stress caused by Jahn-Teller distortion
can be accommodated more easily in the case of nano-domain structure. The entire nano-domains can spontaneously change between
cubic and tetragonal structures during lithiation/delithiation. Therefore, the capacity retention is greatly improved compared with the
normal bulk LiMnO2 [108].
14.5 Nano Metal Oxides in Electrolyte
The conventional electrolyte for Li-ion batteries is Li salt solution based on electrochemical stable organic solvents. The advantage of the conventional electrolyte is the high Li-ion conductivity, but it is undermined by the flammability of the organic solvent
that is a serious safety concern. There are several strategies attempting to solve this problem, including using aqueous electrolytes, solid
ceramic electrolytes, ionic liquid electrolytes and solid polymeric
29
electrolytes [109]. To the best knowledge of the authors, the first
three methodologies do not involve application of nanostructured
metal oxides. Therefore, only the application of nanostructured metal oxides in polymeric electrolytes will be discussed in this section.
In addition to the potential safety enhancement, solid polymeric
electrolytes can also provide the simplicity of manufacture and a
wide variety of battery geometries. Strictly speaking, the solid polymeric electrolytes only refer to those solvent free membranes based
on the mixture of Li salts and polymers. Among them, the most attractive membranes are the ones based on poly(ethylene oxide)
(PEO) and a variety of Li salts such as LiPF6 or LiCF3SO3 [110].
The conduct of Li-ions in these membranes is through the complexation between the ether groups in PEO and the Li-ions. However, the
ionic conductivity is poor at room temperature so that the real-life
application of this type of electrolyte has not been achieved.
A very effective method to enhance the conductivity of the
PEO electrolyte is addition of nano-sized metal oxide particles as
filler, such as TiO2, Al2O3, and SiO2 [111] as shown in Figure 16.13.
A long recognized effect of fillers, traditionally referred as plasticizer, is to lower the degree of crystallinity of the polymer. PEO is a
polymer that tends to crystallize, so that the crystalline domains will
block the Li-ions transport in the amorphous regions. The metal oxide nanoparticle fillers can inhibit the PEO chain to crystallize at
lower temperature. Furthermore, the ionic conductivity enhancement
upon addition of metal oxide nanoparticles was also explained by
the space charge theory [112]. Accordingly, the ionic could be pro-
30
moted by the Lewis acid-base interactions between the surface state
of the metal oxide nanoparticles with both the polymer chains and
the anion of the Li salt. This hypothesis could be proved by the close
relationship between the degree of conductivity and the filler surface
modification. It was demonstrated that the sulfate-promoted superacid zirconia (S-ZrO2) fillers could greatly improve both the ionic
conductivity and the Li-ion transference number due to its high acidic surface state [113].
Fig. 13 Arrhenius plots of the conductivity of filler-free PEO-LiClO4 and of nanocomposite PEO-LiClO4.10 wt% TiO2 or 10 wt% Al2O3 was used based on total
weight (PEO:LiClO4 = 8:1 in all cases) [111]
14.6 Conclusion and Outlook
The state of the art of application of nanoscale and
nanostructured metal oxides in development of Li-ion batteries was
summarized and discussed in this chapter. A large number of metal
oxides can be used as anode and cathode materials in Li-ion battery
according to their specific structural and chemical properties. The
advantages of metal oxides with nano-dimension are undoubted:
nano-sized metal oxides can enhance the lithiation/delithiation kinetics owing to their smaller size and larger surface area. Therefore, the
rate capacity can be significantly enhanced. Even new lithiation/delithiation mechanism, conversion reaction, can be enabled.
31
However, the smaller size and large surface area also bring some
downside effects including low pack density (low energy density)
and large surface side reaction. Future investigation should emphasize to compress these shortcomings without sacrifice the merit of
the nanostructured metal oxides.
One possible means to achieve this goal is to introduce mesoporous (pore size between 2 to 50 nm) structure into bulk metal oxides to form hierarchical nanostructures. For instance, the electric
conductive additive, or dopant should be uniformly dispersed in the
body of metal oxide, and form interconnected networks. The aforementioned RuO2 incorporated anatase TiO2 mesoporous composite
[36] could serve a good example of this type of structure. The overall bulk size could lead to higher packing density, and the uniformly
mixed nanoscale metal oxide domains and nanoscale conductive
network can provide superior charge transfer kinetics. In addition,
mesoporous structure can facilitate the contact with electrolyte.
Therefore, this true three-dimensional structure could exhibit better
performance than the current majority zero-dimensional (particle)
and one-dimensional (tube or wire) structures.
32
References
1.
2.
3.
4.
5.
6.
7.
8.
9.
10.
11.
12.
13.
14.
15.
16.
17.
18.
19.
20.
21.
22.
23.
Maier, J.: Nanoionics: ion transport and electrochemical storage in confined systems.
Nat. Mater. 4, 805 (2005)
Whittingham, M.S., Chianelli, R.R.: Layered compounds and intercalation chemistry:
An example of chemistry and diffusion in solids. J. Chem. Educ 57, 569 (1980)
Thackeray, M.M., Johnson, P.J., De Picciotto, L.A., Bruce, P.G., Goodenough, J.B.:
Electrochemical extraction of lithium from LiMn2O4. Mater. Res. Bull. 19, 179 (1984)
Colbow, K.M., Dahn, J.R., Haering, R.R.: Structure and electrochemistry of the spinel
oxides LiTi2O4 and Li4/3Ti5/3O4. J. Power Sources 26, 397 (1989)
Ferg, E., Gummow, R.J., de Kock, A., Thacheray, M.M.: Spinel Anodes for LithiumIon Batteries. J. Electrochem. Soc. 141, L147 (1994)
Ohzuku, T., Ueda, A., Yamamoto, N.: Zero-Strain Insertion Material of
Li[Li1/3Ti5/3]O4 for Rechargeable Lithium Cells. J. Electrochem. Soc. 142, 1431 (1995)
Kim, J., Cho, J.: Spinel Li4Ti5O12 Nanowires for High-Rate Li-Ion Intercalation Electrode. Electrochem. Solid State Lett. 10, A81 (2007)
Bonino, F., Busani, L., Lazzari, M., M. Manstretta, Rivolta, B., Scrosatti, B.: Anatase
as a cathode material in lithium – organic electrolyte rechargeable batteries. J. Power
Sources 6, 261 (1981)
Ohzuku, T., Hirai, T.: An electrochromic display based on titanium dioxide. Electrochim. Acta 27, 1263 (1982)
Zachou-Christiansen, B., West, K., Jacobsen, R., Atlung, S.: Lithium insertion in different TiO2 modifications. Solid State Ion. 28-30, 1176 (1988)
Huang, S.Y., Kavan, L., Exnar, I., Gratzel, M.: Rocking Chair Lithium Battery Based
on Nanocrystalline TiO2 (Anatase). J. Electrochem. Soc. 142, L142 (1995)
Yang, Z., Choi, D., Kerisit, S., Rosso, K.M., Wang, D., Zhang, J., Graff, G., Liu, J.:
Nanostructures and lithium electrochemical reactivity of lithium titanites and titanium-oxides: A review. J. Power Sources 192, 588 (2009)
Tielens, F., Calatayud, M., Beltran, A., Minot, C., Andres, J., Lithium insertion and
mobility in the TiO2-antase/titanate structure: A periodic DFT Study. J. Electroanal.
Chem. 581, 216 (2005)
Gligor, N.M., de Leeuw, S.W.: Lithium diffusion in rutile structured titania. Solid
State Ionics 177, 2741 (2006)
Lunell, S., Shashans, A., Ojamae, L., Lindstrom, H., Hagfeldt, A.: Li and Na Diffusion
in TiO2 from Quantum Chemical Theory verus Electrochemical Experiment. J. Am.
Chem. Soc. 119, 7374 (1997)
Macklin, W.J., Neat, R.J.: Performance of titanium dioxide-based cathodes in a lithium polymer electrolyte cell. Solid State Ion. 53, 694 (1992)
Koudriachova, M.V., Harrison, N.M., de Leeuw, S.W.: Effect of Diffusion on Lithium
Intercalation in Titanium Dioxide. Phys. Rev. Lett. 86, 1275 (2001)
Koudriachova, M.V., Harrison, N.M., de Leeuw, S.W.: NH4Y and HY zeolites as electrolytes in hydrogen sensors. Solid State Ion. 35, 157 (2003)
Johnson, O.W.: One-Dimensional Diffusion of Li in Rutile. Phys. Rev. 136, A284
(1964)
Gligor, F., de Leeuw, S.W.: Lithium diffusion in rutile structured titania. Solid State
Ion. 177, 2741 (2006)
Koudriachova, M.V., Harrison, N.M., de Leeuw, S.W.: Effect of Diffusion on Lithium
Intercalation in Titanium Dioxide. Phys. Rev. Lett. 86, 1275 (2001)
Shashans, A., Lunell, S., Bergstroem, R.: Theoretical study of lithium intercalation in
rutile and anatase. Phys. Rev. B 53, 159 (1996)
Jiang, C., Honma, I., Kudo, T., Zhou, H.: Nanocrystalline Rutile TiO2 Electrode for
High-Capacity and High-Rate Lithium Storage. Electrochem. Solid State Lett. 10,
A127 (2007)
33
24. Hu, Y.-S., Lorenz, K., Guo, Y.-G., Maier, J.: High Lithium Electroactivity of Nanometer-Sized Rutile TiO2. Adv. Mater. 18, 1421 (2006)
25. Baudrin, E., Cassaignon, S., Koesch, M., Jolivet, J.-P., Dupont, L., Tarascon, J.M.:
Structural evolution during the reaction of Li with nano-sized rutile type TiO2 at room
temperature. Electrochem. Commun. 9, 337 (2007)
26. Reddy, M.A., Pralong, V., Varadaraju, U.V., Raveau, B.: Crystalline Size Constraints
on Lithium Insertion into Brookite TiO2. Electrochem. Solid-State Lett. 11, A132
(2008)
27. Reddy, M.A., Kishore, M.S., Pralong, V., Varadaraju, U.V., Raveau, B.: Lithium Intercalation into Nanocrystalline Brookite TiO2. Electrochem. Solid-State Lett. 10, A29
(2007)
28. Cava, R.J., Murphy, D.W., Zahurak, S., Santoro, A., Roth, R.S.: The crystal structures
of the lithium-inserted metal oxides Li0.5 anatase, LiTi2O4 spinel, and Li2Ti2O4. J. Solid
State Chem. 53, 64 (1984)
29. Sudant, G., Baudrin, E., Larcher, D., Tarascon, J.-M.: Electrochemical lithium reactivity with nanotextured anatase-type TiO2. J. Mater. Chem. 15, 1263 (2005)
30. Kavan, L., Kalbac, M., Zukalova, M., Exnar, I., Lorenzen, V., Nesper, R., Graetzel,
M.: Lithium Storage in Nanostructured TiO2 Made by Hydrothermal Growth. Chem.
Mater. 16, 477 (2004)
31. Zukalova, M., Kalbac, M., Kavan, L., Exnar, I., Graetzel, M.: Pseudocapacitive Lithium Storage in TiO2(B). Chem. Mater. 17, 1248 (2005)
32. Gao, X.P., Lan, Y., Zhu, H.Y., Liu, J.W., Ge, Y.P., Wu, F., Song, D.Y.: Electrochemical Performance of Anatase Nanotubes Converted from Protonated Titanate Hydrate
Nanotubes. Electrochem. Solid- State Lett. 8, A26 (2005)
33. Armstrong, A.R., Armstrong, G., Canales, J., Garcia, R., Bruce, P.G.: Lithium-Ion Intercalation into TiO2-B Nanowires. Adv. Mater. 17, 862 (2005)
34. Armstrong, G., Armstrong, A.R., Canales, J., Bruce, P.G.: Nanotubes with the TiO2-B
structure. Chem. Comm. 41, 2454 (2005).
35. Armstrong, G., Armstrong, A.R., Bruce, P.G., Reale, P., Scrosati, B.: TiO2(B) Nanowires as an Improved Anode Material for Lithium-Ion Batteries Containing LiFePO4
or LiNi0.5Mn1.5O4 or LiNi0.5Mn1.5O4 Cathodes and a Polymer Electrolyte. Adv. Mater.
18, 2597 (2006)
36. Guo, Y.-G., Hu, Y.-S., Sigle, W., Maier, J.: Superior Electrode Performance of
Nanostructured Mesoporous TiO2 (Anatase) through Efficient Hierarchical Mixeed
Conducting Networks. Adv. Mater. 19, 2087 (2007)
37. Wang, D., Choi, D., Li, J., Yang, Z., Nie, Z., Kou, R., Wang, C., Saraf, L.V., Zhang,
J., Aksay, I.A., Liu, J.: Self-Assembled TiO2-Graphene Hybrid Nanostructures for Enhanced Li-Ion Insertion. ACS Nano 3, 907 (2009)
38. Whittingham, M.S.: The Role of Ternary Phases in Cathode Reactions. J. Electrochem. Soc. 123, 315 (1976)
39. Murphy, D.W., Christian, P.A., DiSalvo, F.J., Carides, J.N., Waszczak, J.V.: Lithium
Incorporation by V6O13 and Related Vanadium (+4, +5) Oxide Cathode Materials. J.
Electrochem. Soc. 128, 2053 (1981)
40. Li, W., Dahn, J.R., Wainwright, D.S.: Sci. 264, 1115 (1994)
41. Zhang, S., Li, Y., Wu, C., Zheng, F., Xie, Y.: Novel Flowerlike Metastable Vanadium
Dioxide (B) Microanostructures: Facile Synthesis and Application in Aqueous Lithium
Ion Batteries. J. Phys. Chem. C 113, 15058 (2009)
42. Choi, N.-S., Kim, J.-S., Yin, R.-Z., Kim, S.-S.: Electrochemical properties of lithium
vanadium oxcide as an anode material for lithium-ion battery. Mater. Chem. Phys.
116, 603 (2009)
43. Kohler, J., Makihara, H., Uegaito, H., Inoue, H., Toki, M.: LiV3O8: Characterization
as anode material for an aqueous rechargeable Li-ion battery system. Electrochim.
Acta 46, 59 (2000)
34
44. Kim, S.-S., Ikuta, H., Wakihara, M.: Synthesis and characterization of MnV2O6 as a
high capacity anode material for a lithium secondary battery. Solid State Ion. 139, 57
(2001)
45. Denis, S., Baudrin, E., Touboul, M., Tarascon, J.-M.: Synthesis and Electrochemical
Properties of Amorphous Vanadates of General Formula RVO4 (R=In, Cr, Fe, Al, Y)
vs. Li. J. Electrochem. Soc. 144, 4099 (1997)
46. Guyomard, D., Sigala, C., Le Gal la Salle, A., Piffard, Y.: New amorpous oxides as
high capacity negative electrodes for lithium batteries: the Li xMVO4 (M=Ni, Co, Cd,
Zn; 1<x≤8). J. Power Sources 68, 692 (1997)
47. Son, J.T.: Novel electrode material for Li ion battery based on polycrystalline LiNbO 3.
Electrochem. Commun. 6, 990 (2004)
48. Han, J.-T., Liu, D.-Q., Song, S.-H., Kim, Y., Goodenough, J.B.: Lithium Ion Intercalation Performance of Niobium Oxides: KNb5O13 and K6Nb10.8O30. Chem. Mater. 21,
4753 (2009)
49. Auborn, J.J., Barberio, Y.L.: Lithium Intercalation Cells Without Metallic Lithium. J.
Electrochem. Soc. 134, 638 (1987)
50. Yang, L.C., Gao, Q.S., Tang, Y., Wu, Y.P., R. Holze: MoO2 synthesized by reduction
of MoO3 with ethanol vapor as an anode material with good rate capability for the
lithium ion battery. J. Power Sources 179, 357 (2008)
51. Yang, L.C., Gao, Q.S., Zhang, Y.H., Tang, Y., Wu, Y.P.: Tremella-like molybdenum
dioxide consisting of nanosheets as an anode material for lithium ion battery. Electrochem. Commun. 10, 118 (2008)
52. Dillon, A.C., Mahan, A.H., Deshpande, R., Parilla, P.A., Jones, K.M., Lee, S.-H.:
Metal oxide nano-particles for improved electrochromic and lithium-ion battery technologies. Thin Solid Film 516, 794 (2008)
53. Huang, K., Pan, Q., Yang, F., Ni, S., Wei, X., He, D.: Controllable synthesis of hexagonal WO3 nanostructures and their application in lithium batteries. J. Phys. D:
Appl. Phys. 41, 155417 (2008)
54. Mai, L., Hu, B., Chen, W., Qi, Y., Lao, C., Yang, R., Dai, Y., Lin Wang, Z.: Lithiated
MoO3 Nanobelts with Greatly Improved Performance for Lithium Batteries. Adv. Mater. 19, 3712 (2007)
55. Hassan, M.F., Guo, Z.P., Chen, Z., Liu, H.K.: Carbon-coated MoO3 nanobelts as anode materials for lithium-ion batteries. J. Power Sources 195, 2372 (2010)
56. Lee, S.-H., Kim, Y.-H., Deshpande, R., Parilla, P.A., Whitney, E., Gillaspie, D.T.,
Jones, K.M., Mahan, A.H., Zhang, S., Dillon, A.C.: Reversible Lithium-Ion Insertion
in Molybdenum Oxide Nanoparticles. Adv. Mater. 20, 3627 (2008)
57. Poizot, P., Laruelle, S., Grugeon, S., Dupont, L., Tarascon, J.-M.: Nano-sized transition-metal oxides as negative-electrode materials for lithium-ion batteries. Nat. 407,
496 (2000)
58. Balaya, P., Li, H., L. Kienle, Maier, J.: Fully Reversible Homogeneous and Hetrogeneous Li Storage in RuO2 with High Capacity. Adv. Funct. Mater. 13, 621 (2003)
59. Li, H., Balaya, P., Maier, J.: Li-Storage via Heterogeneous Reaction in Selected Binary Metal Flurorides and Oxides J. Electrochem. Soc. 151, A1878 (2004)
60. Larcher, D., Sudant, G., J-B. Leriche, Y. Chabre, Tarascon, J.-M.: The Electrochemical Reduction of Co3O4 in a Lithium Cell. J. Electrochem. Soc. 149, A234 (2002)
61. Larcher, D., C. Masquelier, D. Bonnin, Y. Chabre, V. Masson, J.-B. Leriche,
Tarascon, J.-M.: Effect of Particle Size on Lithium Intercalation into α-Fe2O3. J. Electrochem. Soc. 150, A133 (2003)
62. Poizot, P., Laruelle, S., Grugeon, S., Tarascon, J.-M.: Rationalization of the LowPotential Reactivity of 3d-Metal-Based Inorganic Compounds toward Li. J. Electrochem. Soc. 149, A1212 (2002)
63. Hu, J., Li, H., Huang, X.: Cr2O3-Based Anode Materials for Li-Ion Batteries. Electrochem. Solid-State Lett. 8, A66 (2005)
35
64. Chen, J., Xu, L., Li, W., Gou, X.: α-Fe2O3 Nanotubes in Gas Sensor and Lithium-Ion
Battery Applications. Adv. Mater. 17, 582 (2005)
65. He, Y., Huang, L., Cai, J.-S., Zheng, X.-M., Sun, S.-G.: Structure and electrochemical
performance of nanostructured Fe3O4/carbon nanotube composites as anodes for lithium ion batteries. Electrochim. Acta 55, 1140 (2010)
66. Reddy, A.L.M., Shaijumon, M.M., Gowda, S.R., Ajayan P.M.: Coaxial MnO2/Carbon
Nanotube Array Electrodes for High-Performance Lithium Batteries. Nano Letters 9,
1002 (2009)
67. Du, N., Zhang, H., Chen, B., Wu, J., Ma, X., Liu, Z., Zhang, Y., Yang, D., Huang, X.,
J. Tu: Porous Co3O4 Nanotubes Derived From Co4(CO)12 Clusters on Carbon Nanotube Templates: A Highly Efficient Material For Li-Battery Applications. Adv. Mater.
19, 4505 (2007)
68. Li, Y., Tan, B., Wu, Y.: Freestanding Mesoporous Quasi-Single-Crystalline Co3O4
Nanowire Arrays. J. Am. Chem. Soc. 128, 14258 (2006)
69. Li, Y., Tan, B., Wu, Y.: Mesoporous Co3O4 Nanowire Arrays for Lithium Ion Batteries with High Capacity and Rate Capability. Nano Lett. 8, 265 (2008)
70. Ryu, J., Kim, S.-W., Kang, K., Park, C.B.: Synthesis of Diphenylalanine/Cobalt Oxide
Hybrid Nanowires and Their Application to Energy Storage. ACS Nano 4, 159 (2010)
71. Jiang, J., Liu, J., Ding, R., Ji, X., Hu, Y., Li, X., Hu, A., Wu, F., Zhu, Z., Huang, X.:
Direct Synthesis of CoO Porous Nanowire Arrays on Ti Substrate and Their Application as Lithium-Ion Battery Electrodes. J. Phys. Chem. C 114, 929 (2010)
72. Taberna, P.L., Mitra, S., Poizot, P., Simon, P., Tarascon, J.-M.: High rate-capabilityes
Fe3O4-based Cu nano-architectured electrodes for lithium-ion battery applications.
Nat. Mater. 5, 567 (2006)
73. Wang, L., Yu, Y., Chen, P.C., Zhang, D.W., Chen C.H.: Electrospinning synthesis of
C/Fe3O4 composite nanofibers and their application for high performance lithium-ion
batteries. J. Power Sources 183, 717 (2008)
74. Liu, J., Li, Y., Fan, H., Zhu, Z., Jiang, J., Ding, R., Hu, Y., Huang, X.: Iron OxideBased Nanotube Arrays Derived from Sacrificial Template-Accelerated Hydrolysis:
Large-Area Design and Reversible Lithium Storage. Chem. Mater. 22, 212 (2010)
75. Reddy, M.V., Yu, T., Sow, C.-H., Shen, Z.X., Lim, C.T., Subba Rao, G.V., Chowdari,
B.V.R.: α-Fe2O3 Nanoflakes as an Anode Material for Li-Ion Batteries. Adv. Funct.
Mater. 17, 2792 (2007)
76. Zhang, W.-M., Wu, X.-L., Hu, J.-S., Guo, Y.-G., Wan, L.-J.: Carbond Coated Fe3O4
Nanospindles as a Superior Anode Material for Lihtium-Ion Batteries. Adv. Funct.
Mater. 18, 3941 (2008)
77. Xiang, J.Y., Tu, J.P., Yuan, Y.F., Wang, X.L., Huang, X.H., Zeng, Z.Y.: Electrochemical investigation on nanoflower-like CuO/Ni composite film as anode for lithium ion
batteries. Electrochim. Acta 54, 1160 (2009)
78. Xiang, J.Y., J. P. Tu, L. Zhang, Y. Zhou, Wang, X.L., Shi, S. J.: Self-assembled synthesis of hierarchical nanostructured CuO with various morphologies and their application as anodes for lithium ion batteries. J. Power Sources 195, 313 (2010)
79. Li, B., Rong, G., Xie, Y., Huang, L., Feng C.: Low-Temperature Synthesis of α-MnO2
Hollow Urchins and Their Application in Rechargeable Li+ Batteries. Inorg. Chem.
45, 6404 (2006)
80. Shaju, K.M., Jiao, F., Debart, A., Bruce, P.G.: Mesoporous and nanowire Co3O4 as
negative electrodes for rechargeable lithium batteries. Phys. Chem. Chem. Phys. 9,
1837 (2007)
81. Lou, X.W., Deng, D., Lee, J.Y. Archer, L.A.: Thermal formation of mesoporous single-crystal Co3O4 nano-needles and their lithium storage properties. J. Mater. Chem.
18, 4397 (2008)
36
82. Liu, J., Li, Y., Ding, R., Jiang, J., Hu, Y., Ji, X., Chi, Q., Zhu, Z., Huang, X.: Carbon/ZnO Nanorod Array Electrode with Significantly Improved Lithium Storage Capability. J. Phys. Chem. C 113, 5336 (2009)
83. Needham, S.A., Wang, G.X., Konstantinov, K., Tournayre, Y., Lao, Z., Liu, H.K.:
Electrochemical Performance of Co3O4-C Composite Anode Materials. Electrochem.
Solid-State Lett. 9, A315 (2006)
84. Morcrette, M., Rozier, P., Dupont, L., Mugnier, E., Sannier, L., Galy, J., Tarascon,
J.M.: A reversible copper extrusion-insertion electrode for rechargeable Li batteries.
Nat. Mater. 2, 755 (2003)
85. Kim, C., Noh, M., Choi, M., Cho, J., Park, B.: Critical Size of a Nano SnO2 Electrode
for Li-Secondary Battery. Chem. Mater. 17, 3297 (2005)
86. Lou, X.W., Chen, J.S., Chen, P., Archer, L.A.: One-Pot Synthesis of Carbon-Coated
SnO2 Nanocolloids with Improved Reversible Lithium Storage Properties. Chem. Mater. 21, 2868 (2009)
87. Li, N., Martin, C.R.: A High-Rate, High-Capacity, Nanostructured Sn-Based Anode
Prepared Using Sol-Gel Template Synthesis. J. Electrochem. Soc. 148, A164 (2001)
88. Meduri, P., Pendyala, C., Kumar, V., Sumanasekera, G.U., Sunkara, M.K.: Hybrid Tin
Oxide Nanowires as Stable and High Capacity Anodes for Li-Ion Batteries. Nano Lett.
9, 612 (2009)
89. Jiang, L.-Y., Wu, X.-L., Guo, Y.-G., Wan, L.-J.: SnO2-Based Hierarchical Nanomicrostructures: Facile Synthesis and Their Applications in Gas Sensors and LithiumIon Batteries. J. Phys. Chem. C 113, 14213 (2009)
90. Yu, Y., Chen, C.-H., Shi, Y.: A Tin-Based Amorphous Oxide Composite with a Porous, Spherical, Multideck-Cage Morphology as a Highly Reversible Anode Material
for Lihtium-Ion Batteries. Adv. Mater. 19, 993 (2007)
91. Liu, H.K., Wang, G.X., Guo, Z.P., Wang, J.Z., Konstantinov, K.: Nanomaterials for
Lithium-ion Rechargeable Batteries. J. Nanosci. Nanotechnol. 6, 1 (2006)
92. Ye, S.H., Lv, J.Y., Gao, W.P., Wu, F., Song, D.Y.: Synthesis and electrochemical
properties of LiMn2O4 spinel phase with nanostructure. Electrochim. Acta 49, 1623
(2004)
93. Nordliner, S., Edstrom, K., Gustafsson, T.: The Performance of Vanadium Oxide Nanorolls as Cathode Material in a Rechargeable Lithium Battery. Electrochem. SolidState Lett. 4, A129 (2001)
94. Patrissi, C.J., Martin, C.R.: Sol-Gel-Based Template Synthesis and Li-Insertion Rate
Performance of Nanostructured Vanadium Pentoxide. J. Electrochem. Soc. 146, 3176
(1999)
95. Jiao, F., Shaju, K.M., Bruce, P.G.: Synthesis of Nanowire and Mesoporous LowTemperature LiCoO2 by a Post-Templating Reaction. Angew. Chem. Int. Ed. 44, 6550
(2005)
96. Hosono, E., Kudo, T., Honma, I., Matsuda, H., Zhou, H.: Synthesis of Single Crystalline Spinel LiMn2O4 Nanowires for a Lithium Ion Battery with High Power Density.
Nano Lett. 9, 1045 (2009)
97. Kim, D.K., Muralidharan, P., Lee, H.W., Ruffo, R., Yang, Y., Chan, C.K., Peng, H.,
Hu, R., Huggins, A., Cui, Y.: Spinel LiMn2O4 Nanorods as Lithium Ion Battery Cathodes. Nano Lett. 8, 3948 (2008)
98. Yamada, A., Koisumi, H., Sonoyama, N., Kanno, R.: Electrochem. Solid-State Lett. 8,
A409 (2005)
99. Yamada, A., Koisumi, H., Nishimura, S.I., Sonoyama, N., Kanno, R., Yonemura, M.,
Nakamura, T., Kobayashi, Y.: Room-temperature miscibility gap in LixFePO4. Nat.
Mater. 5, 357 (2006)
100. Kobayashi, G., Nishimura, S.I., Park, M.S., Kanno, R., Yashima, M., Ida, T., Yamada,
A.: Isolation of Solid Solution Phases in Size-Controlled LixFePO4 at Room Temperature. Adv. Funct. Mater. 19, 395 (2009)
37
101. Meethong, N., Huang, H.Y.S., Carter, W.C., Chiang, Y.M.: Size-Dependent Lithium
Miscibility Gap in Nanoscale Li1-xFePO4. Electrochem. Solid-State Lett. 10, A134
(2007)
102. Gibot, P., Casas-Cabanas, M., Laffont, L., Levasseur, S., Carlach, P., Hamelet, S.,
Tarascon, J.-M., Masquelier, C.: Room-temperature single-phase Li insertion/extraction in nanoscale LixFePO4. Nat. Mater. 7, 741 (2008)
103. Meethong, N., Kao, Y.H., Tang, M., Huang, H.-Y., Carter, W.C., Chiang, Y.M.: Electrochemically Induced Phase Transformation in Nanoscale Olivines Li1-xMPO4
(M=Fe, Mn). Chem. Mater. 20, 6189 (2008)
104. Lee, K.T., Kan, W.H., Nazar, L.: Proof of Intercrystallite Ionic Transport in LiMPO4
Electrodes (M=Fe, Mn). J. Am. Chem. Soc. 131, 6044 (2009)
105. Zhu, Y., Wang, C.: Galvanostatic Intermittent Titration Technique for PhaseTransformation Electrodes. J. Phys. Chem. C 114, 2830 (2010)
106. Chen, Z., Dahn, J.R.: Reducing Carbon in LiFePO4/C Composite Electrodes to Maximize Specific Energy, Volumetric Energy , and Tap Density. J. Electrochem. Soc.
149, A1184 (2002)
107. Wang, Y., Cao, G.: Developments in Nanostructured Cathode Materials for HighPerformance Lithium-Ion Batteries. Adv. Mater. 20, 2251 (2008)
108. Robertson, A.D., Armstrong, A.R., Bruce, P.G.: Layered LixMn1-yCoyO2 Intercalation
Electrodes – Influence of Ion Exchange on Capacity and Structure upon Cycling.
Chem. Mater. 13, 2380 (2001)
109. Goodenough, J.B., Kim, Y.: Challenges for Rechargeable Li Batteries. Chem. Mater.
22, 587 (2010)
110. Lightfoot, P., Metha, M.A., Bruce, P.G.: Crystal Structure of the Polymer Electrolyte
Poly(ethylene oxide)3: LiCF3SO3. Sci. 262, 883 (1993)
111. Croce, F., Appetecchi, G.B., Persi, L,, Scrosati, B.: Nanocomposite polymer electrolytes for lithium batteries. Nat. 394, 456 (1998)
112. Maier, J.: Ionic conduction in space charge regions. Prog. Solid St. Chem. 23, 171
(1995)
113. Croce, F., Settimi, L., Scrosati, B.: Superacid ZrO2-added, composite polymer electrolytes with improved transport properties. Electrochem. Commun. 8, 364 (2006)